The germylenes, germanium(II) 2-(oxidomethyl)phenolate (1), germanium(II) 4-methyl-2-(oxidomethyl)phenolate (2) and germanium(II) 4-bromo-2-(oxidomethyl)phenolate (3) were synthesized and their thermally induced twin polymerization to give organic–inorganic hybrid materials was studied. The compounds 1–3 form oligomers including dimers, trimers and tetramers as a result of intermolecular coordination of the benzylic oxygen atom to germanium. The structural motifs were studied by single crystal X-ray diffraction analysis and DFT-D calculations. Thermally induced twin polymerization of these germylenes gave hybrid materials based on germanium-containing phenolic resins. Carbonization of these resins under reductive conditions resulted in porous materials that are composed of germanium and carbon (Ge@C materials), while oxidation with air provided non-porous germanium dioxide. The porous Ge@C materials were tested as potential anode materials for rechargeable Li-ion batteries. Reversible capacities of 540 mA h g−1 were obtained at a current density of 346 mA g−1 without apparent fading for 100 cycles, which demonstrates that germanium is well accessible in the hybrid material. / Dieser Beitrag ist aufgrund einer (DFG-geförderten) Allianz- bzw. Nationallizenz frei zugänglich.
Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:ch1-qucosa-197302 |
Date | 08 February 2016 |
Creators | Kitschke, Philipp, Walter, Marc, Rüffer, Tobias, Seifert, Andreas, Speck, Florian, Seyller, Thomas, Spange, Stefan, Lang, Heinrich, Auer, Alexander A., Kovalenko, Maksym V., Mehring, Michael |
Contributors | TU Chemnitz, Fakultät für Naturwissenschaften, Royal Society of Chemistry, |
Publisher | Universitätsbibliothek Chemnitz |
Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
Language | English |
Detected Language | English |
Type | doc-type:article |
Format | application/pdf, application/pdf, text/plain, text/plain, application/pdf, application/zip |
Source | J. Mater. Chem. A, 2016, Advance Article DOI: 10.1039/C5TA09891B |