Previous issue date: 2015-04-29 / Voltado para prática da sustentabilidade na construção civil, propõe-se o uso de
vidro plano temperado, fragmentado, em substituição à pedra britada em
concretos em percentuais de substituição de 0%, 50% e 100%. O trabalho teve
como objetivo a análise microestrutural de concretos com traços fixados em 1:3,
fatores água/cimento de 0,45, 0,55 e 0,65, submetidos à cura em câmara úmida
saturada de hidróxido de cálcio nas idades de 7, 28 e 91 dias. As matériasprimas foram caracterizadas através de análise granulométrica. Os concretos no
estado fresco foram classificados através de abatimento por tronco de cone. Os
concretos de referência obtiveram classes desde S10 a S160, enquanto que os
concretos com adição de vidro variaram de S50 a S220. Os corpos de prova
cilíndricos, com dimensões 5 cm x 10 cm, foram submetidos à ensaios de
resistência à compressão simples (RCS). Os concreto de referência (0% de
vidro) se classificaram com classe de resistência C20 e C25. Já os concretos
com percentual de substituição de 50% tevesua classe de resistência variando
do C15 ao C30, enquanto que os de 100% de vidro, classes C15 e C20.
Empregou-se para o estudo do nível de adesão, na interface vidro/pasta,
imagens obtidas via microscopia ótica digital USB, além de microscopia
eletrônica de varredura, constatando-seinterfaces bem preservadas mesmo
após ruptura sob compressão. Utilizou-se difração de Raios-X constatando-se
estruturas semelhantes para os diversos valores intervenientes e média geral de
cristalinidade superior a 94%. Através de microanálise por energia dispersiva
constatou-se que os concretos com percentuais parcial e total tem natureza
química semelhante ao concreto de referência. Os valores de RCS e o
comportamento do vidro como agregado graúdo permitem o emprego desse
concreto em aplicações estruturais, como lajes e pilares, e aplicações não
estruturais, a exemplo de pavimentos e pisos. / Aiming at sustainability practices in civil construction, it isproposed the use of
fragmented, flat tempered glass replacing the crushed stone in concrete in
replacement percentages of 0%, 50% and 100%. The research aimed at the
microstructural analysis in concrete with traces fixed in 1:3, water/cement factors of
0.45, 0.55 and 0.65, and replacement percentage of 0%, 50% and 100%, subjected
to curing in a saturated, calcium-hydroxide humid chamber at the ages of 7, 14 and
28 days. The raw materials were characterized by particle size analysis. The
concrete in the fresh state was classified in rebate by conical frustum. The concrete
of reference obtained classes from S10 toS160, whereas the concrete with glass
addition ranged from S50 to S220. The cylindrical specimens with dimensions of 5
cm x 10 cm underwent strength tests in simple compression(RCS). The concrete of
reference(0% of glass) were qualified with resistance class of C20 and C25, and the
resistance class of the concrete with replacement rate of 50% ranged from C15 to
C30, whereas the class of the concrete with the rate of 100% ranged from C15 to
C20. To the study of the adhesion level in the glass/pasteinterface, there were used
images that were obtained via USB digital microscopy and scanning electron
microscope, noting well preserved interfaces even after rupture under compression.
It was used x-ray diffraction in the process, noting similar structures for the various
factors and crystallinity average value greater than 94%. Using dispersive energy
microanalysis, it was discovered that the concrete with partial and full percentage has
its chemical nature similar to the concreteof reference. The values of RCS and the
behavior of glass as coarse aggregate permit the use of concrete in structural
applications such as slabs and pillars, and in non-structural ones, like in pavings and
floors.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1031 |
Date | 22 June 2018 |
Creators | SILVA, José Glêdson de Sousa. |
Contributors | MORAIS, Crislene Rodrigues da Silva., FERREIRA, Heber Carlos., MAIA, Divanira Ferreira., CAVALCANTI, Maria do Socorro Lopes., AQUINO, José Lourenço Santos. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds