The objective of this study is to successfully deposit Titanium Ti-6Al-4V layers onto Ti-6Al-4V substrate using two new commercially available Cold Spray processes such as Low Pressure Cold Spray (LPCS) and Pulsed Gas Dynamic Spray (PGDS). The second objective of this work is to develop a technique to repair Titanium parts since there is currently no repair technique commercially available. It is envisioned that commercial cold spray systems could be used to repair gashes on Titanium components. The examination of both feedstock powders and coatings were performed by different techniques such as optical microscopy and Scanning Electron Microscopy (SEM). Porosity, hardness, adhesion strength, flattening ratio, wipe test, fracture surface, wear test, XRD and chemical composition of the coatings using EDS have been evaluated. Cold spray has shown to be a promising technique for the deposition of heat sensitive particles such as titanium. LPCS and PGDS both produced high quality coatings. Low porosity, high hardness, adhesion strength over 40 MPa, metallurgical bonding, similar to bulk material wear rate, no oxide and nitride phases inside coating were measured.
| Identifer | oai:union.ndltd.org:uottawa.ca/oai:ruor.uottawa.ca:10393/24239 |
| Date | January 2013 |
| Creators | Pelletier, Jean-Louis |
| Contributors | Jodoin, Bertrand |
| Publisher | Université d'Ottawa / University of Ottawa |
| Source Sets | Université d’Ottawa |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0024 seconds