Previous issue date: 2014 / O processo de oxidação térmica melhora as características na superfície das ligas de titânio pelo aumento da camada de TiO2. Nesta pesquisa, foi avaliado o comportamento da liga Ti-6Al-4V termo oxidada em diferentes temperaturas e duração de tratamento na saliva artificial em diferentes pH. Para compreender as alterações no processo de corrosão, o teste de espectroscopia de impedância eletroquímica fornece a caracterização que ocorre sobre a superfície metálica. Foram utilizadas 60 amostras de discos de liga de Ti-6Al-4V, divididas em 20 grupos(n=3), comparando a relação da saliva artificial com alteração de pH (3e 6.5), temperatura (200°C, 400°C e 700°C) e duração de tratamento (1,3 e 6 horas) em relação ao grupo controle Ti-6Al-4V, que não recebeu tratamento de superfície. Para análise eletroquímica das amostras, foi utilizado teste com OCP, EIS e polarização potenciodinâmica. Os resultados foram avaliados por análise de variância e teste de Bonferroni (p<0,05). As superfícies foram examinadas por microscópio interferometria de luz branca, SEM e FTIR. Na potenciodinâmica, as amostras tratadas por oxidação térmica apresentaram melhoras na resistência à corrosão em relação ao grupo controle. Na comparação entre os grupos testes, os tratamentos a 200°C e 400°C apresentaram os melhores resultados. A duração do tempo de tratamento não foi um fator determinante para melhorar a resistência à corrosão, as amostras mostraram-se menos resistentes à corrosão em pH ácido.<br> / Abstract: The thermal oxidation process improves the surface characteristics of titanium alloys by increasing the TiO2 layer. In this study, we evaluated the behavior of Ti-6Al-4V term oxidized at different temperature and duration of treatment in artificial saliva at different pHs. To understand the changes in the corrosion process of the electrochemical impedance spectroscopy test provides a characterization that happens on the metal surface. It was used 60 samples of Ti-6Al-4V alloy discs divided into 20 groups (n = 3) to analyze the effect of pH (3 and 6.5) in artificial saliva, temperature (200°C, 400°C and 700°C), and duration of treatment (1, 3 and 6 hours) compared to the control group Ti-6Al-4V which received no surface treatment. Electrochemical tests, such OCP, EIS and potentiodynamic were used in a controlled environment to compare the surface reaction. The results were evaluated by analysis of variance and Bonferroni test (p <0.05). The surfaces were examined by white light interferometry microscopy, scanning electron microscopy (SEM) and FTIR. Samples treated by thermal oxidation showed improvement in corrosion resistance compare to the control group in potentiodynamic test. The test groups showed better results at treatments of 200°C and 400°C compared at the control group. The duration of treatment was not a determining factor for improved corrosion resistance and the samples were less resistant to corrosion in acidic pH.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/128814 |
| Date | January 2014 |
| Creators | Lucchiari Júnior, Newton Bergamaschi |
| Contributors | Universidade Federal de Santa Catarina, Gil, José Nazareno |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 101 p.| il., tabs., grafs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0095 seconds