In this dissertation were studied powders and pellets of the CayFe12-yO19-aFe2O3(0 ≤ y ≤ 1,0) obtained by the proteic sol-gel process having as precursor coconut water. Samples were
analyzed by techniques of X-ray diffraction, magnetometry and impedance. The impedance analysis showed that resistivity increased with the calcium concentration to 0.0 <y ≤ 0.2, but
decreased for y> 0.2 and reached saturation at 7.5×106 Ω.cm to y = 0.9. The magnetization curve as a function of the magnetic field presents high values of saturation magnetization (Ms
= 40 emu / g) with low remanent field (Mr = 6.7 emu / g) and coercive field (Hc = 320 Oe). By means of X- ray diffraction we have observed that agglomerates of the type hexaferrite
CaM were formed after the doping with hematite, i.e., there was the existence of the two phases occurring antiferromagnetic coupling confirmed by exchange bias field of 9.6 Oe. / Resumo : Nesta dissertação foram estudados os pós e pastilhas de CayFe12-yO19 - (0 ≤ y ≤ 1,0) obtidos por meio do processo sol-gel proteico que tem como precursor água de coco. As amostras foram analisadas através de técnicas de difratometria de raios X, magnetometria e impedanciometria. A análise de impedância mostrou que a resistividade aumentou com a concentração de cálcio para 0,0 < y 0,2, mas diminuiu para y> 0,2 e atingiu a saturação em 7,5×106 cm para y = 0,9. A curva de magnetização como uma função do campo magnético teve valores elevados de magnetização de saturação (Ms = 40 emu/g) com baixo campo remanente (Mr = 6,7 emu/g) e campo coercivo (Hc = 320 Oe). Por meio da difratometria de raios X observou-se que foram formados aglomerados da hexaferrita tipo CaM a partir da dopagem da hematita, ou seja, houve a existência das duas fases ocorrendo um acoplamento ferro-antiferro, confirmado pelo campo de exchange bias na curva de M x H de 9,6 Oe.
| Identifer | oai:union.ndltd.org:IBICT/oai:ri.ufs.br:riufs/5315 |
| Date | 25 February 2015 |
| Creators | Passos, José Cleverton da Conceição |
| Contributors | Macêdo, Marcelo Andrade |
| Publisher | Universidade Federal de Sergipe, Pós-Graduação em Física, UFS, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFS, instname:Universidade Federal de Sergipe, instacron:UFS |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0038 seconds