000837239.pdf: 5726059 bytes, checksum: ebad9f215e1f252f7f81b01cde8dfac8 (MD5) / Zinc oxide (ZnO) nanoparticles were prepared by a sol-gel method, adapted from a synthesis route already well established. The kinetics of the ZnO synthesis was monitored by in situ UV-visible absorbance spectroscopy, pH measurements and small angle X-ray scattering (SAXS). Results allowed proposing a new mechanism of ZnO formation and growth. The second step of this work was to establish a new route of synthesis to obtain copper doped ZnO from two different sources: copper (II) acetate and copper (II) nitrate, at predetermined Zn/Cu ratio (0,1%; 0,25%, 0,5%; 0,75% e 1,0%). These syntheses were also monitored by UV-visible and SAXS spectroscopy. The powders prepared from colloidal suspensions precipitation were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM-EDS). Results show that the synthesis method is suitable for obtaining copper doped ZnO nanoparticles. The wurtzite crystalline structure, characteristic from bulk ZnO, was kept in doped samples. In fact, both the acetate and the nitrate anions inhibit the particles formation and growth, but induce to distinct growth mechanisms: reaction limited cluster-cluster aggregation (RLCA) and diffusion limited cluster-cluster aggregation (DLCA), respectively. Otherwise, the final size of doped particles was kept irrespective of the doping nature and quantity. Qualitative tests of samples response to visible irradiation show photochromic effects, which intensity and time of duration are influenced by the amount of dopant in the sample.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/124521 |
| Date | 28 April 2015 |
| Creators | Silva, Marlon Nunes da [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Pulcinelli, Sandra Helena [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 147 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.004 seconds