Saab Microwave Systems, SMW is a supplier of radar systems. The circuit boards that are operating in their radars have components which solder joints contains lead. However, the EU directive RoHs and WEEE are causing SMW to prepare for a transition to lead free solder joints. The objective of this thesis is to gain deeper knowledge of lead free solder joints. Brittle fractures in solder joints is a type of failure that might increase in a transition to lead free solder joints. The brittle fractures are induced by the creation of the intermetallic phases which are formed during soldering. The amount and composition of the intermetallics affects the mechanical strength of the joint. An intermetallic layer is thickened during heat exposure as during soldering, thermal aging and rework. The focus of this thesis was to investigate how rework affect the brittleness of the lead free solder joint and thereby how the intermetallic layers change depending on chemical composition, design and reflow cycles. Two types of components and two types of solder materials (SnPb and SAC305) were studied. To study the mechanical properties of the joint a shear testing device was used. This is a way of measuring the reliability of the joint when subjected to mechanical shock. The intermetallic layers were examined in a Scanning Electron Microscope and the fracture surfaces were studied in a optical microscope, a scanning electron microscope and a stereomicroscope. The heat spread over the board where examined by soldering thermocouples to the board and plotting the values of time and temperature. The results showed that the rework process did not have any significant impact of the intermetallic growth. The adjecent and distant components were not damaged during rework. A lead free rework process can therefor be preformed successfully at SMW. The intermetallic layers formed at the interface between the a lead free solder and a nickel finish grew faster than an intermetallic layer formed between a leaded solder and a nickel finish. The presence of nickel could therefore have a more negative effect on the intermetallic growth rate for the lead free material compared to the leaded.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kau-5039 |
| Date | January 2009 |
| Creators | Dornerus, Elin |
| Publisher | Karlstads universitet |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds