In this study, zinc oxide (ZnO) nanotip and nanorod were grown on glass substrate by aqueous solution deposition (ASD). Both characteristics of the two nanostructures were investigated. For fabrication of ZnO nanostructure UV photodetector, In-Zn inter-digitated metal electrode was evaporated on the top of the grown ZnO nanostructure to form the contact via. Compared with the common value (375 nm), both the peaks from the PL spectra of ZnO nanotip and nanorod are red-shifted (409 nm) due to the massive defects in nanotip and nanorod. In order to improve the photosensiblity, heterojunction of ZnO nanostructure/TiO2 film was prepared and were made into UV photodetector. Photoresponses of both nanotip and nanorod were improved after N2O annealing at 300oC. With the heterojunction of ZnO 1D nanostructure on TiO2 film, the photoresponses of both ZnO nanotip/TiO2 film can reach to 22.85, and the rise time and decay time are 40 and 82 seconds, respectively. On the other side, the photoresponses of both ZnO nanorod/TiO2 film can reach to 27.44, and the rise time and decay time are 22 and 133 seconds, respectively.
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0828111-204443 |
Date | 28 August 2011 |
Creators | Hong, Min-Hsuan |
Contributors | Chung-Cheng Chang, Ming-Kwei Lee, I-Kai Lo, Yu-Hao Yang |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0828111-204443 |
Rights | user_define, Copyright information available at source archive |
Page generated in 0.0015 seconds