Indiana University-Purdue University Indianapolis (IUPUI) / Repair is an alternative treatment option in many cases to replacement of resin matrix composite restoration. However, aged resin matrix composites have a limited number of carbon-carbon double bonds to adhere to a new layer of rein. Therefore, surface treatments of the aged resin matrix composite surface prior to repairing could improve the repair bond strength.
The objectives of this study were to: 1) To evaluate various surface treatments on
shear bond strength of repair between aged and new microhybrid resin matrix composite, and 2) To assess the influence of applying a silane coupling agent after surface
treatments.
Eighty disk-shaped resin matrix composite specimens were fabricated and
thermocycled 5000 times prior to surface treatment. Specimens were randomly assigned to one of the three surface treatments (n = 20): 1) Airborne abrasion with 50 μm aluminum oxide, 2) Tribochemical silica coating (CoJet), or 3) Er,Cr:YSGG laser and control group (n = 20). Specimens were cleaned with 35-percent phosphoric acid, rinsed, and dried. Each group was assigned into two subgroups (n =10): a) no silanization, and b) with silanization. Adhesive agent was applied and new resin matrix composite was bonded to each conditioned surface. Bond strength was evaluated by shear test. Data were analyzed with a two-way ANOVA model. The interaction between conditioning and silanization was significant(p = 0.0163), indicating that comparisons of silanization must be evaluated for each conditioning method, and that comparisons of conditioning methods must be evaluated separately with and without silanization. Airborne particle abrasion showed significantly
higher repair bond strength than Er,Cr:YSGG laser without silanization (p < 0.0001) and with silanization(p = 0.0002), and higher repair bond strength than the control without silanization (p < 0.00001) and with silanization (p < 0.00001). Airborne particle abrasion
did not have significantly different in repair bond strength than Tribosilica coating without silanization (p = 0.70) or with silanization (p = 0.33). Tribosilica coating had significantly higher repair bond strength than Er,CR:YSGG laser without silanization
(p < 0.0001) and with silanization (p < 0.0001), and significantly higher repair bond strength than control without silanization (p < 0.0001), but not with silanization (p =0.16). Er,CR:YSGG laser and control did not have significantly different repair bond strength without silanization (p = 1.00) or with silanization (p = 0.11). There was no
effect of silanization on repair bond strength overall (p = 0.34) for any of the surface conditioning methods (p = 0.76 for airborne particle abrasion; p = 0.39 for tribosilica coating; p = 1.00 for Er,Cr:YSGG laser, or p = 0.39 for control). Airborne particle abrasion with 50-μm aluminum oxide particle and tribochemical silica coating followed by the application of bonding agent provided the highest shear bond strength values, suggesting that they might be adequate methods to improve the quality of the repairs of resin-matrix composites.
| Identifer | oai:union.ndltd.org:IUPUI/oai:scholarworks.iupui.edu:1805/2138 |
| Date | January 2010 |
| Creators | Rajitrangson, Phitakphong, 1982- |
| Contributors | Cochran, Michael A. (Michael Alan), 1944-, Cho, Sopanis D., Gonzalez-Cabezas, Carlos, 1966-, Matis, Bruce A., Platt, Jeffrey A., 1958- |
| Source Sets | Indiana University-Purdue University Indianapolis |
| Language | en_US |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0019 seconds