4H-SiC-based bipolar junction transistors (BJTs) are attractive devices for high-voltage and high-temperature operations due to their high current capability, low specific on-resistance, and process simplicity. To extend the potential of SiC BJTs to power electronic industrial applications, it is essential to realize high-efficient devices with high-current and low-loss by a reliable and wafer-scale fabrication process. In this thesis, we focus on the improvement of the 4H-SiC BJT performance, including the device optimization and process development. To optimize the 4H-SiC BJT design, a comprehensive study in terms of cell geometries, device scaling, and device layout is performed. The hexagon-cell geometry shows 42% higher current density and 21% lower specific on-resistance at a given maximum current gain compared to the interdigitated finger design. Also, a layout design, called intertwined, is used for 100% usage of the conducting area. A higher current is achieved by saving the inactive portion of the conducting area. Different multi-step etched edge termination techniques with an efficiency of >92% are realized. Regarding the process development, an improved surface passivation is used to reduce the surface recombination and improve the maximum current gain of 4H-SiC BJTs. Moreover, wafer-scale lift-off-free processes for the n- and p-Ohmic contact technologies to 4H-SiC are successfully developed. Both Ohmic metal technologies are based on a self-aligned Ni-silicide (Ni-SALICIDE) process. Regarding the device characterization, a maximum current gain of 40, a specific on-resistance of 20 mΩ·cm2, and a maximum breakdown voltage of 5.85 kV for the 4H-SiC BJTs are measured. By employing the enhanced surface passivation, a maximum current gain of 139 and a specific on-resistance of 579 mΩ·cm2 at the current density of 89 A/cm2 for the 15-kV class BJTs are obtained. Moreover, low-voltage 4H-SiC lateral BJTs and Darlington pair with output current of 1−15 A for high-temperature operations up to 500 °C were fabricated. This thesis focuses on the improvement of the 4H-SiC BJT performance in terms of the device optimization and process development for high-voltage and high-temperature applications. The epilayer design and the device structure and topology are optimized to realize high-efficient BJTs. Also, wafer-scale fabrication process steps are developed to enable realization of high-current devices for the real applications. / <p>QC 20170810</p>
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-211659 |
Date | January 2017 |
Creators | Elahipanah, Hossein |
Publisher | KTH, Elektronik, Stockholm |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | TRITA-ICT ; 2017:14 |
Page generated in 0.003 seconds