Orientador: Marco Antonio Bica de Moraes / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-06T01:12:05Z (GMT). No. of bitstreams: 1
Gadioli_GiovanaZanini_M.pdf: 816711 bytes, checksum: 5d38a2c08f13049d8af5fd4659ded22e (MD5)
Previous issue date: 2006 / Resumo: As propriedades de filmes obtidos por co-deposição de um material ferromagnético e um não-magnético são objetos de intensa investigação. Neste trabalho, foram investigadas as propriedades de filmes Gdx W1-x, com x variando de 0 a 1. Os filmes foram depositados por magnetron-sputtering a partir de alvos de Gd e W. Para a análises dos filmes foram usadas as técnicas EPMA (microanálise eletrônica) e difratometria de raio-x de baixo ângulo para determinar a composição atômica e a estrutura cristalina, respectivamente. O momento magnético, m , de cada filme foi medido em função da temperatura, T, e do campo magnético aplicado, H, usando um magnetômetro SQUID (superconducting quantum interference device). Os filmes são amorfos para para 0,15 < x < 0,85, mas a coercividade foi observada em todos as amostras. A partir das curvas m vs T, foi observado um forte ordenamento magnético para T < TB. Para T > T B as amostras se mostram paramagnéticas. Os valores de T B foram observados em baixa temperatura (entre 5 e 50 K). A temperatura de Curie-Weiss, deduzida a partir das curvas x -1 vs T, onde x é a suscetibilidade, aumentaram com x. O efeito magnetocalórico foi estudado a partir das isotermas de magnetização, M vs H, das quais a variação de entropia magnética, D S M, foi obtida. As curvas D SM vs T exibiram máximos que variam entre 5 K e temperatura ambiente, dependendo da proporção de Gd / Abstract: The magnetic properties of films obtained by the co-deposition of a ferromagnetic and a non-magnetic components are the subject of intense investigation. In this work, the magnetic properties of Gdx W1-x, with x ranging from 0 to 1, were investigated. The films were deposited by magnetron sputtering from Gd and W targets. EPMA (electron probe microanalysis) and low-angle XRD (x-ray diffraction) were used to determine the film atomic composition and structure, respectively. The magnetic moment, m , of the films was measured as a function of temperature, T, and applied field H, using a SQUID (superconducting quantum device) magnetometer. The films were amorphous for 0.15 < x < 0.85 but coercivity was observed in all samples. From plots of m vs T, a strong magnetic ordering was observed for T < TB. For T > T B the samples were paramagnetic. TB-values occurred at low temperatures (between 5 K and 50 K). The Curie paramagnetic temperature, deduced from the x -1 vs T plots, where x is the susceptibility, was observed to increase with increasing x. The magnetocaloric effect was investigated from the magnetization isotherms, M vs H, from which the magnetic entropy change, D SM, caused by the application and removal of a 50 kOe field, was deduced. The D SM vs T curves exhibited maxima which varied from 5 K to about room temperature, depending on the Gd concentration / Mestrado / Física da Matéria Condensada / Mestre em Física
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/278297 |
Date | 24 March 2006 |
Creators | Gadioli, Giovana Zanini, 1980- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moraes, Mário Antônio Bica de, 1939-, Gama, Sergio, Imaizumi, Momotaro |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 59p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.2704 seconds