Desenvolvimento e caracterização de filmes compostos de alginato e quitosana contendo natamicina como agete antimicotico / Development and characterization of alginate and chitosan composite films containing natamycin as antimiotic agent

Orientador: Theo Guenter Kieckbusch / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-13T22:35:30Z (GMT). No. of bitstreams: 1
Silva_MarianaAltenhofenda_D.pdf: 13012501 bytes, checksum: 23a63960ceb6cf8d4c7d9672c06f5d58 (MD5)
Previous issue date: 2009 / Resumo: Filmes simples de alginato (FA) e filmes compostos de alginato e quitosana nas proporções 82,5:17,5 (FC1) e 65:35 (FC2), de baixo grau de reticulação com cálcio (0,04 g CaCl2.2H2O/g alginato) contendo glicerol como plastificante, foram confeccionados pela técnica de casting. Esses filmes foram submetidos a uma reticulação complementar por imersão durante 30 minutos em uma solução contendo 5g CaCl2.2H2O/100 mL. Filmes FA, FC1 e FC2 com espessura média de 48, 54 e 62 µm, respectivamente, apresentaram massa solubilizada em água de 0,15, 0,19 e 0,23 g/g massa seca, coeficientes de permeabilidade ao vapor de água de 4,04, 4,91 e 7,41 g.mm/m2.dia.kPa, intumescimento em água de 68, 102 e 195% (em massa), tensão na ruptura de 96, 75 e 59 MPa e alongamento na ruptura de 8,4, 12,5 e 17,1%. Esses valores assim como o conteúdo de cálcio e os espectros de FTIR indicaram que, nas condições experimentais utilizadas, a interação do alginato com os íons cálcio foi mais efetiva do que com a quitosana, não havendo indícios de formação de ligação amídica entre o alginato e a quitosana. A análise da Tg por DMA também indicou separação de fases entre os dois polímeros. Os filmes com 35% de quitosana apresentaram estrutura polimérica mais rugosa e heterogênea. As três formulações receberam sorbato de potássio (até 17 g/100g biopolímero) e natamicina (0, 0,5, 1, 2, 4 e 8 g/100g biopolímero) como agentes antimicrobianos, e o efeito antimicótico destes filmes frente às espécies Penicillium roqueforti, Penicillium commune e Debaromyces hansenii foi avaliado através do teste de difusão em ágar. O sorbato de potássio não apresentou efeito inibitório, e a natamicina foi eficiente a partir da concentração de 0,5 g/100g biopolímero para o filme de alginato puro e 1 g/100g biopolímero para os filmes compostos. Ensaios de liberação em água indicaram uma cinética muito lenta de liberação do antimicrobiano, sendo mais lenta para os filmes compostos, provavelmente devido à interações eletrostáticas entre a natamicina e a quitosana. Os coeficientes de difusão da natamicina encontrados foram da ordem de 10-11 cm2/s para FA e FC2 e de 10-12 cm2/s para FC1. A estrutura física menos compacta da matriz polimérica do FC2 acelerou a liberação da natamicina. Nas concentrações testadas, a adição da natamicina influenciou principalmente a cor, transparência, rugosidade e morfologia dos filmes. Os resultados obtidos permitem afirmar que os filmes desenvolvidos contendo natamicina apresentam excelente perspectiva de atuação como filmes ativos (antimicrobianos) para alimentos / Abstract: Films composed solely by alginate (FA) and two composite films with different mass proportions of alginate and chitosan, 82.5:17.5 (FC1) and 65:35 (FC2), were obtained by casting. Using glycerol as plasticizer, the films were partially crosslinked by adding calcium chloride (0.04 g CaCl2.2H2O/g alginate) to the film forming solution. The resulting soluble films were further crosslinked by total immersion in a CaCl2 solution (5g CaCl2.2H2O/100 mL) for 30 minutes. FA, FC1 and FC2 with an average thickness of 48, 54 and 62 µm, respectively, exhibited soluble mass in water of 0.15, 0.19 and 0.23 g/g dry matter, water vapor permeability coefficient of 4.04, 4.91 and 7.41 g.mm/m2.day.kPa, swelling in water of 68, 102 and 195% (mass basis), tensile strength of 96, 75 and 59 MPa and elongation at break of 8.4, 12.5 and 17.1%. The tendencies found for the physical properties, complemented with values of calcium content in the films and results of FTIR analysis indicated that under the experimental conditions used, ionic binding of alginate chains with calcium ions was more effective than with chitosan, and no evidence of amidic bonding between alginate and chitosan was found. DMA thermograms also indicated phase separation between the two polymers, showing two Tg's for composite films. Films with higher content of chitosan showed rougher surfaces and less homogeneous polymeric structure. The film formulations received potassium sorbate (up to 17 g/100g biopolymer) and natamycin (0, 0.5, 1, 2, 4 and 8 g/100g biopolymer) as antimicrobial agents, and their antimycotic effect against Penicillium roqueforti, Penicillium commune and Debaromyces hansenii was evaluated by the agar diffusion test. Potassium sorbate did not show inhibitory effect. Natamycin was effective at concentrations as low as 0.5 g/100g biopolymer for alginate film and 1 g/100g biopolymer for composite films. Diffusion experiments in water indicated very slow release kinetics of the antimicrobial, being markedly hindered for the composite films, probably due to electrostatic interactions between chitosan and natamycin. Diffusion coefficients in films were in the order of 10-11 cm2/s for FA and FC2, and 10-12 cm2/s for FC1. The addition of natamycin affected mainly the color, transparency, roughness and morphology of the films, in the tested concentration range. The results showed that the films containing natamycin obtained in the present work show excellent perspectives for acting as active films intended for food applications / Doutorado / Engenharia de Processos / Doutor em Engenharia Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266051
Date13 August 2018
CreatorsSilva, Mariana Altenhofen da
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Kieckbusch, Theo Guenter, 1942-, Soares, Nilda de Fatima Ferreira, Carvalho, Rosemary Aparecida de, Taniwaki, Marta Hiromi, Moraes, Ângela Maria
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format224 p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds