Orientador: Antonio Ludovico Beraldo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agricola / Made available in DSpace on 2018-08-08T10:50:49Z (GMT). No. of bitstreams: 1
Jose_FlavioJanuario_M.pdf: 4963085 bytes, checksum: 7b25d4ec4eb8715ae3a3a7150fea863d (MD5)
Previous issue date: 2006 / Resumo: A pesquisa sobre o tema ¿Chapa de Partículas Homogêneas de Bambu aglomeradas com Resina Poliuretana à Base de Óleo de Mamona¿ teve como finalidade a confecção e a avaliação de chapas de partículas homogêneas aglomeradas, utilizando-se de dois materiais alternativos considerando a sustentabilidade do processo produtivo. Foram utilizadas partículas de Bambusa vulgaris devido à rapidez de crescimento dessa espécie de bambu, e da possibilidade de ser cultivado em praticamente todo o território brasileiro. Como adesivo foi utilizada a resina poliuretana à base de óleo de mamona, por ser de origem parcialmente renovável e, ao contrário dos adesivos convencionais, ser considerada não tóxica. Para a caracterização do material estudado, foram produzidas, em escala de laboratório, chapas cujas partículas de bambu utilizadas na sua composição, apresentaram espessura inferior a 2,4 mm, e aglomeradas com 5%, 10% e 15% de resina em relação à massa de partículas de bambu. Corpos-de-prova foram submetidos a ensaios físicos (controle de espessura, densidade, absorção de água e inchamento) e mecânicos (arrancamento de parafuso da superfície e do topo, dureza Janka, compressão longitudinal, flexão estática e tração perpendicular, segundo as recomendações da NBR 14810 - Chapas de madeira aglomerada). Corpos-de-prova destinados ao ensaio de compressão longitudinal também foram avaliados por meio de ensaio não destrutivo (END) por ultra-som. Os resultados obtidos foram comparados estatisticamente, sendo que o teor de resina em relação à massa de partículas de bambu afetou as propriedades físicas e mecânicas das chapas. O teor de 10% de resina não diferiu estatisticamente do teor 15%, sendo ambos superiores ao teor 5%. Embora o END tenha sido sensível para detectar o efeito dos teores de resina na velocidade do pulso ultra-sônico (VPU) através dos corpos-de-prova, não foi possível correlacionar a VPU com a resistência à compressão longitudinal. Para a maioria das propriedades avaliadas houve diferença estatística entre as chapas com 10% de resina e chapas de aglomerado cru disponíveis comercialmente, sendo que as chapas de aglomerado cru demonstraram resultados superiores, com exceção ao ensaio de inchamento em 24 h / Abstract: The aim of this research ¿Homogeneous Particleboard of Bamboo Bonded whith Poliurethane Resin Castor Oil Based¿ was to manufacture and to evaluate particleboards made with two alternative materials, looking for the productive process sustainability. Particles from Bambusa vulgaris were employed due to the its fast production cycle and its availability in Brazilian country. Poliurethane resin castor oil based was employed as a binder because it is parcially produced by a renewable source and its low toxicity. For the material caracterization it was manufactured at laboratory scale boards from bamboo particles smaller than 2.4 mm combined with 5%, 10% e 15% of resin in relation to the bamboo particles mass. Specimens were submited to physical (thickness control, density, water absorption and swelling after 2 hrs and 24 hrs of imersion in water) and mechanical (nail withdraw on surface and top, Janka hardness, longitudinal compression strength, static bending and internal bond) evaluations according to the Brazilian Standard NBR 14810 ¿ Boards of agglomerate wood. Specimens evaluated in longitudinal compression were previously tested through a Non Destructive Evaluation (NDE) by ultrasonic method. The results were statistically compared and showed that resin content related to bamboo particles afected the physical and mechanical board properties. 10% resin content was not statiscally different of 15% resin content, both superior to 5% resin content. Nevertheless NDE has been sensible to detect resin content effect on ultrasonic pulse velocity (UPV) across the specimens it was not possible to correlate with longitudinal compression strength. In most of the properties evaluated there was a statistical difference between bamboo particles boards with 10% resin content and the commercial agglomerated boards, being the commercial agglomerated boards demonstrated superior results, with exception to the swelling after 24 hrs / Mestrado / Construções Rurais e Ambiencia / Mestre em Engenharia Agrícola
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/257014 |
| Date | 23 February 2006 |
| Creators | Jose, Flavio Januario |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Beraldo, Antônio Ludovico, 1951-, Freire, Wesley Jorge, Nascimento, Maria Fatima do, Pereira, Marco A. dos Reis |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Agrícola, Programa de Pós-Graduação em Engenharia Agrícola |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 103f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0037 seconds