Objetivo: Comparar in vitro la rugosidad superficial de 2 resinas Bulk Fill utilizando dos sistemas de pulido de cauchos abrasivos: JOTA® (Suiza) (oxido de aluminio, carburo de silicio y silicona) y Optimize® (TDV) (Alemania) (silicona-oxido de aluminio).
Materiales y métodos: Se utilizaron 60 especímenes de resina divididos en cuatro grupos G1: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos)/ sistema de pulido JOTA®(Suiza), G2: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos)/sistema de pulido Optimize® (TDV) (Alemania), G3: Aura Bulk Fill (SDI, Brasil) / sistema de pulido JOTA® (Suiza) y G4: Aura Bulk Fill (SDI, Brasil) /sistema de pulido Optimize® (TDV) (Alemania). Todos los especímenes fueron confeccionados con una matriz metálica (6mm x 4mm), donde se insertó las resinas con una espátula de resina (TNCIGFT2 Hu Friedy), y se fotoactivó con la lámpara Elipar LedTM (3M-ESPE), con una intensidad 1200 mW/cm2. Inmediatamente, se midió la rugosidad inicial de todos los grupos con el rugosímetro Mitutoyo SJ-210P (China). Posteriormente, se realizó los pulidos con los dos sistemas de cauchos según cada grupo, y se procedió a medir la rugosidad final.
Resultados: Se encontró diferencia estadísticamente significativa en la rugosidad del grupo G1. Esta diferencia es mayor a la de los demás grupos evaluados, y que la menor diferencia en la rugosidad fue la encontrada en el grupo G2. Asimismo, se encontró diferencia estadísticamente significativa en la comparación realizada entre las resinas evaluadas y los sistemas de pulido evaluados.
Conclusiones: La rugosidad superficial encontrada en la evaluación de la resina Bulk Fill Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, Estados Unidos), con el sistema de pulido JOTA® (Suiza) presenta una menor rugosidad que la resina Aura Bulk Fill (SDI, Brasil) con los dos sistemas de pulido evaluados. / Objective: Comparison in vitro the superficial roughness of two Bulk Fill resins using two polishing systems of abrasives rubbers: JOTA® (Switzerland) (aluminum oxide, silicium carbide and silicone) and Optimize® (TDV) (Germany) (silicone- aluminum oxide).
Materials and methods: Were used 60 resin specimens of resin divided in four groups G1: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA)/ polishing system JOTA®( Switzerland), G2: Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA)/polishing system Optimize® (TDV) (Germany), G3: Aura Bulk Fill (SDI, Brazil) / polishing system JOTA® (Switzerland) y G4: Aura Bulk Fill (SDI, Brazil) / polishing system Optimize® (TDV) (Germany). All the specimens were made in a metal matrix (6mm x 4mm), were the resins were inserted with a resin spatula (TNCIGFT2 Hu Friedy), and fotoactivated with a lamp Elipar LedTM (3M-ESPE), with an intensity of 1200 mW/cm2. Immediately, the initial roughness of all groups is measured with the Roughness meter Mitutoyo SJ-210P (China). Subsequently, the polishing was executed out with the two rubber systems according to each group, and the final roughness was measured.
Results: Statistically significant difference was found on the roughness of G1. This is even greater than all the groups evaluated, and that the smallest difference was in the G2 group. A statistically significant difference was found when comparing the two resins with the polishing systems evaluated.
Conclusions: The surface roughness found in the evaluation of Bulk Fill Tetric-N Ceram® Bulk Fill (Ivoclar Vivadent, USA), with the JOTA® (Switzerland) polishing system presents the lower roughness than Aura Bulk Fill resin (SDI, Brazil) with the two polishing systems evaluated.
| Identifer | oai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/621895 |
| Date | 16 June 2016 |
| Creators | Vásquez Jiménez, Nadieska Morayma |
| Contributors | Hermoza, Monica |
| Publisher | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Source Sets | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Language | Spanish |
| Detected Language | English |
| Type | info:eu-repo/semantics/bachelorThesis |
| Source | Universidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico - UPC |
| Rights | http://creativecommons.org/licenses/by-nc-nd/4.0/, info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds