Philosophiae Doctor - PhD / Ammonia has attracted attention as a possible fuel for direct fuel cells since it is easy to handle under low pressure, costs only slightly higher than methanol and can easily be cracked down into hydrogen and nitrogen. At low temperature, ammonia oxidation on noble metal electrodes is a sluggish reaction and efficient catalysts are required to convert ammonia to nitrogen and hydrogen at reasonable reaction rates. In this thesis, I present polycrystalline and oriented nanoalloys synthesised at room temperature in aqueous media and their catalytic effects on the oxidation of ammonia. The electro-oxidation of ammonia on palladium-goldsilver (PdAuAgNPs) ternary nanoalloys was systematically studied in alkaline solution of potassium hydroxide (KOH) by cyclic voltammetry (CV). The PdAuAg nanoalloys were prepared through a facile synthesis with ascorbic acid as a reductant and polyvinylpyrrolidone (PVP) as a stabilising agent from aqueous solutions of PdCh/HAuCI4.3H20/AgN03 mixtures. UV-visible spectroscopy was used to confirm the complete reduction of the metal ions; absorption peaks observed at 260 nm, 285 nm and 420 nm for Ag", Au3+ and Pd2+ ions respectively, disappeared after reduction indicating a complete reduction of the metal ions to zero-valent nanoparticles. High resolution transmission electron microscopy (HR TEM) revealed the formation of crystalline nonaggregated 25-35 nm sized nanoalloys. The elemental composition of the nanoalloys measured using energy dispersive X-ray spectroscopy (EDX) showed the presence of the three elements; Pd, Au and Ag. The well-dispersed non-agglomerated PdAuAg nanoalloys exhibited a reduced overpotential and a 33%, 400%,82% and 54% increase in current density for ammonia electro-oxidation compared to Pd, PdAg, PdAu nanoparticles and bare Pt electrode, respectively. The much improved current density of the well-dispersed PdAuAg nanoalloys is attributed to the increased electrochemically active surface area of the nanoalloys. This electro catalytic behaviour of the PdAuAg nanoalloys for ammonia oxidation in KOH solutions provides a promising route for development of low-cost and high performance electro catalyst for electro-oxidation of ammoniaMoreover, ammonia oxidation on platinum surfaces has been found to be a very structure sensitive reaction which takes place almost exclusively on Pt(100) surfaces. I report for the first time the preparation of sodium polyacrylate-capped Pt(100)Pd, pte 1OO)Au, pte 1OO)Ir, Pt(IOO)Rh, Pt(100)PdAu, Pt(100)IrAu, Pt(IOO)PdIr and Pt(IOO)RhAu nanoalloys. The reduction of the metal ions to nanoparticles was confirmed by UV-visible spectroscopy while the shapes and the structures of the nanoparticles were studied using HRTEM and CV. HRTEM analysis showed well distributed non-agglomerated 5-20 nm semi-spherical and cubic nanoalloys with lattice fridges on their surfaces indicating the crystalline nature of the nanoalloys. Pt(100) nanoalloy systems showed particles with triangular and cubic shapes. The existence of the preferentially cubic shaped nanoparticles in the samples indicated that the nanoalloys had some (100) sites orientation/a significant amount of (100) sites at their surfaces. The CV of the nanoparticles in the hydrogen adsorption/desorption region (-200 mV to 100 mV vs. Ag! AgCl) was used to obtain qualitative information about the surface structure of the nanoparticles. The voltammogram of oriented Pt(100) nanoparticles showed very clearly the presence of adsorption states associated with (110) sites, (100) domains and (l00) sites at -131 mV, -34 mV and 29 mV, respectively. The companson of this voltammetric profile with that obtained for a Pt(100) single crystal electrode clearly points out that the synthesised Pt nanoparticles have a high density of (100) sites. However, the peak that was observed at 29 mV in the CV of Pt(100) nanoparticles was not present in the vo ltammo grams of the Pt(100) nanoalloy systems confirming the formation of the nanoalloys. The results reported in this work demonstrate the importance of controlling the intrinsic structural properties of Pt nanoparticles; in terms of nature of the active sites and the effect of adding adatoms (such as Au, Pd, Rh, Ir) in order to understand their catalytic properties. The electrochemical activities of these nanoparticles for ammonia oxidation in basic medium showed an increase of over 100% current density compared to Pt electrode. Pt(lOO)RhAu nanoalloys showed the highest catalytic properties while Pt(lOO)PdAu had the lowest as shown in the trend: Pt(lOO)RhAu > Pt(lOO)PdIr > Pt(lOO) > Pt(lOO)IrAu > Pt(lOO)Pd> Pt(lOO)Rh > Pt(lOO)Au > Pt(lOO)Ir > Pt(lOO)PdAu. The synthesised oriented nanoalloys were further interrogated towards the oxidation of hydrazine as a fuel for hydrazine fuel cells. The oriented Pt(lOO) nanoparticles and Pt(lOO) nanoalloy systems exhibited over 1000% increase in current density and reduced oxidation overpotential compared to bare glassy carbon electrode. These excellent catalytic properties are attributed to the increased surface area and the presence of (100) sites which favour the oxidation of hydrazine.

The present work deals with the use of manganese oxide as a catalyst for positive electrode of fuel cells. The theoretical part is to analyze the problem of fuel cells, focusing on lowtemperature fuel cells. Are discussed and the methods of measurement and evaluation of properties of manganese oxide layer. The practical part deals with doping electrolytic manganese dioxide salts of divalent metals and monitoring their behavior in the cyclic voltammetry by the EQCM method.

Nowadays it is attached to a major effort to study applications of nanoparticles in biosensors technology. We studied the effect of gold nanoparticles on the surface of the electrodes by Electrochemical Impedance Spectroscopy method and Cyclic Voltammetry. For impedance measurements was proposed substitute electrical model and cyclic voltammetry method was used to determine the electroactive surface of electrodes.

The present work deals with the research and development of gel polymer electrolytes and their applications. Thesis talks about the mechanisms that take place in gel electro-lytes. It also discusses the electroanalytical methods used in assessing the gel electro-lytes. The main focus of the work is the preparation of gel polymer electrolytes and compared their properties using methods of impedance spectroscopy, cyclic voltam-metry and methods of measurement of transference numbers. KEYWORDS

The aim of this thesis is to summarize the available evidence about quantum dots and their effects on living systems. The text describes methods for the preparation of quantum dots with respect to their characteristics (size, fluorescence wavelength) and methods of quantum dots bio-functionalization of biomolecules. In living organisms is a large number of proteins, because these are considered as one of the main components of the interaction of organisms. Therefore, the work also provides basic information about proteins. Finally, there are described various methods by which the quantum dots may be characterized mainly by differential pulse voltammetry measurement zeta potential and fluorescence measurement. The main objective of this work is to propose models of different environments in which will be degradation of quantum dots with regard to the evaluation of acquired kinetic parameters for predicting the stability of individual quantum dots.

This dissertation work deals with analysis of nickel hydroxide phases, their oxidation compounds, their stability and degradation mechanisms of electrochemically more active alpha phase on standard beta phase. The active material was prepared by both methods, electrodeposition and chemical precipitation. Main analysis method was Electrochemical Quartz Crystal Microbalance in combination with common analytical methods (cyclic voltammetry, potenciometry) can resolute between alpha and beta phases and quantitatively describe differences in main reaction by monitoring mass changes in the active material. Poor stability of the ?-Ni(OH)2 were improved by adding cations with valence two three and four into the structure instead of Ni atoms. The most important role plays cobalt and its hydroxide. Totally new way is to use titanium in combination with other cations. In electrolyte the most significant addition is LiOH, which has beneficial influent on cycle ability, stability in strong alkaline medium and cycle life.

Nowadays, nanostructures fixed on solid substrates and colloidal nanoparticles permeate through all areas of human life, in area of sensors and detection as well. This dissertation thesis deals with the fabrication of nanostructures on the surface of planar electrodes via self-ordered nanoporous template of aluminum trioxide. The nanofabrication, as one of many possible techniques, is used to increase the active surface area of electrodes by creating unique surface types with specific properties. These electrodes are very perspective in the applications, such as biomolecules electrochemical detection and measurement. The transformation of aluminum layer into non-conductive nanoporous template in the process of anodic oxidation is a fundamental technique employed to obtain the array of nanostructures in this thesis. The fabrication of high quality nanoporous membranes with narrow pore size distribution on various types of metallic multilayers is one of the key experimental parts in this work. Several problems associated with the production of the thin-film systems, including the dissolving the barrier oxide layer, are discussed and solved. Another part of this work deals with the use of nanoporous membrane as a template for the production of metallic nanostructures via electrochemical metal ions deposition directly into the pores. The obtained nanostructures as nanowires, nanorods or nanodots are characterized by the scanning electron microscopy and energy-dispersive or wavelength X-ray spectroscopy. The electrode surface, modified by gold nanostructures suitable for the detection of biomolecules, has been chosen for the electrochemical measurements, due to the gold biocompatibility. The nanostructured electrodes were characterized by electrochemical impedance spectroscopy and cyclic voltammetry. The effect of nanostructured surface geometrical parameters, including the size of the electrochemically active area, on the results of electrochemical measurements has been observed and compared to flat gold electrodes. Two model biomolecules, namely guanine and glutathione, have been chosen for the study of potential application of these nanostructures in biosensors.

This thesis is focused on the effect of plasmatic oxidation of carbon working electrode on its electrochemical response. In the theoretical part, the thesis describes thick film technology, working carbon electrodes, cyclic voltammetry, contact angle measurement and plasma. Experimental part is dedicated to characterization of plasma modified electrode. Results are compare with unmodified electrodes.

Hlavním cílem této práce je charakterizace vzorků titanátů, jako materiálů pro sodíko-iontové (Na-ion) akumulátory. Syntéza některých vzorků je součástí této práce. Charakterizace je zaměřena na elektrochemické vlastnosti, složení a morfologii použitých materiálů. První část se zabývá lithium-iontovými (Li-ion) akumulátory. Byly vybrány, protože jsou ve vědeckých článcích dobře popsány a základní funkční princip je aplikovatelný také na Na-ion akumulátory. Materiály používáné pro katody, anody a elektrolyty následují po krátké části shrnující parametry a konstrukci Li-ion akumulátorů. Následující kapitola je zaměřena na sodíko-iontové akumulátory. Srovnání sodíku a lithia je následováno materiály používanými pro elektrody a elektrolyty (s důrazem na anodové materiály). Třetí část popisuje analytické metody použité pro charakterizaci elektrod a materiálů. Jedná se o elektrochemickou charakterizaci (cyklická voltametrie a galvanostatické cyklování s potenciálovým omezením), morfologii (rastrovací elektronová mikroskopie) a složení (X-ray difrakční spektroskopie). Poslední dvě kapitoly obsahují syntézu a charakterizaci sodného titanátu a charakterizaci dvou vzorků TiO2. Výsledky této práce jsou shrnuty v závěru.

In der vorliegenden Dissertation geht es um die Synthese und Charakterisierung chiraler, redoxaktiver (Raumtemperatur-)Ionischer Flüssigkeiten basierend auf Ferrocen und der natürlich vorkommenden Aminosäure S-Prolin. Diese Baueinheiten sind entweder über eine Ether- oder über eine Esterverbrückung verknüpft. Auch der Anionenaustausch vom I– - zum CF3SO3– - sowie (CF3SO2)2N– -Salz (kurz NTf2–) wird dargelegt und der Einfluss des Anions auf den Schmelzpunkt der Verbindungen untersucht und diskutiert. Die Redoxaktivität wird durch das im Ferrocen enthaltene Fe II eingebracht, das reversibel zu Fe III oxidiert werden kann. Aufgrund des Pyrrolidin-Rings sind die dargestellten Verbindungen stets chiral und bilden nach der Quaternisierung mit Halogenalkanen Diastereomere, soweit die Alkylkette größer als Methyl ist. Das Diastereomerenverhältnis wurde mittels 1H-NMR-Spektroskopie und in einem Fall anhand von Röntgenpulverdiffraktogrammen durch Rietveld-Verfeinerung analysiert. Die Verbindungen wurden thermisch anhand simultaner thermischer Analysenund Tieftemperaturversuchen untersucht, die belegen, dass die Synthese von insgesamt sechs neuen Raumtemperatur-Ionischen Flüssigkeiten gelang. Davon basiert eine Verbindung, (1S2S)- und (1R2S)-2-[(Ferrocenylcarbonyl)oxy]methylen-N-methyl-N-pentylpyrrolidin-1-iumiodid, auf I– und fünf Verbindungen enthalten NTf2– als Gegenion. Das Diastereomerengemisch der Verbindungen (1S2S)- und (1R2S)-N-Butyl-2-[(ferrocenylcarbonyl)oxy]methylen-N-methylpyrrolidin-1-ium NTf2– besitzt den größten Flüssigkeitsbereich von -25 bis +263 °C und auch die höchste Zersetzungstemperatur aller hier dargestellten Verbindungen. Insgesamt werden in dieser Arbeit elf Einkristallstrukturanalysen vorgestellt, wobei es sich um drei Verbindungen des Typs FcCH2N(CH3)2(CnH2n+1)I (Fc = Ferrocenyl, n = 1,2,3), Ferrocenmonocarbonsäurechlorid, zwei ether- sowie fünf esterverbrückte Verbindungen handelt. Mikrokristalline Proben wurden mittels Röntgenpulverdiffraktometrie charakterisiert. Ergänzende Analysen wurden mittels UV-Vis- und IR-Spektroskopie sowie Massenspektrometrie und Elementaranalyse durchgeführt. Ein wichtiger Aspekt bei Ferrocenverbindungen ist das Redoxpotential, welches mittels Cyclovoltammetrie bestimmt wurde. Hierbei liegt das Formalpotential des Fe II /Fe III -Redoxpaars der etherverbrückten Verbindungen bei +0,05 V und bei den esterverbrückten Verbindungen unabhängig vom Anion bei +0,28 V vs. Ferrocen/Ferrocenium in Acetonitril. Bei den iodidhaltigen Verbindungen zeigt das I– -Ion ebenfalls eine Redoxaktivität bei E(0,f,Fc) = -0,18 V und 0,22V. Die Diffusionskoeffizienten der esterverbrückten Triflat- und NTf2– -Verbindungen liegen in der Größenordnung von 7·10−6 cm2/s und die heterogenen Geschwindigkeitskonstanten bei 0,01 cm/s. / The present dissertation deals with the synthesis and characterization of chiral, redoxactive room temperature ionic liquids (RTILs) based on ferrocene and the naturally occurring amino acid S-proline. These building blocks are coupled either via an ether- or an ester-bridge. The anion exchange from I– to CF3SO3– and (CF3SO2)2N– salts (abbreviated as NTf2–) is presented. The influence of the anion on the melting point of the compound is investigated and discussed. The redox activity is introduced into the molecule via the Fe II -containing ferrocenyl groups, which can be oxidized reversibly to Fe III . The synthesized compounds based on the pyrrolidine ring are chiral. After quaternization with alkyl halides, they form diastereomers in case of alkyl chains longer than methyl. The ratio of the different diastereomers was analyzed by 1H NMR spectroscopy and, in one case, by Rietveld refinement of the X-ray powder diffraction pattern. The thermal behavior of the compounds was studied by simultaneous thermal analysis and low temperature experiments. The results show the successful synthesis of six new RTILs. One of them is based on iodide ((1S2S)- and (1R2S)-2-[(ferrocenylcarbonyl)oxy]methylene-N-methyl- N-pentylpyrrolidine-1-ium iodide) and six RTILs contain NTf2– as counter ion. The diastereomeric mixture of compounds (1S2S)- and (1R2S)-N-butyl-2-[(ferrocenylcarbonyl)oxy]methylene-N-methylpyrrolidine-1-ium NTf2– exhibits the widest liquid range from -25 to +263 °C and the highest decomposition temperature of all compounds presented herein. Eleven single crystal structure analyses are presented. Three of them belong to compounds FcCH2N(CH3)2(CnH2n+1)I (with Fc = ferrocenyl and n = 1,2,3), then ferrocene monocarboxylic acid chloride, two of ether- as well as five ester-bridged compounds. Microcrystalline samples were characterized by X-ray powder diffractometry. Supplementary analyses by UV/Vis and IR spectroscopy as well as mass spectrometry and elemental analyses have been carried out. An important feature of ferrocene containing compounds is their redox potential which is determined with cyclic voltammetry. The formal potential of the Fe II /Fe III redox couple in the ether-bridged compounds is at +0.05 V and in the ester-bridged compounds independent from the type of anion at +0.28 V vs. ferro- cene/ferrocenium in acetonitrile. The I– anion shows as well redox activity with formal potentials at E(0,f,Fc) = -0.18 V and 0.22 V. The diffusion coefficients of the ester-bridged triflate and NTf2– compounds are in the order of 7·10−6 cm2/s, the heterogeneous rate constants in the order of 0.01 cm/s.