Previous issue date: 2014-09-23 / Sem bolsa / Pigmentos de Al2O3:Mn foram utilizados de forma inovadora no presente trabalho para melhorar as características estéticas de resinas acrílicas para base de prótese. O objetivo deste estudo foi investigar a síntese e o efeito da pigmentação de nanopartículas de Al2O3:Mn na estabilidade de cor de resinas acrílicas. As resinas acrílicas comerciais Clássico Jet X15 rosa e Clássico Jet X15 incolor foram avaliadas. Nanopós de Al2O3:Mn foram preparados pelo método de precursores poliméricos, para estudar a relação entre a transição de fase. A morfologia dos pigmentos foi analisada por meio de um microscópio eletrônico de varredura (MEV) e a energia dispersiva por técnicas de espectroscopia de raios-X (EDX). Espécimes em forma de prisma (65mm × 10mm × 2,5mm) de resina acrílica incolor cor rosa e de resina acrílica incolor modificada com 1% e 2% de pigmento sintetizado à base de Al1,96Mn0,04O3 foram fabricados. A cor dos espécimes foi medida com um espectrofotômetro e avaliadas dentro do sistema CIE L*a*b*. A resistência à flexão e o módulo de elasticidade dos materiais foram avaliados em ensaio de flexão por três pontos. Os pigmentos obtidos apresentaram colorações diferenciadas em relação à antes e após a aplicação, devido à interação das partículas do pigmento com o material da resina. Notou-se que pigmentos de nanopartículas contendo manganês apresentaram coloração rosa mais compatível com resinas coloridas comerciais. Os conteúdos de cátions cromóforos (responsáveis pela coloração) do Al2O3, de acordo com a metodologia proposta neste trabalho, são mínimos e puderam ser controlados. Por meio de ensaios de flexão, notou-se um efeito positivo em relação ao aumento da resistência mecânica, em função da adição do pigmento sintetizado. Conclui-se que os pigmentos sintetizados têm duas vantagens em relação às resinas acrílicas coloridas comerciais: a possibilidade de controle efetivo de cor e o aumento de resistência mecânica. / Al2O3:Mn pigments were used in an innovative way in this work to improve the aesthetic characteristics of acrylic resin for denture base. The aim of this study was to investigate the synthesis and the effect of pigmentation of nanoparticles of Al2O3:Mn on the color stability of acrylic resins. Commercial acrylic resins Classic Jet X15 pink and colorless Classic Jet X15 were evaluated. Nanopowders of Al2O3:Mn were prepared through the polymeric precursors method, in order to study the relationship between phase transition. The morphology of the pigments was analyzed by a scanning electron microscope (SEM) and x-ray energy dispersive spectroscopy (EDX). Prism-shaped specimens (65mm × 10mm × 2.5mm) of pink-colored acrylic resin and of colorless acrylic resin with 1% or 2% of the synthesized Al1.96Mn0.04O3 pigment were prepared. The color of the specimens was measured with a spectrophotometer and evaluated in the CIE L*a*b* system. The flexural strength and elastic modulus of the materials were measured on three-point bending mode. The pigments obtained showed different color compared to before the application, due to the interaction of the pigment particles with the resin material. It was noted that pigments containing manganese nanoparticles exhibit a pink coloration which is more compatible to commercial resins. The content of Al2O3 chromophore cations (responsible for the color), according to the methodology proposed in this work, is minimal and could be controlled. By using the flexural test a positive effect was noticed as regards the increase in mechanical strength as a function of pigment addition. In conclusion, the synthesized pigments have two advantages in comparion with the commercial colored acrylic resins: the possibility of effective color control and the increase in mechanical strength.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3502 |
| Date | 23 September 2014 |
| Creators | Cruzeiro, Mario Thadeo Rodrigues |
| Contributors | 79636055904, http://lattes.cnpq.br/2853098230406981, Moraes, Rafael Ratto de, Cava , Sergio da Silva |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0049 seconds