Previous issue date: 2014-08-07 / As cerâmicas são materiais sólidos não metálicos inorgânicos. Por apresentar
natureza refratária, dureza e inércia química frente às condições adversas
encontradas na cavidade bucal, as cerâmicas foram introduzidas como material
odontológico devido a sua biocompatibilidade, estabilidade de cor em longo prazo,
resistência ao desgaste e a sua capacidade de serem conformadas em formas
precisas. Destacam-se entre as cerâmicas utilizadas nos implantes ortodônticos a
zircônia e a hidroxiapatita por possuirem propriedades mecânicas muito
semelhantes à de metais e cor semelhante à cor do dente. Baseado nestas
informações este trabalho tem como objetivo estudar as propriedades de blocos
sinterizados de Zircônia/Hidroxiapatita como perspectiva de aplicação como
biomaterial. Verificou-se a possibilidade de obter blocos Zircônia/Hidroxiapatita,
controlando suas características morfológicas e cristalinas pela adição de
hidroxiapatita, com potencial para ser aplicado como biomaterial. / Ceramics are inorganic non-metallic solids. By presenting refractory nature, hardness
and chemical inertness face of the adverse conditions found in the oral cavity,
ceramics were introduced as dental material due to its biocompatibility, color stability
for long-term wear resistance and its ability to be formed into precise shapes.
Prominent among the ceramics used in orthodontic zirconia implants and
hydroxyapatite to possess mechanical properties very similar to the metal and color
similar to the color of the tooth. Based on this information this work was to study the
properties of sintered blocks of zirconia / hydroxyapatite as application perspective
as a biomaterial. It has been found the possibility to obtain zirconia / hydroxyapatite
blocks, controlling their morphological and crystalline characteristics by adding
hydroxyapatite, with a potential to be applied as a biomaterial.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/420 |
| Date | 18 April 2018 |
| Creators | GADELHA, Leonardo Sarmento Meira. |
| Contributors | FOOK, Marcus Vinícius Lia., SILVA, Bartolomeu Jorge da., FREIRE, Waldênia Pereira Freire. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds