000733897.pdf: 2970916 bytes, checksum: 143c1c49a5232d5c6446207a9fe58878 (MD5) / O desenvolvimento do saços avançados de alta resistência tornou-se fundamental na produção de veículos com peso reduzido, seguros e mais econômicos, dentro do contexto daindústria automobilística. Dentre os aços avançados de alta resistência destacam-se os aços de fases complexas (CP) que são caracterizados por apresentarem alta conformabilidade e alta capacidade de absorção de energia e deformação. Eles são considerados aços multifásicos por apresentarem uma microestrutura complexa formada por ferrita, bainita, martensita e austenita retida. O trabalho tem por objetivo caracterizar a microestrutura do aço de fases complexas. Foram empregadas metalografia convencional e colorida, utilizando os reagentes químicos Nital, Metabissulfito de Sódio e LePera para a identificação das fases presentes no material. As análises da microestrutura final foram feitas via microscopia óptica, utilizando-se atécnica mais clássica que é a iluminação em campo claro, mas também foram utilizadas algumas técnicas diferentes tais como, iluminação em campo escuro,contraste por interferência diferencial (DIC) e método de luz polarizada.Os resultados mostraram que, de maneira qualitativa, para os ataques químicos com os reagentes Nital, Metabissulfito de Sódio e LePera se mostrarameficientes, pois pode-se identificar as fases presentes no aço CP; de maneira quantitativa, para o ataquefeito com Nital também se mostraram eficazes para as quatro condições de microscopia óptica,tais como iluminação em campo claro; em campo escuro; DIC e método de luz polarizada, porcausa da estabilidadedos valores para o cálculo das frações de área das fases presentes neste material / The development of advanced high-strength steels became instrumental inthe production of vehicles with reduced weight, insurance, andmore economical, within the contextof the automobile industry.Among the advanced high-strengthsteels are steels complex phase (CP) that are characterized by having high formability and high energy absorption capacity anddeformation. They are considered multiphase steels for presenting a complex microstructure consisting of ferrite, Bainite, martensiteand retained austenite. The work aims to characterize the complexphase steelmicrostructure.Were employed conventional metallography and colorful, using chemical reagentsNital, sodium metabisulfite andLePera for identification of phases present in the material. The final microstructure analyses were made via optical microscopy, usingmore classicaltechnique that is the bright field lighting, but also some different techniques were used such as lighting in dark field, differential interference contrast (DIC)and method of polarized light. The results showed that, of qualitative way, for the chemical attacks with Nital reagents,sodium metabisulfite and LePera were efficient, as it can identify the phases present in the CP steel; quantitative manner,for the attack made with Nital also proved effective for the four conditionsof optical microscopy, such as bright field lighting; in dark field; DIC and method of polarizedlight, because ofthe stability ofthe values for the calculation of area fractions ofphases present in this material
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/94384 |
Date | 29 January 2014 |
Creators | Dias, Erica Ximenes [UNESP] |
Contributors | Universidade Estadual Paulista (UNESP), Pereira, Marcelo dos Santos [UNESP] |
Publisher | Universidade Estadual Paulista (UNESP) |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 135 f. : il. |
Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
Rights | info:eu-repo/semantics/openAccess |
Relation | -1, -1 |
Page generated in 0.0655 seconds