Structural and optical properties of ZnO nanostructures synthesized by low energy ion implantation technique were examined. ZnO molecular ions were implanted into Si/SiO2 substrates at room temperature and then furnace annealed under different temperatures and environments. In all as-implanted samples only Zn nanostructures with varying diameters distributed into the Si/SiO2 matrices were observed. No trace of ZnO was found. The distributions of Zn nanostructures in Si/SiO2 closely matched results from Stopping and Range of Ions in Matter (SRIM) simulations. During annealing at 750 oC, Zn diffused both toward and away from the surface of the substrate and combine with oxygen to form ZnO nanostructures. At higher annealing temperatures ZnO bonding started to break down and transfer to zinc silicate (Zn2SiO4), and at 900 oC the ZnO was completely converted into Zn2SiO4. The average sizes of Zn/ZnO nanostructures depended on the ion fluence. If the fluence increased the average sizes of nanostructures also increased and vice versa. For room temperature photoluminescence (RT-PL), band-edge emission in the ultraviolet (UV) region was observed from all samples annealed at 700 oC/750 oC and were slightly blue shifted as compare to bulk ZnO. Donor-bound exciton (D,X) and acceptor-bound exciton (A,X) transitions were observed in low temperature photoluminescence (PL). The lifetime of both donor-bound excitonic emission (D, X) and acceptor-bound excitonic emission (A, X) were found to be in the picosecond (ps) range.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc500222 |
| Date | 05 1900 |
| Creators | Pandey, Bimal |
| Contributors | Weathers, Duncan L., McDaniel, Floyd Del. (Floyd Delbert), 1942-, Rout, Bibhudutta, Reinert, Tilo |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | xv, 119 pages : color illustrations, Text |
| Rights | Public, Pandey, Bimal, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |