Estudo da biocompatibilidade do cimento de aluminato de cálcio para uso odontológico, avaliação do pH, liberação de íons cálcio e atividade antimicrobiana / Biocompatibility of calcium aluminate cement for dental use, evaluation of pH, calcium ion release and antimicrobial activity

O objetivo desse estudo foi avaliar o pH, a liberação de íons cálcio, a atividade antimicrobiana in vitro de cimento de aluminato de cálcio (EndoBinder) com diferentes radiopacificadores (óxido de bismuto, óxido de zinco e óxido de zircônia) e a biocompatibilidade do cimento acrescido de óxido de bismuto como agente radiopacificador, em comparação ao mineral trióxido agregado (MTA). Para a avaliação do pH e a liberação de íons cálcio, 25 amostras (n=5) de 2,0 x 10 mm foram obtidas de EndoBinder Puro (EBP), EndoBinder com Óxido de Bismuto (EBOB), EndoBinder com Óxido de Zinco (EBOZn), EndoBinder com Óxido de Zircônia (EBOZr) e Mineral Trióxido Agregado (MTA), que foram imersas em 10 ml água destilada e deionizada (pH=6,9). Após 2, 4, 12, 24, 48 horas, 7, 14 e 28 dias, foi medido o pH e a quantidade de íons cálcio da água onde as amostras foram imersas. Para a determinação in vitro da atividade antimicrobiana dos cimentos (EBP, EBOB, EBOZN, EBOZr e MTA), foram obtidas 15 amostras de cada material (n=3) de 5,0 x 5,0 mm colocadas em contato com 5 tipos de microrganismos: Escherichia coli (ATCC 25922), Enterococcus faecalis (ATCC 29212), Staphylococcus aureus (ATCC 25923), Candida albicans (ATCC 10231) e a Candida glabrata (ATCC 2001) em placas de petri com Agar (Muller Hinton e Sabouraud Dextrose) deixadas em temperatura ambiente por 2 horas para a pré-difusão e depois incubadas a 37°C por 24 horas. Utilizou-se uma régua milimetrada com precisão de 0,5 mm para realizar as medidas dos halos de inibição em torno dos corpos de prova. A biocompatibilidade dos materiais foi avaliada a partir da implantação de tubos de polietileno em tecido subcutâneo de 15 ratos machos, sendo 1 implante escapular e 1 pélvico, num total de 2 tubos por animal (n=5). Como controle, foi utilizada a lateral do tubo de polietileno. Após 7, 21 e 42 dias os animais foram sacrificados e os tecidos processados para a obtenção dos cortes histológicos e posterior análise histopatológica. Os resultados do ensaio de pH, liberação de cálcio e de atividade microbiológica foram submetidos à análise estatística (2-way ANOVA, Bonferroni, p<0,05). Os resultados de biocompatibilidade foram classificados quanto à severidade da reação inflamatória e quantificados em relação aos eventos presentes nas áreas pré-determinadas. Ao final de 28 dias não houve diferença estatística (p>0,05) entre nenhum grupo, tanto para o pH quanto para a liberação de íons cálcio. MTA, EBP e EBOB apresentaram atividade antimicrobiana quando em contato com todos os microrganismos, e EBOZr e EBOZn apenas quando em contato com Staphylococcus aureus e Candida glabrata. A reação inflamatória observada com os implantes subcultâneos diminuiu no decorrer do período de análise, porém ao final de 42 dias MTA ainda apresentou uma discreta reação inflamatória, situação não encontrada com o EB. Desta forma, concluiu-se que EB apresentou propriedades químicas e biológicas semelhantes ao MTA, além de apresentar menor reação tecidual, sendo biocompatível quando testado em tecido subcutâneo de ratos. / The purpose of this study was to evaluate the pH, calcium ion release, in vitro antimicrobial activity of a calcium aluminate cement (EndoBinder) with different radiopacifiers (bismuth oxide, zinc oxide, or zirconium oxide) and the biocompatibility of calcium aluminate cement with bismuth oxide radiopacifier in comparison with the mineral trioxide aggregate (MTA). For the evaluation of pH and calcium ion release 25 sample (n=5) measuring 2,0 x 10 mm were obtained from EndoBinder Pure (EBP), EndoBinder with bismuth oxide (EBOB), EndoBinder with zinc oxide (EBOZn), EndoBinder with zirconium oxide (EBOZr) and mineral trioxide aggregate (MTA) wich were immersed in a flask containing 10 ml of deionized and distilled water (pH=6,9). After 2, 4, 12, 24, 48 hours and 7, 14, 28 days, meassurements of the pH and calcium ion release from the water where the samples were immersed were assessed. To determine the in vitro antimicrobial activity of the cements (EBP, EBOB, EBOZN, EBOZr and MTA) 15 samples of each material (n=3) measuring 5,0 x 5,0 mm were placed in contact with five types of microorganisms: Escherichia coli (ATCC 25922), Enterococcus faecalis (ATCC 29212), Staphylococcus aureus (ATCC 25923), Candida albicans (ATCC 10231) e a Candida glabrata (ATCC 2001) .The MullerHinton agar (MH) diffusion method was employed and the plates were kept at room temperature for 2 hours for pre diffusion and then incubated at 37 C° for 24 hours. Zones of inhibition around the specimens were measured using a 0.5mm precision millimeter ruler. The biocompatibility of the test materials was evaluated from the implantation of 2 polyethylene tubes in the subcutaneous tissue of 15 male rats (n=5), 1 being scapular (EBOB) and 1 pelvic (MTA). The external tube wall was considered as the control group. After 7, 21 and 42 days animals were sacrificed, obtaining 5 tissue samples per group at each time interval of analysis then histological analysis was performed. The test results for pH, calcium ion release and in vitro antimicrobial activity were submitted to statistical analysis (two-way ANOVA, Bonferroni, p <0.05). The results of biocompatibility were classified according to severity of inflammatory reaction and quantified in relation to present events in pre-determined areas. After 28 days there was no statistical difference (p> 0.05) between any group for both the pH and calcium ions release. MTA, EBP and EBOB showed antimicrobial activity against all microorganisms and EBOZr and EBOZn only against Staphylococcus aureus and Candida glabrata. The inflammatory reaction observed with subcutaneous implants decreased during the period of analysis however, after 42 days MTA still had a discrete inflammatory reaction, this situation was not found with EBOB. Thus, it was concluded that EB has been shown to have similar biological and chemical properties compared with MTA, it also showed less tissue reaction and biocompatibility when tested in rat subcutaneous tissue.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-22052012-104541
Date20 April 2012
CreatorsAguilar, Fabiano Gamero
ContributorsSouza, Fernanda de Carvalho Panzeri Pires de
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0029 seconds