Influência de lecitina e PGPR no processo de microestruturação de chocolate amargo / Influence of lecithin and PGPR in the microstructuration process of dark chocolates

Orientadores: Lireny Aparecida Guaraldo Gonçalves, Priscila Efraim / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-18T18:52:26Z (GMT). No. of bitstreams: 1
Stroppa_ValterLuisZuliani_M.pdf: 1829992 bytes, checksum: 1eb19d94141314569616332614683d54 (MD5)
Previous issue date: 2011 / Resumo: Chocolates são produtos compostos por uma fase lipídica com predominância de manteiga de cacau, e que contem liquor, açúcar emulsificantes e eventualmente leite em pó (ou derivados lácteos) e aromas. As características físicas dos chocolates como brilho, dureza, fusão a temperaturas da boca e estabilidade térmica são conseqüências da estruturação cristalina induzida na manteiga de cacau. Os triacilgliceróis presentes na manteiga de cacau podem-se organizar em até seis formas polimórficas sendo que apenas duas são estáveis e geram produtos de melhor qualidade. A adição de emulsificantes ao chocolate visa melhorar o comportamento reológico durante o processamento diminuindo as tensões interfaciais entre a fase gordurosa e as partículas sólidas. Os emulsificantes promovem o recobrimento das partículas sólidas com a fase oleosa lubrificando as interfaces que, desta maneira, poderão servir de elementos ativos para a nucleação. Este trabalho avaliou o efeito da adição dos dois emulsificantes mais utilizados na indústria, lecitina de soja e PGPR (poliglicerol poliricinoleato), no processo de estruturação cristalina de chocolate amargo. Foram produzidos chocolates com diferentes teores de emulsificantes conforme um planejamento fatorial completo 2² rotacionado. O nível de lecitina variou de 0,08 a 0,92% e o de PGPR de 0,02 a 0,58%. Para caracterizar esta influência foram utilizadas técnicas de reometria (determinação das propriedades de escoamento), ressonância magnética nuclear (acompanhamento da cinética de cristalização), Índice de temperagem (quantificação da pré-cristalização), e ensaios de ruptura (avaliação da resistência estrutural). Os valores de viscosidade plástica de Casson do chocolate medidos a 40ºC variaram de 1,4 a 5,9 Pa.s enquanto que o limite de escoamento variou de zero a 34Pa. Os parâmetros cinéticos avaliados de isotermas de cristalização a 15ºC ajustadas ao Modelo de Avrami resultaram no expoente n variando de 2,598 a 2,956 e o parâmetro k entre 5,15.10-6 e 2,85.10-5 min-n para os diferentes teores de emulsificantes. Estes efeitos foram associados à capacidade da lecitina em aumentar o volume cristalino e ao potencial nucleador do PGPR / Abstract: Chocolates are confectionary products composed by a lipid phase based mainly on cocoa butter that contains cocoa mass, sugar, emulsifiers and eventually milk solids and aromas. Physical characteristics of chocolates like gloss, hardness, melting at mouth temperature and thermal stability result from the crystalline structuration accomplished by the fat phase. The triacylglycerols in cocoa butter can be organized in up to six different polymorphs but only two of them are stable and therefore yield better quality products. The addition of emulsifiers to chocolates intends to improve the rheological behavior during processing by the reduction of the interfacial tension between the fat phase and the solid particles. The emulsifiers promote the coating of the solid particles by an oily layer, lubricating the interfaces that then can serve as active elements for nucleation. This work examines the effects of the addition of the two most used emulsifiers in chocolate, namely soy lecithin and PGPR (polyglycerol polyricinolate) in the crystalline structuration of chocolates. Chocolates with different contents of the two emulsifiers were produced, following a 22 complete factorial rotational design. The lecithin level varied from 0.08 to 0.92% and the PRPG content from 0.02 to 0.58%. The influence of the additives was characterized by rheometry (determination of the flowing parameters), nuclear magnetic resonance (monitoring the crystallization kinetics), Temperindex (pre-crystallization level quantification), and snap test (structural resistance). The values of Casson's plastic viscosity of the chocolates, measured at 40ºC, varied from 1.4 to 5.9 Pa.s while the yield value ranged between zero to 34 Pa. The kinetic parameters evaluated from crystallization isotherms at 15ºC modeled by the Avrami equation resulted in the exponent n varying from 2.598 to 2.956 and k parameters between 5.15 10-5 min-n and 2.85 10-5 min-n when the different amount of emulsifiers were used. These effects are associated to the ability of lecithin to enlarge the crystal volume and to the nucleating potential of PGPR / Mestrado / Engenharia de Processos / Mestre em Engenharia Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266882
Date07 November 2011
CreatorsStroppa, Valter Luís Zuliani
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Luccas, Valdecir, Kieckbusch, Theo Guenter, 1942-, Gonçalves, Lireny Aparecida Guaraldo, Efraim, Priscila
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format90 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds