The work is focused on the possible use of secondary raw materials of the energy industry in the construction industry, particularly in concrete applications, where as the main raw material of the binder composition are used solid fluidized bed combustion residues - filter and ground. The aim of this work is to prepare concrete or concretes based on solid residues from fluidized bed combustion, that will fulfill or at least approximately approach by their parameters to commonly used concretes based on portland cement. The experimental part is divided into several chapters, at first the results of analyzes of feedstock and solid residues from fluidized bed combustion, portland cement and calcium hydroxide. Other chapters describe proposals for alternative binders, concrete, characterization and testing. Mainly were observed changing properties of the prepared concretes by changing the ratio of binders and aggregates. In tests were evaluated mainly mechanical properties and phase composition.

Bei den Forschungsaktivitäten wird von aktuellen Fragestellungen der Baustofftechnologie ausgegangen, wobei die Lösung akuter Probleme der Baupraxis und die Schaffung von soliden theoretischen Grundlagen in gleichem Maße angestrebt werden. Die Forschung wird hierbei vor allem durch interdisziplinäres Arbeiten geprägt. Zu den aktuellen Forschungsschwerpunkten zählen insbesondere: Entwicklung neuer zementbasierter Verbundwerkstoffe sowie von Verfahren zu deren Herstellung mit besonderem Akzent auf Faserbetone (Hochduktiler Beton mit Kurzfasern, Beton mit textiler Bewehrung, Ultrahochfester Beton mit innerer Nachbehandlung, Selbstverdichtender Leichtbeton, Beton mit sehr hohem Verschleißwiderstand) Untersuchung der Kurz- und Langzeiteigenschaften von neuen und bestehenden Baustoffen auf mineralischer Basis (Beton, Mörtel, Mauerwerk); Erforschung der für das Materialverhalten maßgebenden Mechanismen sowie der Mittel zu deren gezielten Beeinflussung (Festigkeits-, Verformungs- und Bruchverhalten unter monotoner, zyklischer und stoßartiger Beanspruchung sowie Schwinden und Kriechen von Beton; Transport von korrosiven Medien unter Berücksichtigung der Rissbildung, Schädigungsmechanismen und Dauerhaftigkeit) Modellierung des Baustoffverhaltens; Ableitung von stoffgesetzlichen Beziehungen; numerische Simulation des Materialverhaltens in unterschiedlichen Stadien seines "Lebens" (Herstellung, Verarbeitung, Erhärtung, mechanische Beanspruchung, Exposition von korrosiven Medien etc.)

The content of this thesis is the design of street furniture using concrete. The work includes a brief summary of marketing, analyzing current trends in design of street furniture and analysis used technical solutions. The main part is devoted to the design process, resulting in the shape of street furniture while respecting the structural and ergonomic requirements in relation to people who use the furniture.

The content of this thesis is the design of street furniture using concrete. The work includes a brief summary of marketing, analyzing current trends in design of street furniture and analysis used technical solutions. The main part is devoted to the design process, resulting in the shape of street furniture while respecting the structural and ergonomic requirements in relation to people who use the furniture.

Bei den Forschungsaktivitäten wird von aktuellen Fragestellungen der Baustofftechnologie ausgegangen, wobei die Lösung akuter Probleme der Baupraxis und die Schaffung von soliden theoretischen Grundlagen in gleichem Maße angestrebt werden. Die Forschung wird hierbei vor allem durch interdisziplinäres Arbeiten geprägt. Zu den aktuellen Forschungsschwerpunkten zählen insbesondere: Entwicklung neuer zementbasierter Verbundwerkstoffe sowie von Verfahren zu deren Herstellung mit besonderem Akzent auf Faserbetone (Hochduktiler Beton mit Kurzfasern, Beton mit textiler Bewehrung, Ultrahochfester Beton mit innerer Nachbehandlung, Selbstverdichtender Leichtbeton, Beton mit sehr hohem Verschleißwiderstand) Untersuchung der Kurz- und Langzeiteigenschaften von neuen und bestehenden Baustoffen auf mineralischer Basis (Beton, Mörtel, Mauerwerk); Erforschung der für das Materialverhalten maßgebenden Mechanismen sowie der Mittel zu deren gezielten Beeinflussung (Festigkeits-, Verformungs- und Bruchverhalten unter monotoner, zyklischer und stoßartiger Beanspruchung sowie Schwinden und Kriechen von Beton; Transport von korrosiven Medien unter Berücksichtigung der Rissbildung, Schädigungsmechanismen und Dauerhaftigkeit) Modellierung des Baustoffverhaltens; Ableitung von stoffgesetzlichen Beziehungen; numerische Simulation des Materialverhaltens in unterschiedlichen Stadien seines "Lebens" (Herstellung, Verarbeitung, Erhärtung, mechanische Beanspruchung, Exposition von korrosiven Medien etc.)

Anenský Court has more historical layers. When looking at the half-collapsed brick arch and remnants of walls, we can feel the nostalgia. Concrete silos remind time not so long ago. Today, all overgrown with bushes. What man left, takes nature. Nothing remains constant. As a former farm yard, which currently lacks a feature? The lives of the former inhabitants of Justice are long odžity a nostalgic return to the past times do not provide a basis. Presence is rapidly becoming a thing of the past and nothing remains constant. Ruins ANNAHOF slowly disintegrate, disappear one historic layer. The new layer but has already begun to create. Future is quickly becoming the present and nothing remains constant. Constant change is a fundamental characteristic ANNAHOF, as well as any other place in the world. It gives us the challenge to innovation, as opposed to nostalgia. Adaptation to changing environmental conditions is a prerequisite for survival. In the past, human survival depended entirely on natural conditions - people turned to God to ask for a good harvest. Today, we can predict the weather and the soil fertility is largely influenced. Our survival still depends on the same natural conditions. Instead we wayside chapels and build weather stations and invest in research. In ANNAHOF it decided to propose a station for research into climate change with a visitor's center, which could be felt through microclimates global warming "on your own". The whole house is basically built around four outdoor microclimates., In which it can be accessed. The shape of the building and its position in the field is therefore directly result in the formation of microclimates. The structural system is a wall, even using concrete material. I chose it for its possibilities of shaping and visual quality. Quantity retaining walls, landscaping required for the creation of microclimates is used as efficiently as possible at the same time as the walls of the building. Of the existing structures is to use one concrete silo, and a support pole for measuring towers. Lattice structure of the mast is secured with ropes anchored to the concrete silo. On measuring tower are located automatic measuring devices. The main area of my proposal is a gallery exhibition space. There should be a visitor center acquainted with the problems of climate change and from this space ramps can reach all four outdoor microclimates. The gallery is lit by a skylight above the one hand and also tracked through the window, which runs almost around the perimeter, and that desert light through the supporting structure of steel truss grid in the interior. Operationally in the building blends function research / workplace for scientists and their background and / public / gallery microclimates and facilities for visitors. Both functions can then serve multipurpose hall. The proposal also includes necessary facilities for maintenance of outdoor spaces and buildings, as well as an apartment manager. Překladač Google pro firmy:Translator ToolkitPřekladač webových stránekNástroj pro hledán

Thesis theme were nanomaterials and its implementation to cementitious materials. Theoretical part has deal with description of carbon nanotubes types, their properties, production, ways of dispergation, nanotoxicity and CNT’s influence on silicate composites characteristics. Experimental part was divided to 5 stages. The first stages were focused on choosing appropriate carbon nanotubes and surfactants. In the next stage settings of US homogenizator were determinate (amplitude, US energy dosage, time). The part of US homogenizator setting process was observing influence of liquid environment characteristics (especially pH) on surface tension and particle distribution and influence of US energy on CNT walls damages through TEM. After dispergation parameters optimalization cement pastes were prepared and hydration temperature, hydration heat and viscosity were observed. Then testing specimens from cement mortar were prepared and tested form strength characteristics. Last stage was concrete production and their examination: compressive strength, flexural strength, static modulus of elasticity, dynamic modulus of elasticity, tensile splitting strength, depth of penetration of water under pressure, resistance of cement concrete surface to water and defrosting chemicals and determination of frost resistance of concrete. Samples with CNT addition had better strength characteristics and better resistance of penetration of water under pressure, water and defrosting chemicals resistance and frost resistance. Result of thesis is comprehensive study of CNT dispersion production and implementation CNT dispersion to concrete including testing specific concrete characteristics.

Die Querkrafttragfähigkeit eines Bauteils kann durch verschiedene Maßnahmen gesteigert werden. Zu den weltweit anerkannten Verfahren gehört das oberflächige Aufkleben von Bewehrungen aus Stahl oder Faserverbundkunststoffen. Der textilbewehrte Feinbeton hingegen ist eine noch weitgehend unbekannte Alternative. Es fehlen ebenso systematische Untersuchungen zum Tragverhalten einer solchen Querkraftverstärkung wie geeignete Bemessungsmodelle. Ziel der vorliegenden Arbeit war es, die Möglichkeiten einer textilbewehrten Querkraftverstärkung zu analysieren. An Stahlbetonbalken unterschiedlicher Querschnittsgeometrie wurden experimentelle Untersuchungen durchgeführt, die Aufschluss über die Wirkung der Verstärkung sowie typische Versagenszustände geben. Die für die Querkrafttragfähigkeit entscheidenden Verformungen des Steges wurden durch photogrammetrische Messungen erfasst. Der Vergleich der verstärkten und unverstärkten Probekörper verdeutlicht signifikante Unterschiede. Bei den verstärkten Probekörpern ist die Stauchung des gemittelten Hauptdehnungszustandes steiler geneigt als bei den unverstärkten Probekörpern. Die steilere Neigung der Hauptstauchung, aufgrund der aufgebrachten Verstärkung, hat nach der rechnerischen Tragfähigkeit des Fachwerkmodells zur Folge, dass weniger Lasten über die Stahlbügelbewehrung abgetragen werden können. Die so fehlende Tragfähigkeit gegenüber dem unverstärkten Bauteil muss die Verstärkungsschicht zunächst ausgleichen, bevor eine Traglaststeigerung möglich ist. Als zweite wesentliche Wirkung begrenzt die textile Bewehrung die Breite der auftretenden Schubrisse wie anhand der gemessenen Rissbreiten nachgewiesen werden konnte. Die Verstärkung verzögert auftretende Schubrisse und begrenzt deren Breite und Ausdehnung. Ein Versagen der Biegedruckzone durch Schubdruckbruch tritt so erst bei deutlich höheren Lasten ein als es bei unverstärkten Stahlbetonbauteilen der Fall ist. Nach dem herkömmlichen Fachwerkmodell der Stahlbügelbewehrung sind die Stegbewehrungen eines Bauteils in der Biegedruckzone zu verankern. Externe Querkraftverstärkungen können aber nur selten oder mit hohem Aufwand bis zur Höhe der Biegedruckzone geführt werden. Meist behindern anschließende Querschnittsteile die Erreichbarkeit zur Druckzone. Für die experimentellen Untersuchungen wurden die Probekörper mit einer U-förmigen Verstärkung außerhalb der rechnerischen Biegedruckzone versehen. Die geprüften Tragfähigkeiten lagen dennoch deutlich über der Tragfähigkeit der unverstärkten Referenz. Eine Verankerung der Verstärkung am Steg des Bauteils scheint demnach möglich. Das Kräftegleichgewicht einer solchen Verankerung wurde mit einem neu entwickelten Stabwerkmodell nachgewiesen. Die Eignung des Modells zur Berechnung der Tragfähigkeit der Verstärkung wurde durch Nachrechnung der eigenen Versuche geprüft. Zusätzliche konstruktive Maßnahmen zur Verankerung der Verstärkung wurden an separaten Verbundprobekörpern untersucht. Es wurden verschiedene Verankerungsmittel geprüft, die durch Querdruck die Tragfähigkeit der Verbundfuge von Alt- und Feinbeton erhöhen. Die besten Ergebnisse erreichten Verankerungen mit vorgespannten Ankern. Die Steigerung der Verbundtragfähigkeit ist allerdings gering, da die notwendigen Bohrungen für die Anker die wirksame Fläche der textilen Bewehrung schwächen. / Shear resistance of structural members can be increased by different measures. So far only reinforcements from steel or fibre-reinforced plastic pasted on the surface have been acknowledged worldwide. Textile reinforced fine grained concrete, however, is still mostly an unknown option. Systematic research into the load bearing behaviour of this kind of shear strengthening as well as qualified design rules are missing. It is the aim of this thesis to analyse the possibilities of textile reinforced shear strengthening. Experimental investigations on RC beams with different cross sectional geometries provided information about the strengthening effect as well as common failure modes. The web deformations, which are crucial for the shear resistance, were recorded by photogrammetric measurements. A comparison of strengthened and unstrengthened specimen demonstrates significant differences. In case of the strengthened sample, the compressive strain of the averaged principle strain condition has a steeper inclination than in case of the unstrengthened specimen. This steeper inclination ensues from the applied strengthening. According to the calculated load-bearing capacity of the truss model, the steeper inclination results in less loads being removed by the steel stirrup reinforcement. Compared to the unstrengthened structural member, this lack in the load-bearing capacity has to be evened out by the strengthening layer before an increase in the load carrying capacity is possible. Secondly, the textile reinforcement limits the width of the occurring shear cracks. This could be proven by measuring the crack-width. The strengthening delays occurring shear cracks and restricts their widths and extension. Consequently, failure of the flexural compression zone induced by shear cracks only occurs under significantly higher loads than in unstrengthened RC members. In the traditional truss model of the steel stirrup reinforcement, the web reinforcements of a structural member have to be anchored in the flexural compression zone. However, external shear strengthening can be pulled up to the height of the flexural compression zone only rarely or with great effort. Often connected parts of the cross section prevent access to the compression zone. For the purpose of the experimental analysis, the specimens were fit with a U-shaped strengthening layer outside the calculated flexural compression zone. Nevertheless, the measured load-bearing capacities were distinctly higher than the load-bearing capacity of the unstrengthened reference beam. Consequently, anchoring the strengthening at the specimen’s web appears to be possible. The force balance of such an anchorage could be proved with the help of a newly developed strut-and-tie-model. The applicability of the model for calculating the load bearing capacity of the strengthening was checked by recalculating the corresponding test results. Additional structural measures for anchoring the strengthening were tested on separate bond specimens. Furthermore, various anchorage materials which increase the load carrying capacity of the interface between old and fine grained concrete through transverse pressure were tested. The best results could be achieved with pre-stressed anchorages. However, the resulting load-bearing capacity’s increase was only slight because the drill holes required for the anchors reduce the effective area of the textile reinforcement.

Die vorliegende Arbeit befasst sich mit der Verbundverankerung des neuen Verstärkungsmaterials textilbewehrter Beton für Stahlbetonbauteile. Der Detailpunkt der Verankerung mit den Mechanis-men der Kraftübertragung von der textilbewehrten Verstärkungsschicht in den Altbeton wurde auf experimentellem Weg an unterschiedlichen Probekörperformen untersucht. Dazu wurden verschie-dene Haftzug-, Filamentgarnauszug- sowie Schubversuche durchgeführt. Nach der Klärung der grundlegenden Phänomene beim Verbundbruchverhalten von Verstärkungs-schichten wurden zugehörige Versagenskriterien näher beleuchtet. Ein mögliches Versagen des inneren Verbundes wurde durch zusätzlich in das Versuchsprogramm aufgenommene Filamentgar-nauszugsversuche untersucht. Für die Verankerung sind zwei Versagensebenen zu berücksichtigen, die eine getrennte Betrachtung erfordern: der Altbetonuntergrund und die Ebene der textilen Be-wehrung. Mit Hilfe experimenteller Haftzuguntersuchungen wurde ein breit gefächertes Spektrum möglicher Einflussparameter auf die Tragfähigkeit des Verbundes in der Ebene der textilen Bewehrung unter-sucht. Den einzelnen Einflussfaktoren kommt dabei eine unterschiedliche Bedeutung zu. Den aus-schlaggebenden Einfluss auf die Tragfähigkeit des Haftverbundes in der Ebene der textilen Bewehrung liefert die textile Bewehrung selbst. Es wurde ein geeignetes Verfahren zur Ermittlung eines wirksamen Flächenanteiles der textilen Bewehrungsstrukturen entwickelt, welches die Grund-lage für die weiterführenden Betrachtungen zum Verbundversagen durch Delamination in der Ebe-ne der textilen Bewehrung bildet. Das Verbundtragverhalten unter Schubbeanspruchung bildet den Kern der vorliegenden Arbeit. Spezielle Eigenheiten des textilbewehrten Betons werden aufgezeigt und Lösungsvorschläge erar-beitet. Da sich das Verhalten von Verstärkungsschichten aus textilbewehrtem Feinbeton beträcht-lich von bekannten Klebeverbindungen unterscheidet, sind hier völlig neue Wege zu beschreiten. In Zusammenarbeit mit dem Institut für Photogrammetrie und Fernerkundung wurde ein neues, riss-bildorientiertes Messverfahren entwickelt. Anhand eines Beispielversuchs wird diese neu entwi-ckelte Methode vorgestellt und verbleibende Problempunkte diskutiert. Die Ergebnisse dieser Messungen haben gezeigt, dass es mit dem derzeitigen Kenntnisstand nicht möglich ist, für das Verstärkungsmaterial Textilbeton eine Schubspannungs-Schlupf-Beziehung anzugeben. Nach An-sicht der Verfasserin ist die Verwendung einer solchen Modellvorstellung nur für Verstärkungsma-terialien mit linear-elastischem Materialverhalten geeignet. In der vorliegenden Arbeit werden einige alternative Modellvorschläge für die Beschreibung des Verbundverhaltens angegeben. Separate Modellvorschläge für die Verbundtragfähigkeit unter Haft-zugbeanspruchung und unter Schubbeanspruchung wurden zu einer Interaktion zusammengeführt. Diesem wurden weitere alternative Modellvorschläge wie z. B. die Betrachtung als Stabwerk mit veränderlicher Druckstrebenneigung gegenübergestellt.

Die Querkrafttragfähigkeit eines Bauteils kann durch verschiedene Maßnahmen gesteigert werden. Zu den weltweit anerkannten Verfahren gehört das oberflächige Aufkleben von Bewehrungen aus Stahl oder Faserverbundkunststoffen. Der textilbewehrte Feinbeton hingegen ist eine noch weitgehend unbekannte Alternative. Es fehlen ebenso systematische Untersuchungen zum Tragverhalten einer solchen Querkraftverstärkung wie geeignete Bemessungsmodelle. Ziel der vorliegenden Arbeit war es, die Möglichkeiten einer textilbewehrten Querkraftverstärkung zu analysieren. An Stahlbetonbalken unterschiedlicher Querschnittsgeometrie wurden experimentelle Untersuchungen durchgeführt, die Aufschluss über die Wirkung der Verstärkung sowie typische Versagenszustände geben. Die für die Querkrafttragfähigkeit entscheidenden Verformungen des Steges wurden durch photogrammetrische Messungen erfasst. Der Vergleich der verstärkten und unverstärkten Probekörper verdeutlicht signifikante Unterschiede. Bei den verstärkten Probekörpern ist die Stauchung des gemittelten Hauptdehnungszustandes steiler geneigt als bei den unverstärkten Probekörpern. Die steilere Neigung der Hauptstauchung, aufgrund der aufgebrachten Verstärkung, hat nach der rechnerischen Tragfähigkeit des Fachwerkmodells zur Folge, dass weniger Lasten über die Stahlbügelbewehrung abgetragen werden können. Die so fehlende Tragfähigkeit gegenüber dem unverstärkten Bauteil muss die Verstärkungsschicht zunächst ausgleichen, bevor eine Traglaststeigerung möglich ist. Als zweite wesentliche Wirkung begrenzt die textile Bewehrung die Breite der auftretenden Schubrisse wie anhand der gemessenen Rissbreiten nachgewiesen werden konnte. Die Verstärkung verzögert auftretende Schubrisse und begrenzt deren Breite und Ausdehnung. Ein Versagen der Biegedruckzone durch Schubdruckbruch tritt so erst bei deutlich höheren Lasten ein als es bei unverstärkten Stahlbetonbauteilen der Fall ist. Nach dem herkömmlichen Fachwerkmodell der Stahlbügelbewehrung sind die Stegbewehrungen eines Bauteils in der Biegedruckzone zu verankern. Externe Querkraftverstärkungen können aber nur selten oder mit hohem Aufwand bis zur Höhe der Biegedruckzone geführt werden. Meist behindern anschließende Querschnittsteile die Erreichbarkeit zur Druckzone. Für die experimentellen Untersuchungen wurden die Probekörper mit einer U-förmigen Verstärkung außerhalb der rechnerischen Biegedruckzone versehen. Die geprüften Tragfähigkeiten lagen dennoch deutlich über der Tragfähigkeit der unverstärkten Referenz. Eine Verankerung der Verstärkung am Steg des Bauteils scheint demnach möglich. Das Kräftegleichgewicht einer solchen Verankerung wurde mit einem neu entwickelten Stabwerkmodell nachgewiesen. Die Eignung des Modells zur Berechnung der Tragfähigkeit der Verstärkung wurde durch Nachrechnung der eigenen Versuche geprüft. Zusätzliche konstruktive Maßnahmen zur Verankerung der Verstärkung wurden an separaten Verbundprobekörpern untersucht. Es wurden verschiedene Verankerungsmittel geprüft, die durch Querdruck die Tragfähigkeit der Verbundfuge von Alt- und Feinbeton erhöhen. Die besten Ergebnisse erreichten Verankerungen mit vorgespannten Ankern. Die Steigerung der Verbundtragfähigkeit ist allerdings gering, da die notwendigen Bohrungen für die Anker die wirksame Fläche der textilen Bewehrung schwächen. / Shear resistance of structural members can be increased by different measures. So far only reinforcements from steel or fibre-reinforced plastic pasted on the surface have been acknowledged worldwide. Textile reinforced fine grained concrete, however, is still mostly an unknown option. Systematic research into the load bearing behaviour of this kind of shear strengthening as well as qualified design rules are missing. It is the aim of this thesis to analyse the possibilities of textile reinforced shear strengthening. Experimental investigations on RC beams with different cross sectional geometries provided information about the strengthening effect as well as common failure modes. The web deformations, which are crucial for the shear resistance, were recorded by photogrammetric measurements. A comparison of strengthened and unstrengthened specimen demonstrates significant differences. In case of the strengthened sample, the compressive strain of the averaged principle strain condition has a steeper inclination than in case of the unstrengthened specimen. This steeper inclination ensues from the applied strengthening. According to the calculated load-bearing capacity of the truss model, the steeper inclination results in less loads being removed by the steel stirrup reinforcement. Compared to the unstrengthened structural member, this lack in the load-bearing capacity has to be evened out by the strengthening layer before an increase in the load carrying capacity is possible. Secondly, the textile reinforcement limits the width of the occurring shear cracks. This could be proven by measuring the crack-width. The strengthening delays occurring shear cracks and restricts their widths and extension. Consequently, failure of the flexural compression zone induced by shear cracks only occurs under significantly higher loads than in unstrengthened RC members. In the traditional truss model of the steel stirrup reinforcement, the web reinforcements of a structural member have to be anchored in the flexural compression zone. However, external shear strengthening can be pulled up to the height of the flexural compression zone only rarely or with great effort. Often connected parts of the cross section prevent access to the compression zone. For the purpose of the experimental analysis, the specimens were fit with a U-shaped strengthening layer outside the calculated flexural compression zone. Nevertheless, the measured load-bearing capacities were distinctly higher than the load-bearing capacity of the unstrengthened reference beam. Consequently, anchoring the strengthening at the specimen’s web appears to be possible. The force balance of such an anchorage could be proved with the help of a newly developed strut-and-tie-model. The applicability of the model for calculating the load bearing capacity of the strengthening was checked by recalculating the corresponding test results. Additional structural measures for anchoring the strengthening were tested on separate bond specimens. Furthermore, various anchorage materials which increase the load carrying capacity of the interface between old and fine grained concrete through transverse pressure were tested. The best results could be achieved with pre-stressed anchorages. However, the resulting load-bearing capacity’s increase was only slight because the drill holes required for the anchors reduce the effective area of the textile reinforcement.