This report aims to increase the scientific knowledge about long-term prospects for the adhesive and adhesive joints for bonding of stainless steels. The effects of water, temperature and chemicals on the adhesive and adhesive joints are investigated. Stainless steel plates are pretreated with a primer and isopropanol, there after joined together with single lap modeling. The strength of the joint is tested with a tensile test and additionally a watertightness test is performed to determine if the joints are watertight. For this project three versions of stainless steels is used and two different technologies of two- part adhesives, silicone and silane-modified polymer and one technology of tape, a double coated acrylic foam tape are tested. The result shows that all the adhesives fails cohesively and that tape fails partly adhesively. Result shows that all tests are affected by water, temperature and chemicals on different levels but tape is affected the most with a minimum of 40% loss in shear strength. Watertightness test shows that aged tape joints are not watertight. The polymer shows no signs of decreasing in shear strength and is watertight, but does become more viscous by aging. The report shows that a possible combination of adhesive and pretreatment that can withstand the effects of water, temperature and chemicals is found. The polymer presents a possibility to bond stainless steel with a simple pretreatment. Tape didn’t pass the test in a suitable way but presents opportunities if a sufficient pretreatment can be found.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:his-13707 |
| Date | January 2017 |
| Creators | Andersson, Viktor, Larsson, Andreas |
| Publisher | Högskolan i Skövde, Institutionen för ingenjörsvetenskap, Högskolan i Skövde, Institutionen för ingenjörsvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds