Comparación in vitro de la resistencia a la compresión y resistencia flexural de resinas Bulk Fill (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill) / In vitro comparison of the compressive strength and flexural strength of Bulk Fill resin composite (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y FiltekTM Bulk Fill).

Objetivo: Comparar in vitro la resistencia a la compresión y resistencia flexural de resinas Bulk Fill (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill)
Materiales y métodos: Se confeccionaron 132 especímenes en total: G1/G5: Opus™ Bulk Fill, G2/G6: Tetric® N-Ceram Bulk Fill, G3/G7: FiltekTM Bulk Fill y G4/G8: FiltekTM Z350XT (grupo control). Cincuenta y seis especímenes cilíndricos (3x5mm) para evaluar la resistencia a la compresión, divididos en 4 grupos (n=14): G1, G2, G3 y G4 y setenta y seis especímenes rectangulares para evaluar la resistencia flexural, divididos en 4 grupos (n=19): G5, G6, G7 y G8. Las pruebas mecánicas se realizaron en una máquina de ensayo universal Instron® con una carga de 100kN a 1mm/1min (Resistencia Compresiva) y una velocidad de 1mm/1min (Resistencia Flexural). El análisis de datos se realizó mediante estadística descriptiva e inferencial (test de Kruskal Wallis /prueba post hoc).
Resultados: Para la resistencia a la compresión, los resultados fueron: G1 (141.68 MPa ± 22.20), G2 (139.03 MPa ± 23.56), G3 (235.59 MPa ± 26.08) y G4 (99.28 MPa±11.36). Se encontró diferencias estadísticamente significativas entre todas las resinas evaluadas (p<0.001). Para resistencia flexural los resultados fueron: G5 (116.29 MPa ± 7.20), G6 (109.67 MPa ± 7.58), G7 (200.53 MPa ± 10.32) y G8 (90.08 MPa ± 8.63). Se encontró diferencias estadísticamente significativas entre todas las resinas evaluada (p<0.001).
Conclusiones: La resina Filtek™ Bulk Fill presentó mayor resistencia a la compresión y flexural en relación a las resinas evaluadas. / Objective: Compare in vitro the compressive strength and flexural strength of Bulk fill resin composite (Opus™ Bulk Fill, Tetric® N-Ceram Bulk Fill y Filtek™ Bulk Fill).
Method and materials: 132 specimens were made: G1/G5: Opus™ Bulk Fill, G2/G6: Tetric® N-Ceram Bulk Fill, G3/G7: FiltekTM Bulk Fill y G4/G8: FiltekTM Z350XT (control group). Fifty-six cylindrical samples (3x5mm) to evaluate the compressive strength, divided in 4 groups (n=14): G1, G2, G3 y G4 and seventy-six rectangular samples to evaluate flexural strength, divided in 4 groups (n=19): G5, G6, G7 y G8. The mechanical tests were made with the Instron® Universal Testing Machine at crosshead speed of 1.0 mm/min with a load of 100 kN to compressive strength and at crosshead speed of 1.0 mm/min to flexural strength.
The data analysis was performed by descriptive and inferential statistics (test de Kruskal Wallis /test post hoc).
Results: For the compressive strength, the results were: G1 (141.68 MPa± 22.20), G2 (139.03 MPa ± 23.56), G3 (235.59 MPa ± 26.08) y G4 (99.28MPa±11.36). Statistically significant differences were found between all the groups (p> 0.001). For flexural strength the results were: G5 (116.29MPa ± 7.20), G6 (109.67 MPa ± 7.58), G7 (200.53 MPa ± 10.32) y G8 (90.08 MPa ±8.63). Statistically significant differences were found between all the groups (p> 0.001).
Conclusion: Filtek ™ Bulk Fill resin composite showed greater compressive and flexural strength in comparison to the other resins evaluated. / Tesis

Identiferoai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/624900
Date05 December 2018
CreatorsBorja Farfán, Norma Elizabeth, Loyola Livias, Oscar Danilo
ContributorsHermoza Novoa, Mónica
PublisherUniversidad Peruana de Ciencias Aplicadas (UPC)
Source SetsUniversidad Peruana de Ciencias Aplicadas (UPC)
LanguageSpanish
Detected LanguageSpanish
Typeinfo:eu-repo/semantics/bachelorThesis
Formatapplication/pdf, application/epub, application/msword
SourceUniversidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico - UPC
Rightsinfo:eu-repo/semantics/embargoedAccess, Attribution-NonCommercial-ShareAlike 3.0 United States, http://creativecommons.org/licenses/by-nc-sa/3.0/us/

Page generated in 0.0025 seconds