Orientadores: Paulo Kharmandayan, Ivan Felizardo Contrera Toro / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Ciências Médicas / Made available in DSpace on 2018-08-26T14:18:09Z (GMT). No. of bitstreams: 1
Calderoni_DaviReis_D.pdf: 2411163 bytes, checksum: f124b9aeaf19c6f4e86c382fef12ffeb (MD5)
Previous issue date: 2014 / Resumo: Introdução: A reparação de um defeito craniano é um procedimento desafiador, que requer não somente o preenchimento da falha óssea mas também estabilidade a longo prazo do material empregado e restabelecimento do contorno e simetria. Diversos tipos de materiais com diferentes características bem como diferentes métodos de produção dos implantes vêm sendo testados, sem que ainda haja um substituto ósseo considerado ideal. No presente estudo foram investigadas as propriedades de osteointegração de implantes da liga Ti6Al4V construídos por prototipagem com poros tridimensionalmente conectados considerando a influência do recobrimento dos mesmos com uma camada delgada de ?-fosfato tricálcico nestas propriedades. Método: Trinta ratos foram submetidos à criação de defeitos ósseos bilaterais na calvária, que foram preenchidos com implantes, recobertos ou não com ?-fosfato tricálcico, de modo aleatório. Os animais foram distribuídos em grupos e sacrificados 15, 45 e 90 dias após o procedimento. A integração dos implantes foi inicialmente avaliada por ensaio de compressão. A interface osso-implante foi analisada por meio de microscopia eletrônica de varredura. Resultados: A força máxima para produzir o deslocamento inicial dos implantes foi aumentando durante o período estudado, alcançando valores da ordem de 100N para ambos os tipos de implante. Foi observada integração entre o osso e a superfície dos implantes, com crescimento ósseo progressivo no interior dos poros. Não foram observadas diferenças significativas entre implantes recobertos e não recobertos por ?-fosfato tricálcico. Conclusão: Foi alcançada uma adequada osteointegração nas reconstruções cranianas utilizando implantes prototipados da liga Ti6Al4V com as características de porosidade e superfície descritas, sem influência do recobrimento cerâmico adotado. Os resultados sugerem que as características de construção utilizadas podem ser incorporadas aos implantes para reconstrução craniana para melhorar os resultados cirúrgicos / Abstract: Background: The repair of a calvarial defect is a challenging procedure, requiring not only filling of the bone gap but long term stability of the employed material and satisfactory contour and symmetry. Several types of materials with different characteristics have been studied, as well as various methods of implant production. However, to date no ideal bone substitute has been found. The osseointegration properties of porous prototyped implants with tridimensionally interconnected pores made of the Ti6Al4V alloy and the influence of a thin layer of calcium phosphate coating were investigated. Methods: Bilateral critical size calvarial defects were produced in thirty rats and filled with coated and uncoated implants in a randomized fashion. The animals were distributed in groups and kept for 15, 45 and 90 days before sacrifice. Implant mechanical integration to bone was evaluated with a push-out test. Bone-implant interface was analyzed using scanning electron microscopy. Results: The maximum force to produce initial displacement of the implants increased during the study period, reaching values around 100N for both types of implants. Intimate contact between bone and implant surface was present, with progressive bone growth into the pores. No significant differences were seen between coated and uncoated implants. Conclusion: Adequate osseointegration can be achieved in calvarial reconstructions using prototyped Ti6Al4V scaffolds with the described physical characteristics of surface and porosity. The results suggest that the proposed implant design characteristics can be incorporated into calvarial implants to improve reconstructive results. / Doutorado / Fisiopatologia Cirúrgica / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/312994 |
| Date | 26 August 2018 |
| Creators | Calderoni, Davi Reis, 1982- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Toro, Ivan Felizardo Contrera, 1957-, Kharmandayan, Paulo, 1957-, Montero, Edna Frasson de Souza, Filho, Luiz Gonzaga de Freitas, Coy, Claudio Saddy Rodrigues, Miranda, João Batista de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Ciências Médicas, Programa de Pós-Graduação em Ciências da Cirurgia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Multilíngua |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 54 f : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds