DISSERTAÇAO ENCADERNADA 12-6-2014.pdf: 3478342 bytes, checksum: ef9c094eab174182a86dc044604a2113 (MD5) / A construção civil é o principal consumidor de recursos naturais do planeta e um dos maiores desafios contemporâneos é conciliar esta demanda com o desenvolvimento sustentável. Portanto, a utilização de materiais alternativos pode contribuir para minimizar os impactos ambientais e, ainda, melhorar a qualidade dos materiais. Neste trabalho, avaliou-se o comportamento do resíduo de corte de mármore e granito (RCMG), quando adicionado às argamassas comuns de cimento Portland, mistas (cimento e cal) e industrializadas, nos teores de 5% 10% e 15% em relação à massa de cimento. Como parâmetro, foi fixada a relação água/cimento em 0,59 e as argamassas foram analisadas nos estados fresco, endurecido e aplicado, assim como a durabilidade dessas. No primeiro, foram determinados: a densidade de massa, o teor de ar incorporado, a retenção de água e as propriedades reológicas foram avaliadas por meio dos ensaios de abatimento de tronco de cone (flow table), squeeze-flow e reometria. No estado endurecido, foram realizados ensaios para a determinação das propriedades mecânicas (resistência à tração na flexão, à compressão axial e à tração por compressão diametral) e físicas (absorção de água por capilaridade, absorção de água, índice de vazios, massa específica e velocidade de propagação de onda ultrassônica). No estado aplicado, foram realizados ensaios aos 28 dias, de acordo com a normalização nacional, para determinação da dureza superficial por meio do esclerômetro de reflexão, além da resistência de aderência à tração e da absorção de água sob baixa pressão (pipeta de Kirsten). A durabilidade foi avaliada mediante os ensaios de expansibilidade de Le Chatelier e reatividade álcali-agregado (RAA). Os resultados obtidos indicaram que o melhor teor de adição para as argamassas simples e mistas foi de 10% de RCMG e para as argamassas industrializadas foi de 5% de RCMG, atestando que este pode ser utilizado como filler em matrizes cimentícias. / Construction is the main consumer of planet´s natural resources, and one of the greatest challenges nowadays is to conciliate its demand with sustainable development. Therefore, the use of alternative materials can contribute to minimize environmental impacts and to improve the quality of the materials. In this paper, the behavior of Portland cement mortars was evaluated (simple blended, mixed blended - cement and lime – and industrialized) , when both waste marble and granite dust (WMGD) were mixed together, in amounts of 5%, 10% and 15% of cement mass. The water/cement ratio was set at 0.59 and the mortars were analyzed at fresh, hardened and applied states, and their durability was also analysed. At first the mass density, air content and water retention were determined. Then the rheological behavior was evaluated by the flow table, squeeze-flow and the rheometry. In the hardened state, tests were performed to determine the mechanical properties (flexural strength, compressive strength and diametric compression strength) and physical properties (water absorption, void ratio, density and velocity of ultrasonic wave). In applied state, tests were realized in 28 days, in accordance with Brazilian national standards, to determine superficial hardness through sclerometer, beyond tensile bond strength and water absorption under low pressure (pipette Kirsten). The durability was assessed by Le Chatelier expansion and alkali-aggregate reactivity (AAR). The results indicated that the best content added for simple and mixed mortars was 10% WMGD and for industrialized mortars was 5% WMGD, stating that it can be used as filler in cement matrices.
| Identifer | oai:union.ndltd.org:IBICT/oai:192.168.11:11:ri/15276 |
| Date | 17 March 2014 |
| Creators | Apolinário, Elenice Carmo de Abreu |
| Contributors | Ribeiro, Daniel Véras, Silva, Vanessa Silveira, Morelli, Marcio Raymundo, Lima, Paulo Roberto Lopes |
| Publisher | Universidade Federal da Bahia. Escola Politécnica, Engenharia Ambiental Urbana, UFBA, brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFBA, instname:Universidade Federal da Bahia, instacron:UFBA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds