Caracterização microestrutural e de propriedades mecânicas de soldas do aço ASTM A 131 pelos processos FCAW convencional e com adição de arame frio

Submitted by Cleide Dantas (cleidedantas@ufpa.br) on 2014-04-08T11:58:11Z
No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CaracterizacaoMicroestruturalPropriedades.pdf: 6450063 bytes, checksum: 529d7a41d494d15ecf125132e9a03a1e (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2014-06-18T13:00:29Z (GMT) No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CaracterizacaoMicroestruturalPropriedades.pdf: 6450063 bytes, checksum: 529d7a41d494d15ecf125132e9a03a1e (MD5) / Made available in DSpace on 2014-06-18T13:00:29Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_CaracterizacaoMicroestruturalPropriedades.pdf: 6450063 bytes, checksum: 529d7a41d494d15ecf125132e9a03a1e (MD5)
Previous issue date: 2011 / FAPESPA - Fundação Amazônia de Amparo a Estudos e Pesquisas / O trabalho aqui representado retrata de modo comparativo as características mecânicas e microestruturais de metais de solda empregando duas técnicas de soldagem uma já
disseminada, FCAW (Soldagem a Arco Voltaico com Arame Tubular) e a outra é inovadora,
FCAW-AF (Soldagem a Arco Voltaico com Arame Tubular com Adição de um Arame Frio
não energizado) em três níveis de velocidades 6, 8 e 10 m/min. Sendo que este processo
variou os diâmetros dos arames frio adicionados, entre 0.8 e 1.0 mm. O metal de base
utilizado foi o aço naval ASTM 131 grau A (baixo carbono) em geometria de chapas de 150
mm x 300 mm x 9,5 mm, aplicadas em chanfro em V (Bisel de 22,5º) com ângulo somado de
45º, com leve abertura de raiz de 2,4 mm. A solda usada foi do tipo topo com a aplicação de
dois passes, um passe de raiz e o passe de acabamento (ou enchimento). A fim averiguar as
condições desses cordões de solda foram realizados 05 tipos de ensaios destrutivos, são eles:
dobramento transversal de face, tração, tenacidade ao impacto (tipo Charpy com entalhe em
V), microdureza e o ensaio metalográficos. Além das análises não destrutivas como o ensaio
visual e o líquido penetrante. De maneira geral, os resultados para o processo FCAW-AF,
mostraram-se compatíveis, em relação ao processo FCAW convencional, porém alguns
resultados apresentaram valores de propriedades mecânicas menores. Este fato pode, muito
provavelmente ter ocorrido pela presença de descontinuidade na junta pelo FCAW-AF.
Quanto às caracterizações microestruturais, os resultados da junta FCAW-AF foram
semelhantes os da FCAW convencional para todos os níveis estudados. / The work presented here show comparatively mechanical properties and microstructure of
weld metals employing two welding techniques, an already disseminated, FCAW (arc
welding with cored wire) and the other is innovative, FCAW-AF (arc welding with Adding
Tubular Wire with a cold wire is not energized) at three levels of speed 6, 8 and 10 m / min.
In this process two diameters of the cold wire 0.8 and 1.0 mm were used. The base metal used
was a naval steel ASTM 131 grade A (low carbon) in geometry of plates 150 mm x 300 mm
x 9.5 mm, applied to V-groove (Bisel of 22.5°) with angle 45° summed, with mild opening
of root of 2.4 mm. The weld used was top type with the application of two passes, one root
pass and the pass of finish (or filling). In order to establish of weld conditions 5 types of
destructive were carried out: face transverse bend, tension, impact test (Charpy notched type
V), microhardness and metallographic test. In addition to the non-destructive analysis visual
and penetrating liquid. In general, the results for the process FCAW-CW, show themselves
compatibles, regarding the process FCAW conventional, but some results showed smaller
values of mechanical property. This fact much probably happened due the presence of
discontinuities in the welded joint FCAW-CW. The microstructural characterization presented
similar results to FCAW-CW and FCAW conventional for all energy levels studied.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5092
Date23 September 2011
CreatorsRODRIGUES, Lino Alberto Soares
ContributorsBRAGA, Eduardo de Magalhães
PublisherUniversidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis