Orientador: Gustavo Paim Valença / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-22T19:06:31Z (GMT). No. of bitstreams: 1
Martim_Emerson_M.pdf: 2974837 bytes, checksum: 716f19b58a49fc284a9f38944230b569 (MD5)
Previous issue date: 1997 / Resumo: Neste trabalho procurou-se desenvolver a reação de acoplamento oxidativo de metano sobre catalisadores de Li/MgO-Si¿O IND. 2¿ na reação que se desenvolveu com uma relação de gases na alimentação de 'N IND. 2¿:¿C¿¿H IND. 4¿:¿O IND. 2¿ igual a 10:5:5, com o reator à temperatura de 1070K e pressão ambiente. Os óxidos mistos foram preparados por co-precipitação, com relações nominais Mg:Si iguais a 1:0, 4:1, 1:1, 1:4 e 0:1. A adição da solução de 'LI IND. 2¿¿C¿¿O IND. 3¿ se processou pelo método de impregnação incipiente, em diferentes concentrações de lítio, de forma a atingir a seguintes relações de sítios superficiais Li/(Mg+Si): 0,5; 1,0; 2,0 e 4,0. Os sólidos preparados foram caracterizados por difração de raios-X, análise termogravimétrica e termodiferencial, medida de área superficial BET e volume de poros. Constatou-se que para sólidos preparados a partir do óxido misto MgO-Si¿O IND. 2¿, há formação de um novo composto, MgSi¿O IND. 3¿. Na reação de acoplamento oxidativo de metano, quanto maior o teor de magnésio no sólido precursor (mais básico o sólido), maior é a conversão de metano e a seletividade a 'C IND. 2¿ ('C IND. 2¿¿H IND. 4¿ e 'C IND. 2¿¿H IND. 6¿). Por outro lado, o catalisador que apresenta uma relação equimolar Mg:Si foi o que obteve maior atividade areal, atribuída à presença de MgSi¿O IND. 3¿ no precursor, conforme constatado na caracterização / Abstract: The oxidative coupling of methane on Li/MgO-Si¿O IND. 2¿ catalyst was studied in this work. The influence of lithium and acid-basic properties of mixed oxide of MgO-Si¿O IND. 2¿ were studied in this reaction, with reactant gas mixture containing 'N IND. 2¿, 'C¿¿H IND. 4¿ and 'O IND. 2¿ with a volumetric ratio of 10:5:1. The overall flow rate were 100 'cm POT. 3¿ 'min POT. ¿1¿, with the reactor at 1070 and ambient pressure. The mixed oxides were prepared by the co-precipitation method, with nominal ratios Mg:Si of 1:0, 4:1, 1:1, 1:4 and 0:1. Lithium was added as an aqueous solution of 'LI IND. 2¿¿C¿¿O IND. 3¿ by the incipient wetness method, with lithium concentration, obtain the surface sites ratios (Li/Mg+Si) of 0,5; 1,0; 2,0 and 4,0. The solids were characterized by ray-X diffraction, thermogravimetric and thermodifferential analysis and BET surface area. MgSi¿O IND. 3¿ was observed on the mixed oxides of MgO-Si¿O IND. 2¿. Both the methane conversion and selectivity to 'C IND. 2¿ ('C IND. 2¿¿H IND. 4¿ and 'C IND. 2¿¿H IND. 6¿) increased as the ratio Mg:Si in the solids. On the other hand, the solid with ratio Mg:Si = 1:1 had the largest catalytic activity, attributed the presence o MgSi¿O IND. 3¿ in the precursor solid, observed in the characterization / Mestrado / Desenvolvimento de Processos Químicos / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267265 |
| Date | 27 August 1997 |
| Creators | Martim, Emerson |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Valença, Gustavo Paim, 1960-, Sprung, Renato, Assaf, Jose Mansur |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 99f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds