Orientadores: Cecilia Amelia de Carvalho Zavaglia, Eliana Aparecida de Rezende Duek / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-05T03:14:56Z (GMT). No. of bitstreams: 1
Barbantini_SamuelHilsdorf_D.pdf: 12141806 bytes, checksum: 0b989130cb636eca30c7bf3da9bc69f8 (MD5)
Previous issue date: 2005 / Resumo: A utilização de polímeros bioreabsorvíveis como suporte para cultura de células tem se destacado como alternativa para tratamento de lesões e perda de tecidos. O objetivo deste trabalho foi obter e caracterizar suportes densos e porosos de poli(E-caprolactona) (PCL) e poli(D,L-ácido lático-co-ácido glicólico) (50/50) (PLGA50), preparados pelo método de fusão com adição e
lixiviação de citrato de sódio. As amostras foram avaliadas em estudos de degradação in vitro para o estudo do efeito da retirada do sal, e em meio tampão fosfato (pH 7,4) e alcalino com NaOH (pH 12, 13 e 13,7). Os materiais foram utilizados como suporte para cultura de osteoblastos e o estudo in vivo foi realizado pelo implante em noia de ratos. Os resultados obtidos através de análises morfológicas, térmicas e de propriedades mecânicas, mostram que amostras de PCL são mais estáveis quando comparadas às suas análogas de PLGASO.A cultura de células mostrou um padrão de adesão e proliferação satisfatório, com intensa atividade celular. No estudo in vivo as amostras de PCL mostram uma degradação mais acentuada quando comparada com os resultados obtidos no estudo in vitro. Os resultados mostraram que a técnica utilizada no preparo das amostras é útil na confecção de suportes altamente porosos. Em função do tempo de degradação e das propriedades mecânicas, as amostras de PLGA5O foram os suportes mais indicados para aplicações na engenharia de tecidos ósseos / Abstract: The use of bioresorbable polymers as sca:ffolds for the cells culture has received special attention as an alternative for the treatment of lesions and the loss of tissue. The aim of this work was to obtain and to characterize dense and porous scaffolds of poly(e-caprolactone) (PCL) and poly(D,L-lactic acid-co-glycolic acid) (50/50) (PLGA50), prepared by melting method with addition
and leaching of sodium citrate. The samples were evaluated in studies of in vitro degradation, in phosphate bufIer solution (pH 7.4) and alkaline medium ofNaOH (pH 12, 13 and 13.7). Scaffolds samples were used in osteoblast culture and the in vivo study was evaluated by implant in mouse tibia. The results of morphologic, thermal and of mechanical analyses, showed that the PCL samples
are stable compared to their similar of PLGA50. The culture of cells showed a satisfactory adhesion and proliferation, with intense cellular activity. In the in vivo study, the samples of PCL showed a higher degradation when it is compared to the results obtained in vitro study. The results showed that the proposed technique allowed the preparation of highly porous scaffoldsa nd in function of
time degradation and mechanics properties, the samples of PLGA50 were the most suitable scaffolds for applications in the bone tissue engineering / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263597 |
Date | 15 July 2005 |
Creators | Barbantini, Samuel Hilsdorf |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Zavaglia, Cecília Amélia de Carvalho, 1954-, Duek, Eliana Aparecida de Rezende, 1961-, Freire, Celia Marina de Alvarenga, Costa, Necesio Gomes, Mei, Paulo Roberto, Genari, Selma Candelaria |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 157p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds