000831389.pdf: 2171410 bytes, checksum: 8516ec39315e5fd0cac80b4a540a7e3d (MD5) / Proposição: O objetivo do estudo foi avaliar o efeito da limpeza com ácido fosfórico após condicionamento da cerâmica e do tratamento térmico do silano na resistência de união de um cimento resinoso à cerâmica de dissilicato de lítio submetido ao envelhecimento. Método: Foram confeccionados sessenta e quatro blocos de cerâmica de dissilicato de lítio (IPS e-‐max CAD, Ivoclar Vivadent) e de resina composta (7x8x4mm). Os corpos de prova foram divididos aleatoriamente em 4 grupos (n=16) que receberam os seguintes tratamentos: HFS (grupo controle): ácido fluorídrico 10 % e silano; HFPS: ácido fluorídrico, ácido fosfórico 37% e silano; HFSa: ácido fluorídrico e silano aquecido (45◦C ± 5◦C); HFPSa: ácido fluorídrico, ácido fosfórico e silano aquecido. Os espécimes foram cimentados com um cimento resinoso dual, posteriormente os corpos de prova foram divididos em duas condições de envelhecimento (n=8): N - sem envelhecimento e TC: termociclagem 12.000X, 5◦C - 55 ◦C. Foram submetidos ao teste de microtração em uma máquina de testes com velocidade de 0,7mm/min. As superfícies fraturadas foram examinadas para determinar o modo de falha. Os dados estatísticos foram analisados através da Anova de 2 fatores e as médias comparadas por meio do teste Tukey (p< 0.05). Resultados: o grupo HFSa envelhecido apresentou o maior valor de resistência de união (21,49 ± 2,29 MPa), entretanto, sem diferença estatística para o grupo controle (p<0,05). Não houve diferença estatisticamente significante entre as amostras envelhecidas e não envelhecidas, entretanto, foi observada uma diferença estatisticamente significante no grupo HFSa. (p<0,05). Importância: O tratamento térmico do silano e a limpeza pós-‐condicionamento com ácido fosfórico não potencializou a resistência de união da cerâmica à resina / Purpose: The aim of this study was to evaluate the effect of cleaning with phosphoric acid after etching of ceramic and heat treatment of the silane with a stream of hot air on the bond strength of a resin cemente to lithium dissiliacte ceramic submitted to aging. Method: Sixty-‐four blocks-‐ceramic lithium silicate (IPS e-‐max CAD, Ivoclar Vivadent) and composite resin were fabricated (7x8x4mm). The specimens were randomly divided into 4 groups (n = 16) that received the following treatments: HFS (control group): 10% hydrofluoric acid and silane; HFPS: hydrofluoric acid, 37% phosphoric acid and silane; HFSA: hydrofluoric acid and silane heated (45 ◦ C ± 5 ◦ C); HFPSa: hydrofluoric acid, phosphoric acid and heated silane. The specimens were cemented with a dual resin cement, later the specimens were divided into two aging conditions (n = 8): N -‐ no aging and TC: thermocycling, 12,000 x 5◦C -‐ 55◦C. They were submitted to microtensile test in a testing machine with a speed of 0.7 mm / min. Fractured surfaces were examined to determine the failure mode. Statistical data were analyzed by ANOVA with 2 factors and the averages compared by Tukey test (p <0,05). Results: The group HFSa aged showed the highest bond strength (21.49 ± 2.29 MPa), however, without statistical difference for the control group. There was no statistically significant difference between aged and non-‐aged samples, except for, a statistically significant difference in the HFSA group (p <0.05). Significance: The heat treatment of the silane and cleaning after etching with phosphoric acid did not increase the bond strength of ceramic resin
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/123678 |
| Date | 03 July 2014 |
| Creators | Hipólito, Ana Carolina [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Assunção, Wirley Gonçalves [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 107 f : il. + 1 CD-ROM |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0026 seconds