Orientador: Marcos Akira D'Ávila / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-26T13:08:26Z (GMT). No. of bitstreams: 1
DavilaSanchez_JoseLuis_M.pdf: 7833063 bytes, checksum: 1e3a93b9b918ec86f9810207586b8fad (MD5)
Previous issue date: 2014 / Resumo: A engenharia tecidual é uma linha de pesquisa que emerge como a sinergia entre diferentes ramos da ciência. É orientada à obtenção de estruturas com características semelhantes à matriz extracelular (ECM) de diferentes órgãos e tecidos, com o objetivo de reparar, regenerar ou restaurar tecido danificado. Surge como uma solução viável para diferentes problemas de saúde, que com tratamentos convencionais têm limitações, principalmente devido à pequena quantidade de doadores. As estruturas que imitam as características da ECM são chamadas de scaffolds. A manufatura aditiva permite fabricar scaffolds com geometria controlada e 100% de interconectividade, mediante a aplicação progressiva de camadas de material. Neste trabalho foram fabricados scaffolds de policaprolactona (PCL) e scaffolds de compósitos de matriz PCL reforçados com ? fosfato tricálcico (?-TCP) para aplicações em tecido ósseo. Foram utilizadas composições de 10, 20 e 30% em peso de reforço. Primeiramente foram definidos os parâmetros de processamento, além disso, foi realizada a caracterização reológica do PCL mediante reometria capilar. Seguidamente foram fabricados scaffolds utilizando o processo de impressão 3D por rosca de extrusão, desenvolvido no Centro de Tecnologia da Informação Renato Archer (CTI). Para a fabricação dos scaffolds foi desenvolvido um software que permite gerar trajetórias de impressão contínuas em curtos tempos. Posteriormente, foram caracterizadas as propriedades térmicas mediante a análise termogravimétrica (TGA) e calorimetria exploratória diferencial (DSC), a morfologia dos scaffolds utilizando microscopia eletrônica de varredura (MEV) e microtomografia computadorizada (Micro-CT), a presença do reforço mediante difração de raios-X (XRD) e a estrutura química mediante espectroscopia no infravermelho por transformada de Fourier (FTIR). A caracterização mecânica foi realizada mediante o ensaio de compressão e a caracterização das propriedades hidrofílicas mediante a medição do ângulo de contato. Finalmente foi feito o ensaio de citotoxicidade in vitro. Os scaffolds fabricados apresentaram boas características morfológicas e propriedades dentro da faixa de aplicações em tecido ósseo. O ensaio de citotoxicidade in vitro mostrou que os scaffolds fabricados têm potencial para serem utilizados em aplicações em tecido ósseo / Abstract: Tissue engineering emerges as the synergy between different scientific fields. Its main objective is to repair, regenerate or restore damaged tissues or organs through the fabrication of structures with similar characteristics to the extracellular matrix (ECM). It is a viable solution to health problems, because conventional treatments have limitations, mainly due to the small number of donors. Structures that mimic the ECM characteristics are known as scaffolds. Additive manufacturing enables the fabrication of scaffolds with controlled geometry and 100% of interconnectivity through the progressive application of material layers. In this work, polycaprolactone (PCL) and PCL composites reinforced with ? tricalcium phosphate (?-TCP) were manufactured for bone tissue applications. Compositions of 10, 20 and 30% by weight of ?-TCP were used. Initially, processing parameters were determined. Furthermore, rheological properties of PCL were obtained by capillary rheometry. Then scaffolds were fabricated by 3D mini-screw extrusion printing, which was developed at the Renato Archer Information Technology Center (CTI). To fabricate scaffolds in short times and with continuous path, generator software was developed. Subsequently, thermal properties were obtained by thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC), scaffolds morphology using computed microtomography (Micro-CT) and scanning electron microscopy (SEM), the reinforcement presence by X-ray diffraction (XRD) and chemical structure by Fourier transform infrared spectroscopy (FTIR). Mechanical characterization was performed by compression test and hydrophilic properties were studied by measuring the contact angle of water drops. Finally, cytotoxicity in vitro assay was performed. The fabricated scaffolds have good characteristics and suitable properties. Cytotoxicity in vitro assay shows that the scaffolds have potential for bone tissue applications / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265863 |
| Date | 12 November 2014 |
| Creators | Dávila Sánchez, José Luis, 1986- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, D'Avila, Marcos Akira, 1972-, Zavaglia, Cecília Amélia de Carvalho, Silva, Jorge Vicente Lopes da |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 103 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds