Orientador : Maria Aparecida Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-02T14:19:02Z (GMT). No. of bitstreams: 1
Miranda_MirladeNazaredoNascimento_M.pdf: 4035948 bytes, checksum: e0c57455cc7d71613e0d58c4277a3e12 (MD5)
Previous issue date: 2002 / Resumo: Em processos industriais, há muitos exemplos do uso de misturas de diferentes partículas, ou seja, sólidos multicomponentes. O conhecimento das propriedades de misturas de sólidos a partir das propriedades dos materiais puros é de grande aplicação em processos que utilizam misturas de sólidos e poderá trazer muitas vantagens e melhorias esses processos. Por isso, este trabalho teve como objetivo determinar as relações existentes entre as propriedades físicas dos sólidos puros e de misturas de sólidos. Neste trabalho foi estudado o comportamento de misturas dos materiais Zeólita Na Y, Alumina e Caulim. As propriedades de sólidos porosos estudadas foram: densidade real, densidade bulk (aparente), distribuição de tamanho de partículas e de poros, isotermas de sorção, área superficial, permeabilidade intrínseca e porosidade. Os materiais sólidos foram analisados na forma de pó, mas também foram preparadas pastilhas cilíndricas com os materiais puros para verificar a influência do modo de preparo do sólido nas propriedades físicas de densidade real e bulk. As técnicas experimentais utilizadas foram: picnometria a gás, para determinação da densidade real; as isotermas de dessorção foram obtidas utilizando-se o método estático, com uso de soluções salinas saturadas, à temperatura de 30°C; as isotermas de adsorção foram determinadas por adsorção de Nitrogênio; a área superficial foi calculada a partir da equação de BET, utilizando-se os dados das isotermas de sorção; a distribuição do tamanho de partículas foi determinada por difratometria a Ia ser e a permeabilidade intrínseca foi calculada considerando-se poros cilíndricos e escoamento de Hagen-Poiseuille. Também foram feitos experimentos de secagem, na forma de camada delgada, à temperatura de 120°C. As equações propostas neste trabalho relacionam a propriedade física da mistura com a propriedade física dos componentes puros, ponderados por suas respectivas frações mássicas ou volumétricas. Todas as propriedades físicas tiveram boa concordância com as equações propostas, exceto a densidade bulk, que é fortemente influenciada pelo processo de preparo do sólido. Tanto as isotermas de sorção como as curvas de secagem das misturas se encontraram entre as curvas dos materiais puros verificando-se uma proporcionalidade em função da composição da mistura / Abstract: In industrial processes, there are many examples of the use of mixture of different particles, that is, multicomponent solids. The knowledge of the properties of solids mixtures from the properties of the pure materials is of wide application in such processes. Possibly bringing advantages and improvements to the industrial processes. Therefore, the objective of this work was to determine the relationships between the physical properties of the pure solids and those of the solid mixtures. In this work, the mixture behavior of Zeolite Na Y, Kaolin and Alumina materials was studied. True density, bulk density, particle and pore size distributions, sorption isotherms, surface area, intrinsic permeability and porosity were the properties of solids studied. The solid materials were analyzed in the powdered form The pure materials were also analyzed in the form of cylindrical tablets in order to check the influence of the preparation mode on the value of both the true and bulk densities. There follows the experimental techniques used. The true density was determined by Helium picnometry. The adsorption isotherms were obtained using the static method, with the use of saturated salt solutions, at a temperature of 30°C. The adsorption isotherms were determined by Nitrogen adsorption. The surface area was calculated from the BET equation, using the data from the sorption isotherms. The particle size distribution was determined by laser diffratometry. The intrinsic permeability was calculated considering solids with cylindrical pores and the Hagen-Poiseulle flow. In addition, drying experiments were conducted for solids in the form of thin layers, at a temperature of 120°C. The proposed equations in this work relate the physical properties of the pure components pondered by its respective mass and volumetric fractions. All physical properties showed good agreement with the proposed equations. The exception was bulk density, which is strongly influenced by the process of the solid preparation. The sorption isotherms as well as the drying curves of the mixtures lied inside the limits of the curves for the pure materials proving to be direct functions of the mixture compositions / Mestrado / Engenharia de Processos / Mestre em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267386 |
Date | 16 August 2002 |
Creators | Miranda, Mirla de Nazare do Nascimento |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Silva, Maria Aparecida, 1955-, Re, Maria Ines, Taranto, Osvaldir Pereira |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Quimica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 118p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0171 seconds