Previous issue date: 2007 / Resumo: Este trabalho apresenta um método simples de passivação de superfícies semicondutoras III-V de substratos de arseneto de gálio (GaAs) e de heteroestruturas de fosfeto de gálio-índio sobre arseneto de gálio (InGaP/GaAs), que são utilizados em transist res de efeito de campo, MESFET (Metal-Semiconductor Field Effect Transistor) e MISFET Metal-Insulator-Semiconductor Field Effect Transistor), e transistores bipolares de heterojunção (HBT), respectivamente. O processo de passivação visa à máxima redução da densidade de estados de superfícies semicondutoras para níveis menores que 1012 cm-2. A alta densidade de estados na superfície do GaAs provoca corrente de fuga nas regiões ativas dos transistores MESFET e HBT, reduzindo o desempenho destes dispositivos. Além disso, impossibilita a formação de dispositivos MISFET sobre os substratos de GaAs, devido à alta densidade de estados na região da interface isolante-semicondutor. Para o estudo da passivação de superfícies, filmes de nitreto de silício (SiNX) são depositados diretam nte por plasma ECR-CVD (Electron Cyclotron Resonance - Chemical Vapor Deposition) sobre substratos de GaAs e heteroestruturas do tipo InGaP/GaAs. Os plasmas ECR foram analisados por espectroscopia de emissão óptica (OES), e identificou-se baixa formação de espécies H e NH na fase gasosa para pressão de processo de 2,5 mTorr. Os filmes de SiNX foram caracterizados estruturalmente por espectroscopia de absorção do infravermelho (FTIR) e por elipsometria, que indicaram, respectivamente, a formação de ligações Si-N e valores de índice de refração es de nitreto de silício. Capacitores MIS e transisto T foram fabricados para avaliar os efeitos da passivação sobre os dispositivos. Os excelentes resultados obtidos, tais como transist o e em torno de 2,0 nos filmres MISFET e HB ores HBT passivados apresentando maiores ganhos de corrente do que os não-passivados, e os transistores MISFET apresentando maiores valores de transcondutância do que os MESFET (que foram usados como dispositivos de controle), indicam que o nosso processo de passivação é muito eficiente, sendo completamente compatível com a tecnologia de fabricação de circuitos integrados monolíticos de microondas (MMIC) / Abstract: This work presents a simple passivation method for III-V semiconductor surfaces of gallium arsenide (GaAs) substrates and indium-gallium phosphide on gallium arsenide (InGaP/GaAs) heterostructures, which are us in field effect transistors MESFET (Metal-Semiconductor Field Effect Transistor) and MISFET (Metal-Insulator-Semiconductor Field Effect Transistor) and heterojunction bip lar transistors (HBT), respectively. The passivation process aims the maximum reduction of semiconductor surface state density at levels lower than 1012 states/cm2. The high surface state density on GaAs surface produces current leakage in active regions of MESFET and HBT transistors, reducing the device performance. Furthermore, the MISFET device formation on GaAs substrate is not allowed, passivation study, silicon nitride films (SiNX) are deposited by ECR-CVD (Electron Cyclotron Resonance - Chemical Deposition Vapor) plasma directly over GaAs substrate and InGaP/GaAs heterostructures. The ECR plasmas were analyzed by optical emission spectroscopy, (OES), and low formation of H and NH molecules in the gas phase was detected at process pressure of 2.5 mTorr. The SiNX film structural characterization was obtained by infra-red absorption spectrometry (FTIR) and ellipsometry, which, respectively, indicate the Si-N bo tive index values of about 2.0 at the silicon nitride films. MIS cap BT transistors were fabricated to verify the passivation process effect on devices. The excellent results obtained, such as higher and formation and refracacitors, MISFET and H current gain of passivated device compared to unpassivated HBTs and higher transconductances of MISFET devices compared to MESFET (which were used as control devices), indicate that our simple passivation process is very efficient, being fully compatible with monolithic microwave integrated circuits (MMIC) / Doutorado / Eletrônica, Microeletrônica e Optoeletrônica / Doutor em Engenharia Elétrica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/260858 |
Date | 12 May 2007 |
Creators | Zoccal, Leonardo Breseghello |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Diniz, José Alexandre, 1964-, Martins, Everson, Frateschi, Newton Cesário, Swart, Jacobus Willibrordus, Tatsch, Peter Jürgen, Doi, Ioshiaki |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Elétrica e de Computação, Programa de Pós-Graduação em Engenharia Elétrica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 171p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds