Previous issue date: 2017-12-19 / Sem bolsa / O hidrogel de alginato é utilizado para diferentes fins, entre eles, a engenharia tecidual e como curativos para cicatrização. Devido suas baixas propriedades, há um esforço contínuo para superar suas limitações, incluir outros materiais é uma alternativa para melhorar suas propriedades. Diante disso, o objetivo desse estudo foi realizar uma membrana de hidrogel de alginato com celulose, hidroxiapatita, óxido de grafeno e chalconas com propriedades antimicrobianas. Para obter a celulose foram utilizadas fontes alternativas de resíduos agroindustriais, do talo da casca de banana. A celulose
foi recoberta com hidroxiapatita. Para o recobrimento, foi sintetizado hidroxiapatita assistida por micro-ondas,sendo utilizado nitrato de cálcio tetra-hidratado, ácido fosfórico, 1,2-etilenodiamina e solução de celulose com variações de (0,25; 0,5 e 1 g celulose), 140 ° 5 minutos. Para confeccionar as membranas de hidrogel de alginato foi utilizado alginato de sódio e sulfato de cálcio P.A Dihidratado e água deionizada. No alginato modificado foi acrescentado hidroxiapatita ou celulose precipitada com
hidroxiapatita, hidroxiapatita com óxido de grafeno, celulose hidroxiapatita e óxido de grafeno e chalconas. Após a completa homogenização, as amostras foram congeladas e liofilizadas, a concentração de chalconas foi de 0,0015 g dissolvidas em 0,2ml DMSO para cada 10 ml de solução final. As amostras foram congeladas e liofilizadas. As amostras foram caracterizadas por: BET (Brunauer Emmett Teller), DRX (Difração por Raio X), FITR (Espectrometria de infravermelho), MEV
(Microscopia eletrônica de varredura), FEG (Microscopia por emissão de elétrons), TG (Teste termogravimétrico) e teste de viabilidade celular para celulose recoberta com hidroxiapatita, e teste microbiológico com Candida albicans e parapsilosis para membranas com GO e com a bactéria gran positiva Staphylococcus aureus (S. Aureus) para as variações das chalconas. / The alginate hydrogel is used for different purposes, among them, tissue engineering and as curatives for healing. Due to its low properties, there is an ongoing effort to overcome its limitations, including other materials is an alternative to improve its properties. Therefore, the objective of this study was to perform an alginate hydrogel membrane with cellulose, hydroxyapatite, graphene oxide and chalcones with antimicrobial properties. To obtain the pulp, alternative sources of agroindustrial residues were used, from the stem of the banana peel. Cellulose was coated with hydroxyapatite. For the coating, microwave assisted hydroxyapatite was synthesized using calcium nitrate tetrahydrate, phosphoric acid, 1,2-ethylenediamine and cellulose solution with variations of (0.25, 0.5 and 1 g cellulose), 140º 5 minutes. To prepare the alginate hydrogel membranes was used sodium alginate and calcium sulfate P.A Dihydrate and deionized water. In the modified alginate was added hydroxyapatite or
cellulose precipitated with hydroxyapatite, hydroxyapatite with graphene oxide, hydroxyapatite cellulose and graphene oxide and chalcones. After complete homogenization, the samples were frozen and lyophilized, the chalcone concentration was 0.0015 g dissolved in 0.2 ml DMSO for each 10ml final solution. Samples were frozen and lyophilized. The samples were characterized by: BET (Brunauer Emmett Teller), XRD (Ray Diffraction), FITR (infrared spectrometry), SEM (Scanning Electron
Microscopy), FEG (Electron Emission Microscopy), TG (Thermogravimetric Test) and cell viability test for cellulose coated with hydroxyapatite, and microbiological test with Candida albicans and parapsilosis for membranes with GO and with the positive bacteria Staphylococcus aureus (S. aureus) for chalcone variations.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/4246 |
| Date | 19 December 2017 |
| Creators | Pieper, Cari Maristela |
| Contributors | 00349064645, http://lattes.cnpq.br/4035574249612354, Villareal, Neftali Lenin |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Dentística, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds