Titanium alloys are major materials used in the airplane industry, and prospects show that airplane production will double in the next 20 years. Consequently, the demand for cutting tools for machining of titanium alloys will increase. The primary problem when machining titanium alloys is their low thermal conductivity. Crater wear is the main factor limiting tool life, and is generally caused by thermal diffusion due to high temperatures in the tool-chip interface. This master’s thesis was performed in collaboration with Sandvik Coromant, with the prospect to increase knowledge of how diffusion and chip formation influences crater wear progression. The aim was to study tool wear of cutting tools when turning Ti–6Al–4V. This was done by testing two different rake face geometries, both coated and uncoated, at cutting speeds of 30–115 m/min. Diffusion was investigated to learn about the impact it has on crater wear. Chips were examined to investigate chip formation and shear strain. The coated modified rake face insert showed less crater wear only for the initial few seconds of machining. Uncoated inserts with a modified rake face showed higher diffusion rate and faster crater wear progression than did standard inserts. The standard inserts showed twice as long tool life as did the modified inserts. No significant differences in the chip formation mechanism were found between modified and standard inserts. Cracks were found within shear bands that were thinner than usual, which suggest that the generation of cracks allows less shear deformation.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-306373 |
Date | January 2016 |
Creators | Bamford, Erik |
Publisher | Uppsala universitet, Tillämpad materialvetenskap |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | UPTEC K, 1650-8297 ; 16021 |