El propósito de este estudio fue evaluar la influencia del grabado ácido previo a la aplicación de cuatros sistemas autograbantes, Adper Easy Bond (AEB), Futurabond DC (F), Go! (G) y OneCoat Self Etching Bond (OC), sobre esmalte dental de bovino.
Se utilizaron 24 dientes anteriores de bovino, los cuales fueron colocados en bloques de resina acrílica de 1.5 cm x 1.5 cm, dejándose expuesta la cara vestibular la cual fue posteriormente desgastada ligeramente y pulida. Las piezas dentales fueron dividas en dos grupos experimentales y un grupo control, al primer grupo experimental se le aplicó el sistema adhesivo autograbante según las indicaciones del fabricante, mientras que al segundo grupo se le realizó grabado con ácido ortofosfórico al 35% previamente, el grupo control fue tratado con un sistema adhesivo convencional de grabado total; finalmente se colocó un bloque de resina compuesta Z350 (3M) utilizando un molde de teflón de 8mm de diámetro x 4 mm de altura. Los dientes se almacenaron durante 24 horas en saliva artificial a 37°C. Se obtuvieron cortes de entre 0.8 y 1.00 mm2 de área transversal, los especímenes obtenidos fueron sometidos a Test de Microtensión a una velocidad de 0.5 mm/min. Para el análisis estadístico se utilizaron las pruebas de Kruskall Wallis (p menor a 0.05) y Mann Whitney.
Los valores de adhesión resultantes en MPa para los grupos experimentales sin grabado ácido fueron: AEB: 14.6 ± 3.8; F: 14.3 ± 8.7; G: 9.5 ± 3.8 y OC: 10.5 ± 6.2; para los grupos con grabado ácido previo fueron: AEB: 24.7 ± 14.2; F: 15.6 ± 4.8; G: 16.2 ± 8.9; OC: 14.9 ± 7.1. El grupo control All Bond 2 obtuvo valores de adhesión de 18.6 ± 7.3 MPa.
Se encontraron diferencias estadísticamente significativas entre los grupos experimentales, mientras que en relación al grupo control, el grupo experimental con grabado ácido previo obtuvo valores similares a este a excepción del sistema AEB el cual obtuvo un valor significativamente mayor. / The aim of this study was to evaluate the influence of prior acid etching to application of four self-etching adhesive systems, Adper Easy Bond (AEB), Futurabond DC (F), Go!(G) And OneCoat Self Etching Bond (OC), on bovine enamel.
Twenty four bovine lower incisors were used, which were mounted in cold – cure acrylic blocks of 1.5 x 1.5 cm, keeping exposed the buccal enamel surface subsequently abraded and polished. The teeth were divided in two experimental groups and a control group. In the first experimental group the adhesive system was applied following manufactures’ instructions, meanwhile the second experimental group was etched with ortophosphoric acid 35% prior to application of the adhesive. Control group was treated with a conventional total etch system. Finally a composite resin restoration Z350 (3M) was built using a Teflon mold of 8 mm diameter and 4 mm height. The teeth were stored in artificial saliva at 37°C during 24 hours. Specimens between 0.8 and 1.00 mm of cross-sectional area were obtained and stressed in tension at 0.5 mm/min cross-head speed. The statistical analysis was developed using Kruskall Wallis (p less than 0.05) and Mann Whitney tests.
The bond strengths in MPa obtained for the experimental groups without prior acid etching were: AEB: 14.6 ± 3.8; F: 14.3 ± 8.7; G: 9.5 ± 3.8 y OC: 10.5 ± 6.2; for the groups with prior acid etching the results were: AEB: 24.7 ± 14.2; F: 15.6 ± 4.8; G: 16.2 ± 8.9; OC: 14.9 ± 7.1. Control Group All Bond 2 obtained bond strengths of 18.6 ± 7.3 MPa.
Statistically significant differences of bond strengths values were found between both experimental gropus, the experimental group with prior acid etching obtained similar bond strength values to the control group, except for the AEB adhesive which obtained higher significant values.
| Identifer | oai:union.ndltd.org:Cybertesis/oai:cybertesis.unmsm.edu.pe:cybertesis/626 |
| Date | January 2009 |
| Creators | Romero Salaverry, Wilfredo Daniel |
| Contributors | Horna Palomino, Hernán |
| Publisher | Universidad Nacional Mayor de San Marcos |
| Source Sets | Universidad Nacional Mayor de San Marcos - SISBIB PERU |
| Language | Spanish |
| Detected Language | Spanish |
| Type | info:eu-repo/semantics/bacherlorThesis |
| Source | Universidad Nacional Mayor de San Marcos, Repositorio de Tesis - UNMSM |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds