Previous issue date: 2006 / Resumo: Fraturas por impacto e flexão ainda são os principais problemas relatados tanto pelos portadores de próteses removíveis como pelos cirurgiões dentistas. Na tentativa de solucionar esse problema, alterações na composição química das resinas acrílicas como a inclusão de co-polímeros, adição de agente de ligação cruzada e a incorporação de partículas de borracha na forma de butadieno estireno têm sido propostas. Entretanto, poucos estudos avaliaram a incorporação destes aditivos modificadores de impacto no processo de fratura, deformação e microestrutura de resinas acrílicas. Além disso, devido à fragilidade dos materiais poliméricos a presença de trincas e fraturas em base de
próteses removíveis ainda é alta e reparos são procedimentos comuns tanto por métodos diretos ou indiretos. Entretanto, as propriedades mecânicas de resinas acrílicas reparadas ainda não estão claramente descritas. Assim, os objetivos do presente trabalho foram: I) avaliar a resistência ao impacto e a flexão, bem como tensão de ruptura, módulo Young e deslocamento de escoamento de resinas acrílicas contendo modificadores de impacto e analisar sua microestrutura; II) determinar a resistência ao impacto e flexão de resinas acrílicas para base de prótese previamente fraturadas e reparadas com resinas fotopolimerizável, autopolimerizável e termopolimerizável. Como resultado, observou-se que a resina contendo borracha considerada de alto impacto, demonstrou alta capacidade de dissipação de energia, absorção de tensão e baixo percentual de deformação; entretanto exibiu processo de fratura frágil. Com relação às resinas utilizadas para reparo, concluiu-se que reparos realizados com a mesma resina usada para confecção dos corpos-de-prova, apresentaram melhores resultados quanto à resistência mecânica / Abstract: Fractures by impact and flexural action are the main problems described by denture users and dentists. Attempting to solve this problem, modifications on the chemical composition of the acrylic resins as co-polymer inclusion, cross linking agents addition and rubber particles incorporation in the form of butadiene styrene have been described as effective and worthwhile means to improve the impact strength and fracture propagation. However, literature lacks information regarding the incorporation of these modifying impact additives in the fracture process, plastic deformation and microstructure of acrylic resins. Furthermore, due to the brittleness of the polymeric materials, the presence of cracks and fractures in the removable prosthesis denture bases still remains high. Thus, frequent repairs are somewhat common procedures in the clinical practice, being by direct or indirect methods. Therefore, the effect of the repairs materials on the mechanical properties of acrylic resins is not clearly described yet. Front of these considerations, the purposes of the present study were: I) evaluate the impact and flexural strength, as well as, stress at yield, Young modulus and displacement at yield of acrylic resins containing impact modifiers and analyze their microstructure; II) determine the impact and flexural strength of denture base acrylic resins previously fractured and repaired with visible-light, auto and heat-polymerized acrylic resins. As results, it could be observed that the acrylic resin containing rubber particles, considered as the high impact, showed high capacity of energy dissipation and stress absorption before the fracture, lower percentage of deformation, however it exhibited brittle fracture process. Regarding to acrylic resins used as repair materials, it was concluded that repairs performed with the same resin used to fabricate the specimens showed the best results for mechanical resistance / Doutorado / Protese Dental / Doutor em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288669 |
Date | 11 October 2006 |
Creators | Faot, Fernanda |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Del Bel Cury, Altair Antoninha, 1948-, Rodrigues-Garcia, Renata Cunha Matheus, 1964-, Ribeiro, Ricardo Faria, Rached., Rodrigo Nunes, Rosa, Rosena Santos da, Correr Sobrinho, Lourenço |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 70f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.2129 seconds