Behavior of cutting tool coating material Ti<sub>1-x</sub>Al<sub>x</sub>N at high pressure and high temperature / Faser i Ti<sub>1-x</sub>Al<sub>x</sub>N-ytbeläggningar vid högt tryck och hög temperatur

<p>The high pressure and high temperature (HPHT) behavior of Ti<sub>1-x</sub>Al<sub>x</sub>N coatings on cutting tool inserts have been of interest for this diploma work. A literature study of HPHT techniques as well as measurement methods has been done. A diamond anvil cell (DAC) would be a good device to achieve high pressure and high temperature conditions on small samples. Another way to obtain these conditions would be a cutting test, which has been performed on a Ti<sub>1-x</sub>Al<sub>x</sub>N coated cutting tool insert with x = 0.67. Also a cubic press could be used to apply HPHT on a     Ti<sub>1-x</sub>Al<sub>x</sub>N sample or a large volume press on a whole cutting tool insert. To measure hardness on thin coatings a nanoindentor could be used, which have been done on heat-treated Ti<sub>0.33</sub>Al<sub>0.67</sub>N and TiN samples. X-ray diffraction (XRD) is a suitable method to measure phase composition of a sample and was performed on the cutting tested insert as well as on an untreated reference insert. Three ways to continue this project have been outlined all starting with more comprehensive cutting tests.</p>

Identiferoai:union.ndltd.org:UPSALLA/oai:DiVA.org:liu-52773
Date January 2009
CreatorsDilner, David
PublisherLinköping University, Department of Physics, Chemistry and Biology
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, text

Page generated in 0.0016 seconds