Previous issue date: 2016-07-29 / O processo de fabricação de uma peça cerâmica é composto por uma sequência de etapas, sendo quatro as etapas principais: preparação da massa, conformação, secagem e queima. É importante destacar que as propriedades dos produtos cerâmicos estão relacionadas com as características iniciais da matéria- prima, tais como: granulometria, composição química, composição mineralógica e com os parâmetros de processamento. Dentro deste contexto, este trabalho teve como objetivo avaliar a influência das características das massas e das variáveis de processamento sobre a microestrutura e as propriedades tecnológicas de produtos obtidos a partir de massas da cerâmica vermelha. Foram utilizadas argilas e uma massa fornecidas por indústrias de cerâmica vermelha dos Estados de Pernambuco e da Paraíba. As argilas e a massa foram beneficiadas e em seguida, assim como as massas formuladas, caracterizadas através das técnicas de análise granulométrica e avaliação das características de plasticidade, bem como através de análises química, mineralógica e térmica. Os corpos de prova foram conformados por prensagem e extrusão e, posteriormente, submetidos a queima nas temperaturas de 800, 900, 1000, 1100 e 1200ºC, taxa de aquecimento de 5ºC/min e tempo de permanência na temperatura máxima de 60 e 180 min. Após tratamento térmico, foi realizada uma avaliação da variação da cor de queima em função das temperaturas supracitadas, bem como analisadas as propriedades tecnológicas (perda de massa ao fogo, retração linear de queima, absorção de água, porosidade aparente, massa específica aparente e resistência mecânica à flexão em três pontos), as fases formadas para os diferentes tratamentos térmicos e as morfologias das superfícies de fratura dos corpos de prova. Os resultados mostraram que a interação entre as características granulométricas, mineralógicas e químicas das amostras, a depender do tipo de processo de conformação utilizado e do ciclo de queima estabelecido, acarretam alterações relevantes sobre a microestrutura, impactando sobre as propriedades mecânicas do produto final. / The process for manufacturing a ceramic part consists of a sequence of steps, four major steps: preparation of the dough, shaping, drying and firing. It is important to note that the properties of ceramics are related to the initial characteristics of the raw material, such as particle size, chemical composition, mineralogical composition and processing parameters. Within this context, this study aimed to evaluate the influence of the characteristics of the masses and processing variables on the microstructure and technological properties of products obtained from the mass of red ceramic. clays were used and a mass provided by red ceramic industries of Pernambuco and Paraíba States. Clays and mass spectra were processed and then issued as well as the masses, characterized by the granulometric analysis techniques and evaluation of the characteristics of plasticity, as well as through chemical, mineralogical and thermal analysis. The specimens were shaped by pressing and extrusion and subsequently subjected to burning at temperatures of 800, 900, 1000, 1100 and 1200°C, heating rate of 5°C/min and residence time in the maximum temperature of 60 and 180 min. After heat treatment, an evaluation of the variation in the burning color according to the above temperatures was performed and analyzed technological properties (mass loss on ignition linear firing shrinkage, water absorption, porosity, apparent specific gravity and strength mechanical bending in three points), the phases formed for different heat treatments and the morphologies of the fracture surfaces of the specimens. The results showed that the interaction between the granulometric characteristics, mineralogical and chemical samples, depending on the type of forming process used and the set firing cycle, result in significant changes on the microstructure, an impact on the mechanical properties of the final product.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1064 |
| Date | 29 June 2018 |
| Creators | SANTOS, Renato Correia dos. |
| Contributors | SANTANA, Lisiane Navarro de Lima., MENEZES, Romualdo Rodrigues., NEVES, Gelmires de Araújo., MACEDO, Reginaldo Severo de., ALMEIDA, Ester Pires de., SILVA, Valmir José da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds