Orientador: Monica Campos Serra / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T00:07:36Z (GMT). No. of bitstreams: 1
Magalhaes_ClaudiaSilamide_M.pdf: 2310367 bytes, checksum: abc110f4c4d7e29799ce02a031a83b58 (MD5)
Previous issue date: 1997 / Resumo: O objetivo deste estudo "in vitro" foi avaliar quantitativamente a microinfiltração em cavidades de classe V restauradas com materiais híbridos de ionômero de vidro/resina composta, comparando-os com um cimento de ionômero de vidro e com um sistema de resina composta/adesivo dentinário. Foram preparadas cavidades cilíndricas na superfície radicular de 105 dentes humanos extraídos, a cerca de 4 mm da junção amelo-cemeotária. Os dentes foram divididos aleatoriamente em cinco grupos, cada um contendo 21 unidades experimentais. Os grupos controles foram restaurados com um cimento de ionômero de vidro ou com um sistema de resina composta/adesivo dentinário. Os grupos experimentais foram restaurados com três materiais híbridos de ionômero de vidro/ resina composta, sendo dois cimentos de ionômero de vidro modificados por resina e uma resina composta modificada por poliácido. Todos os dentes foram termociclados por 500 vezes, entre temperaturas de 5 ± 2 °C e 55 ± 2 °C, com um tempo de permanência de 1 minuto em cada banho. Em seguida, os espécimens foram imersos em solução aquosa de azul de metileno a 2%, por 24 horas, a 37 °C. A microinfiltração foi quantificada através de espectrofotometria e expressa em micrograma de corante por mililitro de solução. A análise estatística dos dados não indicou diferença significante entre os materiais (^2=5,37, a > 0,05). Sob as condições experimentais utilizadas neste estudo, pôde-se concluir que o desempenho dos materiais híbridos de ionômero de vidro/resina composta, frente à microinfiltração, foi similar ao do cimento de ionômero de vidro e ao do sistema de resina composta/adesivo dentinário / Abstract: The purpose of this "in vitro" study was to quantify the marginal leakage of three glass ionomer - composite resin hybrid materials in dentin cavities, compared with a glass ionomer cement and a bonded composite resin system. Standardized cylindrical class V cavities were prepared on root fecial surface of 105 extracted human uniradicular teeth, about 4 mm below the CEJ. The teeth were randomly assigned into five groups of 21 each. Control groups were restored with either a glass-ionomer cement or a bonded composite resin system. The experimental groups were restored with three glass-ionomer composite resin hybrid materials. All materials were manipulated according to manufacturers' instructions. The teeth were stored in distilled water at 37" C for 24 hours. After this storage period, the restorations were finished and polished with abrasive discs. All teeth were thermally stressed for 500 cycles with a dwell time of 1 min at 5° + 2 °C and 55° ± 2 °C, and subjected to dye penetration test (2 % methylene blue at 37 °C for 24 hours). The microleakage was quantified by spectrophotometry and was expressed as ja.g dye / mL. Statistical analysis indicated no significant differences among the five groups (x2-5.37, a > 0,05). Hence, it was concluded that glass ionomer -composite resin hybrid materials, glass ionomer cement and bonded composite resin system microleakage performances were similar, under the experimental conditions / Mestrado / Dentística / Mestre em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288308 |
Date | 14 November 1997 |
Creators | Magalhães, Claudia Silami de |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Serra, Mônica Campos, 1964-, Pimenta, Luiz Andre Freire, Candido, Maria Salete Machado |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 85f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0081 seconds