Porous Metal Oxides and Their Applications

Porous metal oxides formed by supercritical carbon dioxide (SCCO2) treatments at low temperature were used for displays, solar cells, and light emitting diodes (LEDs) applications. The SCCO2 fluid, also known as green solvents, exhibits low viscosity, low surface tension and high diffusivity as gases, and high density and solubility same with liquids. In this thesis, we successfully fabricated porous antimony-doped tin oxide (ATO) and porous indium tin oxide (ITO) by the SCCO2 treatments. In addition, the treatment can also be used to improve the work function and surface energy of ITO anode of an organic LED (OLED). The performance of the OLEDs was drastically enhanced in comparison with that of the devices without any ITO surface treatments.
First, the porous ATO films were formed by the SCCO2 treatment for absorption of silver molecules in silver electro deposition devices. The porosity, resistivity and average optical transmittance of the porous ATO film in visible wavelength were 43.1%, 3 £[-cm and 90.4%, respectively. For the silver electro deposition devices with the porous ATO film, the transmittance contrast ratio of larger than 12 in visible spectrum was obtained at an operating voltage of 1.5 V. Furthermore, for the 0.25 cm2 device, the switching time of 4.5 seconds was achieved by applying a square-wave voltage ranging from 1.5 to -0.2 V between the electrodes.
On the other hand, the porous ITO with low refractive index was prepared by SCCO2/IPA treatment on gel-coated ITO thin films. The high refractive index of the ITO film was achieved by long-throw radio-frequency magnetron sputtering technique at room temperature. The index contrast (£Gn) was higher than 0.6 between porous ITO and sputtered ITO films. The large £Gn is useful for fabricating conductive anti-reflection (AR) and high reflection (HR) structures using the porous ITO on sputtered ITO bilayers. The weighted average reflectance and transmittance of 4.3% and 83.1% were achieved for the double-layer ITO AR electrode with a sheet resistance of 1.1 K£[/¡E. For HR structures, the reflectance and sheet resistance were 87.9% and 35 £[/¡E with 4 periods ITO bilayers.
Finally, the SCCO2 treatments with strong oxidizer H2O2 were proposed to modify surface property of ITO anode of a fluorescent OLED. The highest work function and surface energy of 5.5 eV and 74.8 mJ/m2 was achieved by the SCCO2/H2O2 treatment. For the OLED with 15 min SCCO2 treatment at 4000 psi, the turn-on voltage and maximum power efficiency of 6.5 V and 1.94 lm/W were obtained. The power efficiency was 19.3% and 33.8% higher than those of the OLEDs with oxygen plasma treated and as-cleaned ITO anodes.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0715112-155903
Date15 July 2012
CreatorsTien, Wei-Chen
ContributorsPo-Chun Liu, Ann-Kuo Chu, Yi-Jen Chiu, Chao-Kuei Lee, Ting-Chang Chang, Dong-Sing Wuu, Ray-Hua Horng
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0715112-155903
Rightsuser_define, Copyright information available at source archive

Page generated in 0.002 seconds