Orientador: Maria do Carmo Gonçalves / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Química / Made available in DSpace on 2018-08-25T19:34:46Z (GMT). No. of bitstreams: 1
DeFarias_MarceloAlexandre_D.pdf: 6813625 bytes, checksum: 734f14c74ec0690013d0549463dd8b09 (MD5)
Previous issue date: 2014 / Resumo: O principal objetivo desta tese consiste na síntese de nanopartículas de prata e de sílica e sua posterior modificação de superfície. Visando atribuir um caráter hidrofóbico às nanopartículas, sintetizou-se o copolímero em bloco de poliestireno-bloco-poli(N-vinil-2-pirrolidona) (PS-b-PVP), via técnicas de polimerização radicalar controlada. A metodologia utilizada produziu copolímeros de PS-b-PVP com baixa polidispersidade e massa molar controlada, capazes de estabilizar a emulsão de água em clorofórmio. Nanopartículas de prata (AgNP) produzidas à temperatura ambiente exibiram diâmetros médios de 8 e 11 nm, utilizando PVP ou PS-b-PVP como agentes estabilizantes, respectivamente. Nanopartículas de sílica (SiO2NP) foram sintetizadas pelo método de Stöber e apresentaram diâmetros aproximados de 40, 80 e 150 nm. Também foram utilizadas SiO2NP comerciais, que apresentaram duas populações com diâmetros médios de 12 e 25 nm, além de aglomerados. Por este motivo, a adsorção de PVP ou de PS-b-PVP à superfície das SiO2NP só foi caracterizada adequadamente com as SiO2NP sintetizadas. Mapas elementares de carbono, obtidos por imagem espectroscópica de elétrons (ESI-TEM) de dispersões de AgNP ou SiO2NP, mostraram que ambas as nanopartículas tiveram sua superfície modificada por PVP ou PS-b-PVP. Adicionalmente, as nanopartículas foram incorporadas em matrizes de poliestireno-bloco-polibutadieno-bloco-poliestireno (SBS) para produção de nanocompósitos. Observou-se por espalhamento de raios X de baixo ângulo (SAXS) e microscopia eletrônica de transmissão (TEM) que filmes de SBS puros apresentaram elevado grau de auto-organização da microestrutura de cilindros empacotados hexagonalmente, devido às condições de tratamento térmico e de casting utilizadas. Os nanocompósitos contendo SiO2NP apresentaram o mesmo comportamento termomecânico que a matriz de SBS, embora perturbações na microestrutura da matriz tenham sido observadas. Imagens de microscopia de força Kelvin mostraram a presença de domínios com potenciais elétricos distintos, indicando a ocorrência de uma forte interação entre o SBS e as AgNP/PS-b-PVP. Análises de DMA e TEM sugeriram que as AgNP/PS-b-PVP apresentaram maior interação com os cilindros de PS da matriz de SBS, em comparação com as AgNP/PVP. O conjunto de resultados obtidos neste trabalho indica que foi possível modificar superficialmente as nanopartículas inorgânicas empregando o copolímero PS-b-PVP / Abstract: The main objective of this thesis is the synthesis and surface modification of silver and silica nanoparticles. Aiming towards a hydrophobic character for the nanoparticles, the polystyrene-block-poly(N-vinyl-2-pyrrolidone) (PS-b-PVP) amphiphilic block copolymer was synthesized by controlled radical techniques. This methodology produced PS-b-PVP block copolymers with low polydispersity and controlled molar mass, which are able to stabilize water/chloroform emulsions. Silver nanoparticles (AgNP) produced at room temperature showed 8 and 11 nm mean diameters when using PVP or PS-b-PVP, respectively. Silica nanoparticles (SiO2NP) synthesized by Stöber method showed 40, 80 and 150 nm mean diameters. Commercial SiO2NP was also used and presented two populations with mean diameters of 12 and 25 nm, as well as agglomerates. The adequate characterization of PVP or PS-b-PVP adsorption onto SiO2NP surfaces was only possible using the SiO2NP obtained by the Stöber method. Carbon maps, obtained by electron spectroscopic imaging (ESI-TEM) showed that AgNP and SiO2NP were both surface modified by PVP or PS-b-PVP. Additionally, the nanoparticles were incorporated into polystyrene-block-polybutadiene-block-polystyrene (SBS) matrices to produce nanocomposites. Small angle X ray scattering (SAXS) and transmission electron microscopy (TEM) showed that SBS films presented a high self-assembly degree of the hexagonally packed cylinder due to annealing and casting conditions. Similar thermal-mechanical behavior was observed for the nanocomposites containing SiO2NP in relation to pure SBS, although perturbations in the SBS microstructure had also been observed. Kelvin force microscopy (KFM) showed domains with different electrical potentials, indicating a strong interaction between SBS and AgNP/PS-b-PVP. DMA and TEM analysis suggested that AgNP/PS-b-PVP interacted preferentially with SBS matrix PS cylinders. The results obtained in this work indicate that the inorganic nanoparticle surfaces were successfully modified by the PS-b-PVP copolymer / Doutorado / Físico-Química / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248731 |
Date | 25 August 2018 |
Creators | De Farias, Marcelo Alexandre, 1986- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gonçalves, Maria do Carmo, 1957-, Bertran, Celso Aparecido, Rezende, Camila Alves de, Rubira, Adley Forti, Carastan, Danilo Justino |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
Source Sets | IBICT Brazilian ETDs |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 140 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.01 seconds