This thesis describes improvements on newly-discovered high-strength pozzolan-based materials fabricated via a low-cost chemical reaction that takes place between 90 and 115 ℃ for 3 to 24 hours. The reported results focus on pozzolan constituents acquired from Coal Combustion Products (CCPs) such as cenospheres, fly ash C and F, as well as bottom ash. The thesis reports on various types of these materials with specific gravity ranging from 0.5 to 1.6; compressive strength ranging from 300 to 3600 psi, and compressive modulus ranging from 50 to 240 ksi. In addition to their good mechanical properties under compression that are attractive for the building and construction industries, the materials further exhibit great potential for applications as energy absorption cores in sandwich construction that could extend their value in other industries including the automotive and aerospace industries. For example, the load-displacement curve exhibits a short elastic zone followed by a long load-plateau; while the materials crush through a controlled vertical cracking process. Additionally, an attempt was made to further decrease the manufacturing cost of the material by investigating incorporation of chemicals that accelerates dehydration of the mixture. One such successful chemical reported in this thesis is aluminum phosphate; while it is not conclusive how the chemical improves any major property.
Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/31804 |
Date | 19 November 2008 |
Creators | Claus, Julien |
Publisher | Georgia Institute of Technology |
Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
Detected Language | English |
Type | Thesis |
Page generated in 0.0063 seconds