O objetivo desta pesquisa foi avaliar a transmitância de diferentes tipos e cores de cerâmicas e seus efeitos no grau de conversão (GC) de dois tipos de cimentos resinosos com modo de polimerização dual. Foram confeccionadas 60 pastilhas com a cerâmica IPS e.max (Ivoclar Vivadent, Schaan, Liechtenstein) e divididas em 3 grupos: LT, MO e Z, com 20 pastilhas cada um. Nos grupos LT e MO, as pastilhas foram confeccionadas com a cerâmica de dissilicato de lítio de baixa translucidez (LT - low transluscency) e de média opacidade (MO - medium opacity), respectivamente. No grupo Z, as pastilhas foram confeccionadas em zircônia. Cada grupo foi subdividido em 5 subgrupos (n=4), de acordo com a cor da cerâmica: A2; A3,5; B2; C2; D3. No grupo LT, as pastilhas foram prensadas nas cores anteriormente citadas e, nos grupos MO e Z, as pastilhas foram, inicialmente, confeccionadas para simular infraestruturas e, posteriormente, receberem aplicação de cerâmica de revestimento IPS e.max Ceram (Ivoclar Vivadent, Schaan, Liechtenstein) nas mesmas cores. O espectrofotômetro UV 1800 Shimadzu foi utilizado para medir a transmitância de cada espécime de cerâmica (2,0 mm de espessura). Para medir o GC, espécimes dos cimentos resinosos Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) e Rely X U200 (3M ESPE, St. Paul, MN, USA), com espessura de 100 μm, foram fotopolimerizados sob os discos de cerâmica por 40 s. Espécimes dos cimentos fotoativados sem a interposição da cerâmica foram usados como grupo controle. A polimerização dos cimentos foi avaliada através da espectrometria no infravermelho com transformada de Fourier (FTIR) empregando o método de reflexão atenuada total (ATR) imediatamente após a fotopolimerização. Os resultados foram submetidos aos testes ANOVA a 1 critério e Teste de Tukey (α=5%). Os valores de transmitância foram inferiores a 1%, sendo que as do grupo LT apresentaram, em geral, os maiores valores de transmitância, seguidos dos grupos MO e Z. O GC do cimento Variolink II não sofreu influência da interposição da pastilha de cerâmica. Para o cimento Rely X U200, a interposição de alguns tipos/cores de cerâmica (LT A3,5; MO A2; MO A3,5 e Z A3,5) diminuíram o GC em relação ao grupo controle. Concluiu-se que os valores de transmitância e GC foram influenciados pelos tipos/cores de cerâmica. Entretanto, somente o grupo formado pela cerâmica de dissilicato de lítio LT, usando o Rely X U200, apresentou correlação negativa entre transmitância e GC. / The aim of the present study was to evaluate the transmittance of different ceramic types and shades and their effects on the degree of conversion (DC) of two dual-cure resin cements. Sixty discs were fabricated with IPS e.max ceramic (Ivoclar Vivadent, Schaan, Liechtenstein) and divided into three groups (n= 20 in each group): LT, MO and Z. For LT and MO groups discs were fabricated with low translucency (LT) and medium opacity (MO) lithium disilicate ceramic, respectively. Discs from Z group were manufactured of zirconia. Each group was divided into five subgroups (n = 4), according to the ceramic shade: A2; A3,5; B2; C2; D3. In the LT group, specimens were heat-pressed in shades cited above and in the MO and Z groups, the discs were initially fabricated as core materials and then veneered with veneer ceramic (IPS e.max Ceram, Ivoclar Vivadent, Schaan, Liechtenstein) in the same shades. A spectrophotometer UV-1800 Shimadzu was used to determine the transmittance percentage of each ceramic specimen (2.0-mm-thick). For DC measurements, the resin cements (Variolink II - Ivoclar Vivadent, Schaan, Liechtenstein and Rely X U200 - 3M ESPE, St. Paul, MN, USA) specimens (thickness: 100 μm) were photocured under the ceramic discs (2.0-mm-thick) for 40 s. Specimens photocured without the ceramics discs were used as control group. ATR/FTIR spectrometry was used to evaluated the extent of polymerization for all cement specimens immediately after photocuring. The results were submitted to one-way ANOVA and Tukey test (α=5%). The transmittance percentage was less than 1% and the LT group had the highest transmittance values, followed by MO and Z groups. The %DC of Variolink II cement was not influenced by the ceramic disc interposition. For Rely X U200 cement, the interposition of some ceramics types/shades (LT A3,5, MO A2, MO A3,5 and Z A3,5) significantly decreased the %DC compared to control group. It was concluded that the transmittance values and %DC were influenced by the ceramics types/shades. However, only the LT group, using the Rely X U200, showed a negative correlation between transmittance and %DC.
| Identifer | oai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-10032016-110136 |
| Date | 14 September 2015 |
| Creators | Mendonça, Luana Menezes de |
| Contributors | Pegoraro, Luiz Fernando |
| Publisher | Biblioteca Digitais de Teses e Dissertações da USP |
| Source Sets | Universidade de São Paulo |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | Tese de Doutorado |
| Format | application/pdf |
| Rights | Liberar o conteúdo para acesso público. |
Page generated in 0.0024 seconds