Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015. / Made available in DSpace on 2016-04-15T13:15:32Z (GMT). No. of bitstreams: 1
337936.pdf: 64482450 bytes, checksum: 97bd8c65afbab985f380186230ac4351 (MD5)
Previous issue date: 2015 / O objetivo do presente trabalho foi avaliar a influência da rugosidade do preparo dental na adaptação interna (AI) e marginal (AM) de coroas confeccionadas por tecnologia CAD/CAM. Para tanto, foram confeccionados 4 troquéis em zircônia Y-TZP com preparo para coroa total, com 4 diferentes rugosidades (G1 - 0,828µm; G2 - 0,564µm; G3 ? 0,37µm; e G4 ? 0,102µm). Sobre cada troquel, foram confeccionadas, posteriormente, 10 coroas em cerâmica vítrea reforçada por dissilicato de lítio em um sistema CAD/CAM de consultório. A adaptação interna e marginal das coroas foram avaliadas por meio da técnica da réplica de silicone, onde se mensurou a espessura da camada análoga ao cimento por meio de microscopia óptica em um aumento de 100 vezes. Os dados foram analisados pelo teste estatístico de ANOVA e teste post-hoc Tukey (a=0,05). Verificou-se que houve diferenças estatísticas entre os grupos testados (p<0,05). A maior desadaptação média interna e marginal foi verificada e G1 (AI?192,54µm e AM?157,74µm), este estatisticamente significante em relação aos demais grupos (p<0,05). Enquanto, as melhores médias de adaptação foram encontradas em G2 (AI?148,79µm e AM?98,14µm) e G3 (AI?154,19µm e AM?104,20µm), sem diferenças estatísticas entre si (p>0,05), e logo depois em G4 (IA?157,94µm e MA?117,24µm) Dentro das limitações desse estudo, conclui-se que a rugosidade do preparo pode influenciar na adaptação interna e marginal de coroas cerâmicas confeccionadas em um sistema CAD/CAM.<br> / Abstract : The aim of this study was to evaluate the influence of the prepared tooth roughness on the internal (IA) and marginal adaptation (MA) of all-ceramic crowns made by CAD/CAM technology. Thus, 4 dies were made from Y-TZP zirconia prepared for a ceramic crown, with different superficial roughness (G1 - 0,828µm; G2 - 0,564µm; G3 Â 0,37µm; e G4 Â 0,102µm). Ten lithium disilicate glass-ceramic crowns were made for each zirconia die by in-office dental CAD/CAM system. The internal and marginal adaptation of the crowns was evaluated by replica technique, which the thickness of cement layer analog is measured by optical microscopy under 100x magnification. Data were analyzed with ANOVA and Tukey post-hoc test (a=0.05). There were statistical differences between the groups tested (p<0.05). The highest average internal and marginal misfit was observed in G1 (IAÂ 192.54µm and MAÂ 157.74µm) and was statistically significant compared to other groups (p<0.05). Whereas the best marginal and internal adaptation was found in G2 (AI-148.79µm and AM-98.14µm) and G3 (AI-154.19µm and AM-104.20µm), with no statistical differences between them (p>0.05), and soon after in G4 (IA-157.94µm and MA-117.24µm). Within the limitations of this study, it can be concluded that the surface roughness may influence the internal and marginal adaptation of ceramic CAD/CAM crowns.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/160557 |
| Date | January 2015 |
| Creators | Shibata, Shizuma |
| Contributors | Universidade Federal de Santa Catarina, Baratieri, Luiz Narciso, Vieira, Luiz Clóvis Cardoso |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 127 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds