Estudos físicos e mecânicos de telhas de cimento de escória de alto-forno reforçado com fibras celulósicas residuais / Physical and mechanical studies of roofing tiles made of blast furnace slag cement reinforced with residual cellulose fibers

A presente pesquisa tem como objetivo desenvolver um novo elemento de cobertura, compatível com o meio ambiente: telhas de cimento alternativo reforçado com fibras celulósicas. Para tanto, foram utilizadas matérias-primas consideradas resíduos industriais (cimento de escória de alto-forno e rejeito de polpa de celulose de eucalipto) para obtenção de pastas cimentícias reforçadas. Os compósitos foram produzidos por dispersão prévia das fibras em água, mistura do compósito em argamassadeira convencional, adensamento por vibração, moldagem em fôrmas, seguida de cura úmida. Foram moldadas placas planas de diferentes formulações de matrizes cimentícias, com as matérias-primas alternativas disponíveis. Com base nos melhores resultados dessa fase preliminar, foram produzidas duas séries de telhas tipo romana \"capa canal\". Foram avaliados o desempenho físico-mecânico, os custos de produção e o comportamento térmico das telhas. Os resultados revelaram a potencialidade dos compósitos obtidos na produção de fibrocimentos alternativos, por meio de técnicas simples e de baixo consumo de energia, direcionados à autoconstrução urbana e rural de baixo custo. / The objective of this study was to develop a new roofing material that would be compatible with the environment: roofing tiles made of alternative cement reinforced with cellulose fibers. Industrial waste materials were used as raw materials (blast furnace slag cement and waste eucalyptus cellulose pulp) to obtain reinforced cement pastes. The composites were produced by previously dispersing the fibers in water, mixing the composite in a conventional cement-mixer, compaction by vibration, shaping them in molds, followed by moist curing. Flat sheets were molded using different formulations of cement matrixes with the alternative raw materials avaiable. Based on the best results from this preliminary phase, two series of Roman tiles for roofing were produced. The physical and mechanical performance, the cost of production, and the thermal behavior of the tiles were evaluated. The results revealed the potential of composites made of alternative fiber-cements, using simple techniques and with low energy consumption, in urban and rural areas for low-cost self-construction.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-24102016-111618
Date07 July 2003
CreatorsDevito, Reginaldo Araujo
ContributorsVecchia, Francisco Arthur da Silva
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0019 seconds