91 |
Resistencia ao cisalhamento de braquetes fixados com resinas polimerizadas por diferentes tipos de ativaçãoGuedes-Pinto, Eduardo 27 November 1997 (has links)
Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T01:37:33Z (GMT). No. of bitstreams: 1
Guedes-Pinto_Eduardo_M.pdf: 2855830 bytes, checksum: ffca1786148a3514f02f16d72b6577e2 (MD5)
Previous issue date: 1997 / Resumo: A proposta deste estudo foi avaliar a resistência ao cisalhamento de três materiais de colagem, polimerizados por diferentes sistemas de ativação. Foram utilizados 60 pré-molares humanos, extraídos com finalidade de tratamento ortodôntico. As faces vestibulares foram condicionadas com ácido fosfórico a 37% durante 30 segundos e os bráquetes fixados ao esmalte dentário com as . resinas Concise Ortodôntico (3M), Z-100 (3M) e cimento resinoso Dual (3M). Após a fixação dos bráquetes metálicos, os corpos-de-prova foram submetidos ao teste de cisalhamento 10 minutos e 24 horas após as colagens. Os resultados submetidos à análise estatística mostraram que houve diferença estatisticamente significante entre os três tipos de resina para os dois períodos de tempo de armazenamento. O sistema de colagem mais resistente foi promovido pelo Concise Ortodôntico, seguido pela resina fotoativada Z-100, e o menos resistente foi o cimento resinoso Dual. O tempo de armazenamento foi estatisticamente significante, pois representou aumento na resistência ao cisalhamento nos três tipos de materiais, provavelmente, devido à contínua conversão dos radicais livres / Abstract: The purpose of this study was to evaluate the shear bond strengths of three bonding materiaIs, activated by different systems. Sixty human premolars, extracted for orthodontic reasons, were used. Vestibular faces were etched for 30 seconds with 37% phosphoric acid gel and brackets were bonded to enamel surface using Concise chemically cured adhesive (3M), Z-100 light-cured adhesive (3M) and Dual cemerit resin (3M). After the bonding of metal brackets, specimens were tested and the shear stress at bond failure was recorded at 10 minutes and 24 hours. Results submitted to statistical analysis demonstrated a statistically significant difference in shear bond strengths among the three resins for both periods of storage. The most resistant bonding system was the Concise group, followed by the light-cured Z-100 and the less resistant Dual cement resin. The storage was statistically significant by increasing the shear bond strengths of the three materiaIs, probably because of the continue conversion / Mestrado / Ortodontia / Mestre em Ciências
|
92 |
Influencia do substrato dentinario e do material restaurador na infiltração marginal de restaurações cervicaisSaito, Solange Katia 08 January 2001 (has links)
Orientador : Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T23:46:19Z (GMT). No. of bitstreams: 1
Saito_SolangeKatia_D.pdf: 2022044 bytes, checksum: 1448f462721703745289700cf45f625b (MD5)
Previous issue date: 2001 / Resumo: O objetivo deste trabalho foi avaliar, quantitativamente, a infiltração marginal de diferentes sistemas restauradores, quando colocados em substrato dentinário normal ou hipermineralizado artificialmente. Cento e oito cavidades foram confeccionadas em raízes de dentes bovinos e divididas em dois grupos experimentais (normal ou hipermineralizado), sendo subdivididas em quatro grupos, conforme o sistema restaurador utilizado: Vidrion R caps, Vitremer, Single Bond/Filtek Z250 e Clearfil SE Bond/Filtek Z250. A dentina foi hipermineralizada nas soluções: 1,5M de cálcio (CaCl2H2O, pH 5,7) por 1 hora e 1,5M de fosfato (K2HPO4, pH 9,5) por mais 1 hora, sendo, estocados em saliva artificial {1,5mM de cálcio (CaCl2H2O)+ 0,9mM de fosfato (K2HPO4)+ 0,15M de KCI; pH 7,0} por 24 horas, após a realização dos preparos cavitários. Os sistemas restauradores foram colocados em dentina hipermineralizada (Grupos I, ID, V e VII) e dentina normal (Grupos II, IV, VI e VllI). Os dentes restaurados foram submetidos a 1000 ciclos térmicos, entre temperaturas de 5 e 55±2°C. Em seguida, foram imersos em solução de azul de metileno a 2% por 24 horas. As amostras foram trituradas e o pó diluído em 4 ml de álcool absoluto. A infiltração marginal foi determinada e expressa em concentração de corante (ml). Os dados analisados pelos testes de Kruskal-Wallis e Ryan mostraram que não houve diferença estatística entre substrato; no entanto, houve diferença significante entre os materiais (p<0,01). Os resultados obtidos foram (mg/mI): GI-55,9a; GII-64,3a; GIII-12,lb; GIV-2I,2b; GV-32,9bc; GVI 30,lbc; GVll-41,9cd; GVIII-37,7cd. A microinfiltração relacionada com Vidrion R caps foi maior quando comparada com a dos outros materiais. As cavidades restauradas com Vitremer apresentaram valores de infiltração marginal semelhante ao sistema Single Bond/Filtek Z250 e este não diferiu do sistema Clearfil SE Bond/Filtek Z250 / Abstract: The aim of this study was to evaluate, quantitatively, the marginal leakage around different esthetic materials placed on normal and artificially hypermineralized cervical dentin cavities. One hundred eight cavities were prepared in bovine teeth roots and divided in two experimental groups (normal or hypermineralized), then subdivided in four subgroups according to the restorative system: Vidrion R caps, Vitremer, Single Bond/Filtek Z250 and Clearfil SE Bond/Filtek Z250. Dentin was hypermineralizing into the solutions contained: 1,5M calcium (CaCl2H20, pH 5,7) for 1 hour and 1,5M phosphate (K2HPO4, pH 9,5) for more 1 hour and then, stored in synthetic saliva {1,5mM calcium (CaCl2 H2O)+ 0,9mM phosphate (K2HPO4)+ 0,15M KCI; pH 7,0} for 24 hour, after cavities preparation. The restorative materials were placed in hipermineralized dentin (Groups 1, m, V and Vll) and normal dentin (Groups lI, IV, VI and VID). The restored teeth were submitted to 1000 thermal cycles between 5±2 °C and 55±:2 °C, then imersed in to 2% methylene blue solution for 24 hours. The samples were triturated and the powder were placed into absolute alcohol to dye extraction. The marginal leakage was determined and expressed by dye concentration (mm/ml). Data were analysed by the Kruskal-Wallis and Ryan test. The results were (mm/ml): GI- 55,9a; G-II 64,3a; G-III 12,lb; G-IV 21,2b; G-V 32,9bc; G-VI 30,lbc; G-VII 41,900; G-VIII 37,7cd. There was no statistically significant difference between the evaluated substrates; however, there was significant difference among materials (p<0,01). Microleakage related to Vidrion R caps material was greater than that any other material. Vitremer material presented the same marginalleakage values as Single BondIFiltek Z250. The latter didn't differ from Clearfil SE Bond system / Doutorado / Dentística / Doutor em Clínica Odontológica
|
93 |
"Avaliação da resistência adesiva e do padrão de condicionamento da dentina e do esmalte após a aplicação do ácido bórico a 2%".Leonardo Cesar Costa 13 June 2003 (has links)
O objetivo deste trabalho foi avaliar a resistência adesiva e o padrão de condicionamento do esmalte e da dentina após aplicação do ácido bórico a 2%. Foram utilizados terceiros molares humanos, condicionados com o ácido fosfórico a 35%, em forma de gel, e com diferentes formas de apresentações do ácido bórico a 2%. Para o estudo do padrão de condicioname nto, utilizaram-se discos de dentina e espécimes quadrangulares de esmalte que sofreram o condicionamento com as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% utilizadas por diferentes tempos de aplicações. Após os condicionamentos, os espécimes foram preparados para observação no microscópio eletrônico de varredura. Para a avaliação da resistência adesiva do esmalte e da dentina, através de testes de microtração, foram utilizadas as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% previamente à aplicação de dois sistemas adesivos (Single-Bond e Prime & Bond NT) e de duas resinas composta (Z-250 e TPH). Após os procedimentos adesivos, os dentes sofreram seccionamentos seriados a fim de que fossem obtidos espécimes para os testes de resistência adesiva. Os valores adesivos foram submetidos ao teste de análise de variância (ANOVA) e ao teste de Tukey, para a verificação de possíveis diferenças estatísticas entre os grupos, e em ambos os testes foi adotado um nível de significância de 5% (p< 0,05%). Na dentina e no esmalte, a solução de ácido fosfórico a 35% apresentou um maior poder desmineralizante comparado com as soluções de ácido bórico a 2%. Com relação aos valores de resistência adesiva na dentina, quando se utilizaram as diferentes soluções ácidas com o sistema adesivo Single-Bond e a resina composta Z-250, o grupo condicionado com ácido fosfórico apresentou valores adesivos significantemente maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Porém, quando se utilizou o sistema adesivo Prime & Bond NT e a resina composta TPH, os valores adesivos dos grupos que sofreram os diferentes condicionamentos ácidos não apresentaram diferenças estatísticas entre si. No esmalte, quando se utilizaram as diferentes soluções ácidas em associação com o sistema adesivo Single-Bond e a resina composta Z-250, e também com o sistema adesivo Prime & Bond NT e a resina composta TPH, os grupos que sofreram o condicionamenmto com o ácido fosfórico a 35% apresentaram valores adesivos significantementre maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Assim, pode-se concluir que o tratamento superficial da dentina e do esmalte com as soluções de ácido bórico a 2% não forneceu substratos com características suficientes para proporcionar resistência adesiva semelhante à fornecida pelo ácido fosfórico a 35%. / The aim of this laboratory work was to evaluate the bond strength and etching pattern of dentin and enamel conditioned by 2% boric acid. In this study, human third molars etched with 35% phosphoric acid and different solutions of 2% boric acid were utilized. For the etching pattern determination discs of dentin and square enamel specimens were conditioned (35% phosphoric acid and 2% boric acid solutions) and prepared for scanning electron microscopic observations. For dentin and enamel bond strengths evaluation the microtensile test was used. Phosphoric acid (35%) and boric acid (2%) were utilized in combination with two adhesive systems (Single-Bond and Prime & Bond NT) and two different composite resins (Z-250 and TPH). After bonding procedures, the teeth were sectioned and the obtained specimens submitted for microtensile tests. The results were analyzed by ANOVA followed Tukeys analysis at a significance level of 5% (p<0,05). The 35% phosphoric acid solution presented higher demineralization power when compared to 2% boric acid solutions either in dentin or enamel. Regarding to the bond strength in dentin, when 35% phosphoric acid solution was used in combination with Single-Bond adhesive system and Z-250 composite resin the values were significantly higher when compared to other acid solutions. Therefore,whem the Prime & Bond NT adhesive system and TPH composite resin were utilized,no statisticaly different values were demonstrated for bond strenght among different acid solutions. In enamel, different acid solutions were also combined with Single-Bond and Prime & Bond adhesive systems and Z-250 and TPH composite resins. Groups etched with 35% phosphoric acid solution presented bond strength values significantly higher than other acid solutions. In conclusion, the utilization of 2% boric acid solution for etching dentin or enamel did not provide characteristics in this substrates and bond strength values similar to 35% phosphoric acid solution.
|
94 |
Avaliação do laser Er:YAG como condicionador de esmalte e dentina para procedimento de união a materiais resinososGuimarães, Priscilla Santos 15 January 2003 (has links)
Orientador : Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T20:41:10Z (GMT). No. of bitstreams: 1
Guimaraes_PriscillaSantos_D.pdf: 2015772 bytes, checksum: 3f7222b016b716845a6ac1634aeb1d81 (MD5)
Previous issue date: 2002 / Resumo: O objetivo deste estudo foi verificar: 1) qual nível de energia que produziria o aspecto morfológico mais próximo do esmalte e dentina condicionados pelo ácido fosfórico no tecido dental irradiado por laser Er:YAG, por meio da observação ao microscópio eletrônico de varredura; 2) a resistência de união à tração de um sistema adesivo sobre superfícies de esmalte e dentina tratados com ácido fosfórico ou com laser Er:YAG, utilizando a energia estabelecida na observação morfológica. Para esta observação foram utilizados quatro terceiros molares humanos hígidos, extraídos por razões ortodônticas, que tiveram suas coroas separadas das respectivas raízes e então, seccionadas ao meio, no sentido mésio-distal. As superfícies vestibulares em esmalte, foram irradiadas com laser Er:Y AG, sob refrigeração com água, em sete pontos de incidência. Foram utilizados os seguintes níveis de energia, para cada ponto irradiado: 60, 100, 160, 200, 300, 400 e 500 mJ. A superfície lingual dos dentes foi preparada com pontas diamantadas em alta rotação, sob refrigeração, até exposição da dentina, sendo em seguida irradiada da mesma forma descrita. Decorridas 48 horas após a irradiação, as amostras foram metalizadas e observadas ao microscópio eletrônico de varredura. Para o ensaio de resistência de união foram utilizados 40 terceiros molares humanos hígidos, que tiveram suas raízes seccionadas e as coroas foram incluídas em resina acrílica ativada quimicamente em cilindros de plástico, com 20 mm de diâmetro externo por 20 mm de altura, com a face oclusal voltada para cima. Os cilindros de resina contendo as porções dentárias foram separados aleatoriamente em quatro grupos de 10 amostras cada, de acordo com o tipo de tecido e de condicionamento a ser empregado. Em seguida, as amostras foram desgastadas em politriz horizontal com lixas d'água de granulação 220, 400, 600, 800 e 1000. As superfícies das amostras foram examinadas em lupa estereoscópica, para assegurar que na região de teste só houvesse esmalte ou dentina expostos, dependendo do grupo experimental ao qual pertencem. A obtenção dos corpos-de-prova para o ensaio de tração foi realizada com um dispositivo, preconizado pela ISO, visando um perfeito alinhamento durante o procedimento de união. Os grupos 1 e 3 tiveram suas superfícies condicionadas com laser Er:Y AG com potência de 100 mJ, selecionada a partir dos resultados obtidos na observação morfológica; e as amostras dos grupos 2 e 4 foram condicionadas com ácido fosfórico a 35%, por 15 segundos. O sistema adesivo empregado para todos os grupos foi o Single-Bond (3M) e a resina Z-250 (3M), de acordo com instruções do fabricante. O ensaio de tração foi realizado 24 horas após o procedimento de união, em máquina de ensaio universallnstron modelo 4411, à velocidade de 0,5 mm/min. Os resultados foram submetidos ao teste de Tukey em nível de 5% de probabilidade. O aspecto morfológico das amostras irradiadas com laser Er:Y AG com potência de 100 mJ por pulso, apresentou-se como o mais favorável para o procedimento de união com materiais resinosos, tanto em esmalte quanto em dentina. Os valores médios de resistência de união ao esmalte e dentina condicionados com laser Er:YAG foram estatisticamente inferiores (p<0,05) àqueles obtidos para o condicionamento com ácido fosfórico. Os valores médios de resistência de união ao esmalte foram estatisticamente superiores àqueles para o tecido dentinário (p<0,05), independente do tipo de condicionamento utilizado / Abstract: The purpose of this study was to verify: 1) the energy levei that could produce the morphologic aspect similar to dental tissues conditioned with phosphoric acid on dental tissues irradiated by Er:Y AG (Yttrium aluminium gamet Y ~L5012) laser; 2) the tension bond strength of an adhesive system applied over enamel and dentin, after pretreatment with phosphoric acid or Er:YAG laser, using the energy levei established on the morphologic analysis. Four third human molars, extracted for orthodontic reasons, were used to make the morphologic analysis. The teeth had their crowns separated from the roots and than, each crown were sectioned in two. The buccal surfaces in enamel, were irradiated with Er:YAG laser, under water cooling, in seven different spots. The following energy levels were used for each spot of irradiation: 60, 100, 160, 200, 300, 400 and 500 mJ. The lingual dental surfaces were prepared with diamond burs, under water cooling, in order to expose dentin substrate, and afterwards were irradiated in the same way described for enamel. After 48 hours, the samples were sputtered with gold and observed under scanning electron microscope. For the tension bond strength test, 40 third human molars had their crowns separated from the roots and were than included in auto activated acrylic resin in plastic cylinders, with 20 mm in outside diameter by 20 mm high, with the occlusal surface facing up. The resin cylinders with the dental portions were randomly separated in four groups of 10 samples each, according to the dental tissue and conditioning method to be used. After, the samples were polished, under water, in a horizontal polishing machine with sandpaper 220, 400, 600, 800 and 1000 grito The samples surfaces were examined under esthereoscopic lens, to assure that on the test region would be exposed only enamel or dentin, depending on the experimental group they belong. In order to obtain the samples for the tension bond strength test, a device idealized by ISO were used, with the purpose of getting a perfect alignment during the bonding procedure. Groups 1 and 3 had their surfaces irradiated with Er:Y AG laser, energy levei of 100 mJ, chosen from the results obtained in morphologic analysis; and the samples of groups 2 and 4 were conditioned with 35% phosphoric acid, for 15 seconds. The adhesive system used, for ali test groups, was Single Bond (3M) and the resin 2-250 (3M), according to manufacturer's instructions. The tension bond strength test was realized 24 hours after the bonding procedure, in a universal test machine Instron model 4411, with a cross head speed of 0,5 mm/min. The results were submitted to Tukey's test at a significance levei of p<0.05. From the results, the mean values of bond strength to enamel and dentin irradiated with Er:Y AG laser were statistically lower (p<0.05) than those for phosphoric acid conditioning. The mean values of bond strength to enamel were statistically higher (p<0.05) compared with dentin, no matter which type of conditioning method used. / Doutorado / Doutor em Materiais Dentários
|
95 |
Avaliação de tecnicas para inserção da resina composta e da utilização de um composito de baixa viscosidade na resistencia de união a parede gengival de cavidades classe IIReis, Andre Figueiredo 03 August 2018 (has links)
Orientador : Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T08:31:11Z (GMT). No. of bitstreams: 1
Reis_AndreFigueiredo_M.pdf: 27890848 bytes, checksum: 0ebc10d01fd7a4da9c97f26cca6fe9b5 (MD5)
Previous issue date: 2003 / Mestrado
|
96 |
Efeito da associação composito-materiais resilientes sobre a resistencia da união dentina/composito em modelos experimentais bi e tridimensionaisSantos, Alex Jose Souza dos 15 December 2003 (has links)
Orientador: Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T22:58:40Z (GMT). No. of bitstreams: 1
Santos_AlexJoseSouzados_D.pdf: 5116499 bytes, checksum: f65e728e88daf4b8db91116fb4821145 (MD5)
Previous issue date: 2003 / Resumo: O objetivo deste estudo foi avaliar o efeito do tipo de compósito e da camada elástica sobre a resistência da união dentina/compósito em modelos bi e tridimensionais. O esmalte oclusal de 96 molares humanos foi removido expondo a superfície plana de dentina na qual foram preparadas cavidades Classe I (Fator C = 4,5; dimensões= 4 mm M-D, 3 mm V -L e 3 mm de profundidade). Dezoito grupos experimentais (n=4) foram distribuídos pela combinação de três compósitos: SureFil, Filtek Z250 e Z100; e de seis diferentes camadas elásticas: 1- SB(lc), camada única do adesivo Single Bond; 2- SB(3c), três camadas do adesivo Single Bond; 3- SB+SBMP, uma camada de SB associada a duas camadas adicionais do adesivo Scotchbond Multi Purpose; 4- OS, aplicação de uma
camada do adesivo OptiBond Solo Plus; 5- SB+PLF, uma camada de SB associada ao compósito de alto escoamento Protect Liner F; e 6- SB+FF, uma camada de SB associada ao compósito de alto escoamento Filtek Flow. Cada camada adicional de adesivo foi fotoativada separadamente. Após a criação da "camada elástica", o compósito foi inserido em incremento único. Seis grupos adicionais foram obtidos a partir da união do compósito Esthet-X à parede livre de dentina vestibular (Fator C= 0,22; contração efetiva), seguindo os mesmos seis tipos de "camada elástica" realizados no modelo cavitário. As amostras foram armazenadas em água destilada a 37°C, por 24 h, antes do teste de tração. Os dentes foram preparados para microtração realizada numa máquina de ensaio universal (Instron 4411). Foram obtidos 4 palitos de cada dente (A _ 0,8 mm2), removidos da parede dentinária vestibular e testados a velocidade de 0,5mm/min. Os dados foram analisados pela análise de variância ANOV A e as médias de resistência de união (MRU) comparadas pelo teste de Tukey e Teste Dunnett ao nível de 5'0 de significância. As MRU variaram entre 11,2 e 29,6 MPa. Foi verificada diferença estatística entre as MRU para os diferentes compósitos (p= 0,0079) e entre as diferentes camadas elásticas tanto em cavidade (p< 0,0001) quanto parede-livre (p= 0,0095). O compósito Z250 apresentou, de forma geral, as maiores MRU com diferenças estatísticas daquelas apresentadas pelo compósito Z100. O compósito SureFil obteve resultados intermediários, sem diferenças estatísticas dos outros dois. No modelo cavitário, as MRU para o Z250, Z100 e SureFil foram respectivamente: SB+SBMP (27 / 22,9 / 20,4)a, SB+PLF (19,8 / 21,3 / 18,5)ab, SB+FF (21,3 / 19 / 15,4)bC, SB-3c (17,9 / 16,4 / 14,2)bC, 05-1 c (15,9 / 14,2 / 16)bC e SB-1c (17 / 14,8 / 11, 2)C . Os valores de resistência de união foram menores quando produzidos num modelo cavitário e dependentes do tipo de compósito e "camada elástica" formada. A associação do compósito Z250 às "camadas elásticas" SB+SBMP, SB+PLF, SB+FF e SB(3c) e a associação do compósito SureFil a SB+PLF foram capazes de produzir MRU, no modelo cavitário, semelhantes estatisticamente àquelas desenvolvidas quando o compósito foi submetido à "contração efetiva". Conclui-se que a utilização de compósitos de baixa viscosidade e de camadas espessas de adesivo, como camada intermediária, pode funcionar como uma zona de absorção de tensões, preservando a união e promovendo aumento dos valores de resistência da união dentina/compósito em cavidades Classe I / Abstract: T he aim of this in vitro study was to assess the effect of different { resin composites and elastic layers on resin/dentin bond strength on " the buccal wall of Class I cavities. Ninety-six caries-free third molars were ground flat to expose the dentin surface under running water. Class I cavities (C-factor = 4.5, 4 mm mesial-distal, 3 mm buccal-lingual and 3 mm deep) were prepared in occlusal dentin and then randomly distributed into eighteen experimental groups by changing of three resin composites (SureFil, Filtek Z250 e Z100) and six elastic layers: 1SB(lc), Single Bond adhesive was applied of according manufacturer instruction's; 2- SB(3c), Single Bond adhesive received two additional coats; 3- SB+SBMP, Single Bond adhesive received two additional coats of Scotchbond Multi-Purpose adhesive; 4- OS(lc) Optibond Solo Plus adhesive was applied of according manufacturer instruction's; 5- SB+PLF, Single Bond adhesive received intermediate layer of low-viscosity composite Protect Liner F; and 6- SB+FF, Single Bond adhesive received intermediate layer of low-viscosity composite Filtek Flow. Each additional adhesive layer was individually light-cured. After created elastic layer, the composite was placed using a bulk-filling increment. The teeth were prepared for microtensile bond strength (IlTBS) with the bonded beams (of approximately 0.8 mm2) obtained from the buccal wall of the cavity. The samples were stored in distilled water at 37°C for 24 h prior to IlTBS Testing. For each elastic layer, one additional group was accomplished to measure the bond strengths on corresponding buccal flat surface by cutting away the rest of the cavity walls (C-factor = 0.22). The data were analyzed using one and two-way ANOV A, Tukey Test for multiple comparisons and Dunnett's Test, at a significance levei of 0.05. The characteristic strength (TBSO) in this study varied about 11.2-29.6 Mpa. Statistical significant differences were verified among the resin composites (p = 0.0079) and among the various elastic layers in both cavity bonding groups (p< 0.0001) and flat bonding groups (p = 0.0095). The Z250 resin composite showed the higher TBS means, with statistical differences of the Zl00. The SLirefil groups exhibited comparable TBS means to others two composites. In the cavity bonding groups, the TBS values for Z250, Z100 and Surefil were respectively: SB+SBMP (27, 22.9, 20.4)a, SB+PLF (19.8, 21.3, 18.5)ab, SB+FF (21.3, 19, 15.4)bC, SB-3e (17.9, 16.4, 14.2)bc, OS-1e (15.9, 14.2, 16)bc and SB-1e (17, 14.8, 11.2)C. The mean bond strengths obtained in eavity bonding group were significantly lower than those of the flat bonding group, exeept when the Z250 resin eomposite was associate with SB+SBMP, SB+PLF, SB+FF and SB(3e) and the Surefil resin eomposite was associate with SB+PLF. This association provides the best bond strengths in eavity, similar to the bonding on a flat eavity. The TBS means are dependent of the eomposite and the various formed elastie layer. The use of a low-viseosity eomposite or multiple applieations of adhesive as intermediate layer ean provide a stress absorbing layer, whereby inereasing the resin/dentin bond strength in box-shaped eavities / Doutorado / Dentística / Doutor em Clínica Odontológica
|
97 |
Influencia da escovação mecanica sobre a infiltração marginal de restaurações de amalgama de prata associadas a agentes resinosos e condensadas com diferentes metodosBerger, Roberta da Silva Nunes 21 July 1999 (has links)
Orientador: Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T02:26:41Z (GMT). No. of bitstreams: 1
Berger_RobertadaSilvaNunes_M.pdf: 4696200 bytes, checksum: 020b7353feec458b48987963e3977e5d (MD5)
Previous issue date: 1999 / Resumo: o objetivo deste estudo foi avaliar a infiltração marginal de restaurações de amálgama de prata confeccionadas com diferentes métodos de condensação, associadas ou não a diversos agentes resinosos e submetidas ou não à escovação. Para isso utilizou-se 144 dentes molares e pré-molares, divididos em 18 grupos de 8 dentes cada, nos quais foram confeccionadas cavidades classe V (2 mm de profundidade x 3mm de extensão mésio-distal x 1,5 mm de extensão oc1uso-cervical) nas superfícies vestibulares. As cavidades foram restauradas com a liga encapsulada Duralloy (Degussa, SI A)
através de 3 maneiras: somente com amálgama de prata ( controle); amálgama associado ao sistema de união Scotchbond Multi-Uso Plus (3M); e amálgama associàdo ao Scotchbond Cimento Resinoso (3M). O amálgama foi condensado utilizando 3 técnicas: manual, mecânica e ultrassônica. Após restauradas e polidas, metade das amostras foram submetidas à escovação mecânica (30.000 ciclos) utilizando uma máquina de escovação Equilabor. Após, todas amostras foram termocicladas 500 vezes, sendo em seguida imersas em solução de azul de metileno a 2% por 4 horas. Os dentes foram seccionados para análise da infiltração e analisados numa lupa estereoscópica (63X). Foi utilizada também microscopia eletrônica de varredura para observação da margem dente-restauração. Os resultados foram analisados
estatisticamente, aplicando o teste exato de Fisher. De acordo com os resultados obtidos, conclui-se que de um modo geral as restaurações de amálgama associadas à agentes resinosos apresentaram menor nível de infiltração. Quando realizou-se o pFocedimento de escovação mecânica, nenhum grupo foi influenciado, com exceção do grupo restaurado com amálgama associado ao Scotchbond Multi-Uso Plus com condensação mecânica, que apresentou maior nível de infiltração marginal, quando escovado. As fotomicrografias eletrôRicas de varredura mostraram que nos grupos escovados mecanicamente houve formação de valamento na margem dente/restauração / Abstract: The object of this study was to evaluate the marginal leakage of amalgam restoration associated or not to resinous agents, when they are submitted to brushing using differents resinous agents and differents condensation methods. With this purpose, 144 molar and pre-molar teeth were used and divided into 18 groups of 8 teeth each. Class V cavities preparation (2mm of deep x 3mm of length x 1,5 mm of width) were performed on buccal surface. The cavities were filled with Duralloy capsuled silver alloy (Degussa, SI A) by following different ways: only silver amalgam (control); amalgam associated with SBMU Plus (3M) adhesive system and amalgam associated to the Scotchbond Resin Cement (3M). The amalgam was condensed using 3 differehts technics: manual, mechanic and ultrasonic. After restored and polished, half ofthe samples were submitted to the mechanic brushing (30.000 cycles) using a Equilabor machine and after thermocycled to 500 times, being also immersed into 2% metilene blue solution for microleakage analysis and examined in a stereoscopic loupe (63x). Scanning electronic microscopy was used to analyse the toothlrestoration margin. The results were statistically analysed applying Fisher exact test. According to the results obtained we can conclude that generally, the amalgam restoration associated to resinous agents showed the smaller leveI of microleakage. When the mechanic brushing procedure was performed, any group was influenced, except the group restored with amalgam associated to SBMU Plus with mecharnc condensation, which showed the greatest leveI of microleakage, when brushed. The scanning
electronic photomicrography showed that in groups mechanically brushed, noted a gap in the tooth/restoration margin / Mestrado / Materiais Dentarios / Mestre em Ciências
|
98 |
Efeito da quantidade de primer na adaptação marginal, nanoinfiltração e resistência à união de sistemas adesivos após envelhecimento termomecânico = Effects of primer amount on marginal adaptation, nano leakage and bond strength of adhesive systems after thermomechanical aging / Effects of primer amount on marginal adaptation, nano leakage and bond strength of adhesive systems after thermomechanical agingBarreto, Suelem Chasse, 1987- 26 August 2018 (has links)
Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-26T22:01:59Z (GMT). No. of bitstreams: 1
Barreto_SuelemChasse_M.pdf: 116094135 bytes, checksum: 14295d9814cd8a3d1872c717dd154522 (MD5)
Previous issue date: 2015 / Resumo: O estudo teve como objetivo avaliar a influência da quantidade de primer usada na hibridização do substrato na resistência de união por microtração, nanoinfiltração e adaptação marginal em restaurações com sistemas adesivos e resina composta após envelhecimento termomecânico. Foram selecionados 48 molares hígidos que foram restaurados em uma cavidade tipo classe I pela técnica incremental com sistema adesivo convencional de três passos (Adper Scotchbond Multiuso - 3M ESPE) e sistema autocondicionante de dois passos (Clearfill SE bond - Kuraray). Para o sistema adesivo convencional foi realizado o condicionamento ácido total e para o sistema adesivo autocondicionante, o condicionamento ácido foi seletivo no ângulo cavosuperficial em esmalte. Em seguida, os dentes foram alocados aleatoriamente em 6 grupos resultantes da interação da aplicação de uma quantidade padronizada de 1, 2 ou 3 gotas de primer e sistema adesivo. Todos os dentes foram restaurados com a resina composta microhíbrida Charisma (Heraeus Kulzer). Após o polimento das restaurações, estas foram moldadas com polivinilsiloxano e as réplicas foram obtidas em resina epóxica. Em seguida, os espécimes foram levados à máquina de ciclagem termomecânica ERIOS 37000 (ERIOS, São Paulo, Brasil), na qual realizou-se o envelhecimento artificial da restauração através de 200.000 ciclos com carga de 86 N a uma frequência de 2 Hz associados a ciclos térmicos com a temperatura variando entre 5ºC, 37ºC e 55ºC, a cada 30 segundos. Terminado o envelhecimento, obteve-se novas réplicas que foram levadas ao microscópio eletrônico de varredura (MEV) para análise de fendas em comparação com as imagens iniciais. Em seguida os dentes foram submetidos ao ensaio mecânico de resistência de união à microtração por meio de palitos obtidos da interface vestibular, e, posteriormente, avaliou-se o padrão de fratura usando MEV. Para análise de nanoinfiltração, oito palitos de cada grupo foram separados, aleatoriamente, para se avaliar a infiltração de íons de nitrato de prata em MEV. Após o teste termomecânico, os dados foram submetidos à Análise de Variância dois fatores e teste de Tukey com ?= 0,05. Quando o excesso de primer na camada adesiva foi avaliado, o sistema adesivo convencional de três passos apresentou melhores resultados de resistência à união quando comparado ao sistema adesivo autocondicionante de dois passos (?= 0,0015). A quantidade de gotas influenciou a resistência de união à microtração (?= 0,0057). A nanoinfiltração foi maior quando se utilizou maior quantidade de primer e o envelhecimento termomecânico aumentou a formação de fendas marginais. O uso de primer em excesso não é recomendado pois reduz a resistência de união à microtração e forma uma camada híbrida de baixa qualidade / Abstract: This study aimed to evaluate the effects of the amount of primer used in the tooth substrate hybridization on the microtensile bond strength (?TBs), nanoleakage and marginal sealing in dental restorations with adhesive systems and composite resin after thermomechanical aging. A total of 48 human molars were restored class I cavities with incremental technique with a three-step etchand- rinse adhesive system (Adper Scotchbond Multipurpose, 3M ESPE) and twostep self-etching adhesive system (Clearfill SE Bond, Kuraray), For three-step etch-and-rinse adhesive system used total acid etching and for the two-step selfetching system adhesive only enamel cavosurface was acid etching. Then, the teeth were aleatory alocated in 6 groups resulted the interaction between the factors application of standard quantity of primer (1, 2 or 3 drops) and adhesive systems. Afterward a standardized amount of each primer was applied (1, 2, or 3 drops of primer). All teeth were restored with microhybrid composite resin (Charisma, Heraeus Kulzer). After polishing of restorations, they were molded with polyvinylsiloxane and replicas were obtained with epoxy resin. Then the specimens were taken to thermomechanical cycling machine (model 37000 ERIOS), which carried out the artificial aging of restoration through 200,000 cycles with 86 N load at a frequency of 2 Hz associated with thermal cycling and temperature ranging from 5, 37and 55°C every 30 seconds. After aging, new replicas were obtained and images were taken by scanning electron microscope (SEM) to analyze gaps. These images were compared to the initial ones. Then the teeth were subjected to ?TBs testing through beams obtained from buccal interface, and fracture pattern was evaluated using SEM. For nanoleakage analysis, eight beams of each group were randomly separated to assess infiltration with silver nitrate ions and subsequently evaluated by SEM. After the mechanical test, the data were subjected to statistical analysis using two-way Analysis of Variance and Tukey's test (? = 0.05). When primer excess was evaluated at the adhesive layer, the three-step etch-and-rinse adhesive system showed higher bond strength results x when compared to two-step self-etching adhesive system (? = 0.0015). The primer excess influenced ?TBS (? = 0.0057). Nanoleakage was higher when using larger amount of primer was used. Thermomechanical aging increased the formation of marginal gaps. The use of primer in excess is not recommended, because the excess reduces the ?TBs and creates an unsatisfactory hybrid layer on tooth substrate / Mestrado / Dentística / Mestra em Clínica Odontológica
|
99 |
Influência da fonte de luz fotoativadora na resistência de união e na micromorfologia da interface adesiva de restaurações de resina composta - Um estudo 'in vitro' com microscopia de fluorescência / Influence of light-curing sources on bond strength and on interfacial micromorphology of resin composite restorations a fluorescence microscopy studyD'Alpino, Paulo Henrique Perlatti 07 April 2005 (has links)
Propôs-se avaliar a influência de diferentes fontes de luz fotoativadoras na micromorfologia e na resistência de união adesiva de restaurações de resina composta. Selecionaram-se terceiros molares hígidos que receberam preparos cavitários classe I (6,0 mm x 4,5 mm; 2,5 mm profundidade). A resina composta (Filtek Z250 - RC) foi inserida em incremento único após a aplicação e polimerização do sistema adesivo (Adper Single Bond - SB). Os materiais restauradores foram fotoativados com os seguintes aparelhos: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight 2 (LED: 750 mW/cm2) e Arc Light IIM (PAC: 2.130 mW/cm2). Nove grupos experimentais foram avaliados de acordo com as combinações de fonte de luz para fotoativar SB/RC: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Para a análise da micromorfologia foi utilizada microscopia de fluorescência (Laser de Fóton Duplo), sendo que um corante fluorescente vermelho (Rodamina B) foi adicionado ao sistema adesivo. Além disso, utilizou-se uma solução de corante fluorescente verde (Dextran- Fluoresceína), que foi aplicada na câmara pulpar durante 4 horas, para que se difundisse em direção à interface. Os dentes foram então lavados, incluídos, seccionados e analisados microscopicamente. Os parâmetros analisados foram: espessura da camada de adesivo, espessura e qualidade da camada híbrida, micropermeabilidade, qualidade e habilidade de selamento dos tags de resina e, ainda, localização e extensão de fendas. Para o teste de resistência adesiva, os dentes foram restaurados, de acordo com as combinações de fonte de luz, e armazenados por 24 horas a 37 °C. Em seguida os dentes foram seccionados e submetidos ao teste de microtração. Realizou-se ainda a análise dos parâmetros de cinética de conversão de monômeros (conversão total, taxa máxima de conversão, conversão na máxima taxa, tempo em que ocorreu a máxima taxa e relação conversão na máxima taxa/conversão total) em um espectrofotômetro de raios infravermelho, ao qual foram aplicados os mesmos materiais restauradores que foram polimerizados com as diferentes fontes de luz. Para as avaliações qualitativas foi realizado o teste estatístico Kruskal-Wallis e o teste de Dunnet para comparações múltiplas (α = 0,05). Para as avaliações quantitativas foi realizada análise de variância e teste de Tukey para comparações múltiplas (α = 0,05). Da análise dos resultados, observou-se que as fontes de luz utilizadas influenciaram nos parâmetros de cinética de conversão de monômeros. De forma geral, ocorreu uma relação inversa entre a conversão total e a densidade de potência quando se polimerizou o sistema adesivo. Na resina composta base, houve uma relação direta. Para ambos os materiais houve uma maior taxa máxima de conversão, em um menor tempo, proporcional à densidade de potência dos aparelhos. Quanto aos parâmetros de micromorfologia, não se observou diferença siginificante entre os grupos experimentais em relação à espessura e qualidade de camada híbrida. Em relação à espessura da camada de adesivo, observaram-se maiores espessuras quando o sistema adesivo foi polimerizado com o PAC. Para a micropermeabilidade, também não se observou diferença entre os grupos. Também, não se observou diferença siginificante em relação à qualidade e habilidade de selamento dos tags de resina. Em relação à presença de fendas, quando o PAC polimerizou o sistema adesivo, menores porcentagens de piores escores e menores extensões de fendas foram observadas. A combinação PAC/QTH apresentou valores significantemente maiores de resistência adesiva e LED/QTH, as menores. A espessura da camada de adesivo, localização de fendas e resistência adesiva foram significantemente influenciados pela fonte de luz que polimerizou o sistema adesivo, sendo que, quando o PAC foi utilizado, melhores resultados foram observados. As combinações de mesma fonte de luz apresentaram, de forma geral, resultados similares. As diferentes fontes de luz fotoativadoras influenciam na resistência de união adesiva e em alguns parâmetros da micromorfologia da interface de restaurações de resina composta. / The purpose of the present in vitro study was to evaluate the effect of different light-curing sources on interfacial micromorphology and on bond strength of resin composite restorations. Class I preparations (6.0 mm long, 4.5 mm wide, 2.5 mm deep) were made in extracted human third molars, after abrading cusps, following university approved HAC guidelines. Restorations were placed in bulk, using a dentin bonding agent (DBA) / resin composite (RC): Adper Single Bond / Filtek Z250. Restoratives were light-cured as follows: XL 3000 (QTH: 540 mW/cm2); Elipar FreeLight2 (LED: 750 mW/cm2); Arc Light II (PAC: 2,130 mW/cm2). Nine experimental groups were developed from the different light combinations with respect to curing the DBA/COMP: QTH/QTH; QTH/LED; QTH/PAC; LED/LED; LED/QTH; LED/PAC; PAC/PAC; PAC/QTH; PAC/LED. Fluorescing agent (Rhodamine B) was added to the DBA, highlighting the bonded interface and surrounding structures. A different colored dye (FTIC-Dextran) was placed in the pulp chamber for 3 hours, allowing time to diffuse toward the different-colored interface. The teeth were then embedded, sectioned, and microscopically analyzed using fluorescence microscopy (Two-Photon Laser) at 40x magnification. Micromorphology quantitative and qualitative evaluations were: quality and thickness of hybrid layer; micropermeability test, adhesive layer thickness; quality and sealing ability of resin tags; location and extension of gaps. For bond strength test, the same experimental groups were obtained. After restorative procedures, the teeth were stored in distilled water for 24 h at 37 °C. After this time period, resin layers were added to the restoration surface (providing same dentin/resin length), and then sectioned and subjected to microtensile test in a universal testing machine. Kinetics conversion parameters were also evaluated in an FT-IR spectrophotometer (total conversion, maximum rate of cure, time when maximum rate occurred, conversion at maximum rate, conversion at maximum rate/ total conversion ratio). The same restorative materials were applied to the ATR device, attached to the spectrophotometer, and then polymerized according to manufacturers instructions. Data was statistically analyzed as mentioned below. Statistical analyses revealed that different light sources influenced the kinetics conversion (one-way ANOVA, p< 0,05). It was found an inverse relation between power density and monomer conversion when polymerizing DBA. For resin composite (bottom), there was a positive relation between power density and total conversion. High intensity, broad banded PAC light produced higher maximum rate of cure (in %/s), in shorter times. In terms of micromorphology, no significant difference was found in terms of quality and thickness of hybrid layer (two-way ANOVA, p> 0.05). No significant difference was noted for in quality and in sealing ability of tags (Kruskal Wallis, p> 0.05). QTH/QTH presented higher percentages of best scores for both parameters. Adhesive layers were found to be significantly thicker when PAC light was used to polymerize DBA. Even thought it was also found no significance in micropermeability scores (Kruskal Wallis, p> 0.05), it was found higher percentage of best scores for control QTH/QTH. Photo-polymerizing DBA using PAC produced lower incidence of gap formation, irrespective of RC curing source. Combination PAC/QTH presented significantly higher bond strength and LED/QTH, the lower (two-way ANOVA, Dunnets pos-hoc test, p< 0.05). Part of interfacial micromorphology parameters and bond strength were more dependent on the photo-polymerization source used for dentin-bonding agent than for resin composite. Photo- polymerizing DBA using PAC produced best results for adhesive thickness, gap location, and bond strength. Although QTH/QTH, LED/LED, and PAC/PAC combinations produced similar general results, it was found inherent characteristics when analysing tested parameters. Different light curing units influence bond strength and some parameters of micromorphology.
|
100 |
Estudo 'In Vitro' da Infiltração Marginal em Dentes Submetidos a Diferentes Técnicas de Clareamento e Restaurados com um Sistema Adesivo/Resina Composta.Souza, Patrícia de Almeida Rodrigues da Silva e 05 August 1999 (has links)
Foi avaliado o efeito do clareamento na infiltração marginal de dentes restaurados com o sistema adesivo Scotchbond Multi-uso Plus e resina composta Z-100. Sessenta pré-molares foram divididos em 6 grupos: grupo I, técnica imediata, uma bolinha de algodão saturada em peróxido de hidrogênio a 30% foi colocada no interior da câmara coronária e na superfície vestibular dos dentes e aquecida a uma temperatura de 42ºC por 3 períodos de 15 minutos, num total de três sessões semanais; grupo II, técnica mediata, era selado um curativo na câmara coronária de peróxido de hidrogênio a 30% mais perborato de sódio por 21 dias, e no intervalo de sete dias renovado; grupo III, associação das duas técnicas acima descritas; grupo IV, técnica caseira com aplicação de peróxido de carbamida a 10% por três horas diárias durante 21 dias; grupo V, associação da técnica caseira mais mediata; grupo VI foi o controle que não foi submetido ao tratamento clareador. Após, todos os grupos permaneceram com um curativo de hidróxido de cálcio por dez dias, para em seguida serem restaurados, termociclados e imersos em fucsina básica à 0,5% por 24 horas. A medida da penetração do corante pela interface dente restauração foi realizada através do programa ImageTool. As médias obtidas foram de 3,09; 1,83; 2,11; 2,36; 1,60 e 2,20(mm) para os grupos de I ao VI, respectivamente. Nenhum grupo impediu a infiltração marginal; a técnica imediata mostrou os maiores valores de infiltração, diferente estatísticamente dos grupos II e V; nos grupos onde aplicou-se o perborato de sódio houve uma tendência a menor infiltração. Não houve diferença entre as demais técnicas e estas em relação ao grupo controle. / The effects of different bleaching techniques on the dental structures were assessed using microleakage tests. Sixty pre molars were used in this study according to the following procedures: group I a cotton pellet saturated with 30% hydrogen peroxide was placed in the pulp chamber and on the buccal surface and heated to 42 oC three times of fifteen minutes each. This procedures was repeated three times. Group II - In the pulp chamber was inserted a paste of sodium perborate and 30% hydrogen peroxide for 21 days. Every seven days the material was renewed. Group III The two techniques described above were associated. Group IV 10% carbamide peroxide was applied on the external surfaces three hours per day during 21 days (home bleaching) Group V Association of group II and IV techniques. Group VI- No treatments were performed in this group (Control). A CaOH2 paste was sealed in the pulp chamber for 10 days, the teeth were restored with Scotchbond Multi-uso Plus/Z-100, thermocycled and immersed in basic fucsin. The die penetration was determined in mm using the software Imagetool. The means (mm) of die penetration for groups I to VI were: 3,09; 1,83; 2,11; 2,36; 1,60; and 2,20. The microleakage occurred regardless the bleaching procedures. Group I technique exhibited higher die penetration when compared to groups II and V. The groups where sodium perborate was applied there was a trend of less die penetration.
|