Made available in DSpace on 2014-07-29T15:12:47Z (GMT). No. of bitstreams: 1 dissertacao Leonardo Francois quimica.pdf: 194110 bytes, checksum: 750a31eb02f149c7536ac63de960592b (MD5) Previous issue date: 2008-11-27 / In this study PLGA copolymers were synthesized with molecular weight above 10 kDa through direct polycondensation of L-lactic acid and glycolic acid monomers. Catalysts based on sulfonated styrenedivinylbenzene copolymer (SC) containing or not Sn2+ íons adsorbed as SnCl2.H2O colloidal particles from neutral solution or [SnCl3]- complex anions from acid solution were prepared. All catalysts were evaluated by specific surface area and pore volume measurements, infrared spectroscopy, X-ray diffraction, atomic absorption spectrophotometry and ion exchange capacity. The obtained PLGA copolymers were characterized by infrared spectroscopy, X-ray diffraction and inherent viscosity measurements. Independent of pH solution of the adsorptions, it was observed that Sn2+ ions were oxidized to Sn4+ forming SnO2. This oxidation probably occurred during catalysts drying process in the presence of oxygen. The PLGA copolymers with highest inherent viscosities, i.e., highest molecular weights were obtained with SC catalyst containing SnO2 prepared by adsorption of SnCl2.H2O colloidal particles in neutral solution. It was estimated that the highest PLGA molecular weights were equal or larger than 35 kDa. The produced PLGA presented white or lightly yellow color and Sn contamination less than 1 ppm which is below the limit allowed by the Brazilian legislation / No presente trabalho foram sintetizados copolímeros PLGA com massa molar acima de 10 kDa por policondensação direta dos monômeros ácido L-láctico e ácido glicólico. Foram preparados catalisadores à base de copolímero estireno-divinilbenzeno sulfonado (CS) contendo ou não íons Sn2+ adsorvidos na forma de partículas coloidais de SnCl2.H2O em meio neutro ou na forma do ânion complexo [SnCl3]- em meio ácido. Todos os catalisadores foram avaliados por medidas de área superficial específica e volume de poros, espectroscopia de infravermelho, difração de raios X, espectrofotometria de absorção atômica e capacidade de troca iônica. Os copolímeros PLGA obtidos foram caracterizados por espectroscopia de infravermelho, difração de raios X e medidas de viscosidade inerente. Foi verificado que independente do pH do meio de adsorção, os íons Sn2+ foram oxidados a Sn4+ formando o óxido SnO2. Essa oxidação ocorreu, provavelmente, durante o processo de secagem dos catalisadores na presença de oxigênio. Os copolímeros PLGA com maiores viscosidades inerentes, ou seja, maiores massas moleculares foram obtidos pelo uso de catalisador CS contendo SnO2 preparado pela adsorção de partículas coloidais de SnCl2.H2O em meio neutro. Foi estimado que as maiores massas moleculares de PLGA foram iguais ou maiores que 35 kDa. Os copolímeros PLGA produzidos apresentaram coloração branca ou levemente amarelada e contaminação por Sn inferior a 1 ppm bem abaixo do limite permitido pela Legislação Brasileira

Předložená diplomová práce je zaměřená na studium viscoelastického chování kostních past na bázi fosforečnanu vápenatého a vodného roztoku termosenzitivního triblokového kopolymeru, zlepšujícího tokové vlastnosti pasty. V teoretické části je zpracována stručná charakteristika cementů na bázi fosforečnanu vápenatého. Rovněž se zabývá charakteristikou reologických vlastností injektabilních kostních past. Součástí je také stručný přehled aditiv ovlivňujících právě reologické a mechanické vlastnosti past. Experimentální část je zaměřena na charakterizaci triblokového kopolymeru pomocí nukleární magnetické rezonanční spektroskopie a reologie. Dále byly připravovány modifikované fosfátové cementy, u kterých byly posléze studovány viskoelastické vlastnosti. Kostní pasta byla modifikována přídavkem adhezivních sloučenin (dopamin a jodičnan sodný) a antibakteriálním činidlem (selenové nanočástice). Analýza viskoelastických vlastností byla provedena reologickou analýzou, během níž byl primárně sledován proces vytvrzování a tixotropní chování jak nemodifikovaných, tak modifikovaných fosfátových past. Proces vytvrzování probíhal při teplotě 23 °C a 37 °C, imitující fyziologické prostředí. Morfologie fosfátové keramiky byla charakterizována pomocí rastrovací elektronové mikroskopie a velikost částic byla zjištěna pomocí laserového analyzátoru částic. Bylo prokázáno, že výše zmíněná aditiva mají pozitivní vliv na kinetiku procesu vytvrzování kostních past. Selenové nanočástice navíc vylepšily tixotropní chování polymer-fosfátových past. Z tohoto důvodu jsou tyto nové injektabilní kompozitní pasty vhodné pro miniinvazivní chirurgii. Díky aditivům, vykazujících adhezivní vlastnosti, mají potenciál uplatnit se při léčbě zlomenin. Stejně tak se nabízí možnost využít pasty při léčbě osteomyelitidy, a to díky možnému uvolňování antibakteriálních nanočástic.

No description available.

Chemical catalysts are divided into two traditional categories: homogeneous and heterogeneous catalysts. Although homogeneous (molecular) catalysts tend to have high activity and selectivity, their wide application is hampered by the difficulties in catalyst separation. In contrast, the vast majority of industrial scale catalysts are heterogeneous catalysts based on solid materials. Immobilized catalysts, combining the advantages of homogeneous and heterogeneous catalysts, have developed into an important field in catalysis research. This dissertation presents synthesis, characterization and evaluation of several novel immobilized catalysts. In the first part, MNP supported aluminum isoproxide was developed for ROP of Є-caprolactone to achieve facile magnetic separation of catalysts from polymerization system and reduce toxic metal residues in the poly(caprolactone) product. Chapter 3 presents a silica coated MNP supported DMAP catalyst that was synthesized and displayed good activity and regio-selectivity in epoxide ring opening reactions. In Chapter 4, hybrid sulfonic acid catalysts based on polymer brush materials have been developed. The unique polymer brush architecture permits high catalyst loadings as well as easy accessibility of the active sites to be achieved in this catalytic system. In Chapter 5, aminopolymer-silica composite supported Pd catalysts with good activity and selectivity were developed for the selective hydrogenation of alkynes. In this case, the aminopolymer composite works as a stabilizer for palladium nanoparticles, as well as a modifier to tune the catalyst selectivity. All in all, the general theme of the thesis is developing new immobilized catalysts with improved activity/selectivity as well as easy separation via rational catalyst design.

L’objectif de ces travaux de recherche était de synthétiser de mousses polyuréthane (PUF) bio-basées à partir d’oligomères hydroxytéléchéliques issus du caoutchouc naturel (HTNR) ou à partir de poudrettes de pneus usagés (HTWT) et du diol de la polycaprolactone (PCL) comme segments soft. Les paramètres étudiés ont été le type de polyol et le rapport molaire entre HTNR/PCL et HTWT/PCL. La masse molaire de HTNR, HTWT et PCL étaient respectivement 1,800, 1400 et 2000 g/mol. L’effet du rapport molaire HTNR/PCL et HTWT/PCL (1/0, 1/0/5/, 1/1, et 0.5/1) sur la vitesse de formation des mousses et sur les propriétés chimiques et physiques a été étudié. Les structures chimiques de HTNR, HTWT et PUF ont été confirmées par FTIR et 1H-RMN. Le diol de la PCL était le plus réactif donc augmentant le contenu de PCL-diol la vitesse de formation des mousses a augmenté. La densité des mousses a changé légèrement avec le rapport molaire cependant la résistance à la traction reste dans la même gamme. Le diamètre moyen des cellules a augmenté en fonction du contenu de PCL-diol et la tendance inverse a été observée pour l’allongement à la rupture et la résistance à la compression. L’observation au microscope électronique à balayage (MEB) a montré que les mousses basées sur les HTNR étaient alvéolées et fermées. La biodégradabilité a été évaluée selon le test de Sturm. Polyéthylène à baisse densité et benzoate de sodium ont été utilisés respectivement comme témoins négatif et positif. Les mousses ont montré une période d’induction de 33 jours dans lequel le pourcentage de dégradation était ~ 7-10%. La biodégradation de PUF contenant seulement HTNR a été 8.4% après 28 jours et 31.89% après 60 jours ; les PUF contenants 1/0.5 HTNR/PCL ont montré un pourcentage supérieure : 11.31% après 28 jours et 45.6% après 60 jours. Le rapport molaire HTWT/PCL a influencé beaucoup la vitesse de formation des mousses et leur morphologie. Cellules fermées de forme polyédrique ont été observé par microscopie électronique à balayage. Les résultats de l’analyse thermogravimétrique ont montré que l’addition du diol de la PCL a augmenté la température de dégradation. Il a été observé qu’une basse vitesse de réaction génère des mousses à haute densité, petit diamètre de cellule et haute distribution des diamètres. La biodégradation des PUF contenant seulement HTWT a été 31.2% après 28 jours et 51.3% après 60 jours, tandis que les PUF contenant 1/0.5 HTWT/PCL ont montré une dégradation plus élevée : 39.1% après 28 jours et 64.3% après 60 jours. La vitesse de formation des mousses basées sur les HTWT était supérieure à celle des mousses basées sur les HTNR. Toutes les mousses basées sur les HTWT ont une densité supérieure et une taille de cellule inférieure à celles basées sur HTNR. La structure des cellules des mousses basées sur les HTNR ou HTWT était différente cependant toutes les mousses ont montré des cellules quasi complètement fermées. Les mousses basées sur les HTWT ont montré des propriétés thermiques et de biodégradation meilleures par rapport aux mousses basées sur les HTNR. / The aim of this research was to prepare a bio-based polyurethane foam (PUF) containing hydroxyl telechelic oligomers from natural rubber (HTNR) and waste tire crumbs (HTWT) and polycaprolactone diol (PCL) as soft segments. The studied parameters included type of polyols and molar ratio between HTNR/PCL and HTWT/PCL. The molecular weight of HTNR and HTWT derived from 1H-NMR spectra were 1,800 and 1,400 g/mol, respectively. The molecular weight of PCL diol was 2000 g/mol. The effect of HTNR/PCL and HTWT/PCL molar ratio (1/0, 1/0.5, 1/1 and 0.5/1) on the foam formation rate and physical and chemical properties of the resulting PUF was investigated. The chemical structure of HTNR, HTWT and PUF were confirmed by FTIR and 1H-NMR. PCL diol provided faster reaction, thus higher PCL diol content showed higher foam formation rate. The foam density slightly changed with the molar ratio whereas the specific tensile strength of all samples was in the same range. The average diameter of cell increased with increasing contents of PCL diol. The addition of PCL diol resulted in reduced elongation at break and compressive strength. The cellular structure observed by SEM micrographs of HTNR based foams showed an almost closed cell. The biodegradability was assessed according to a modified Sturm test. Low density polyethylene and sodium benzoate were used as a negative and positive control sample, respectively. PUF samples showed an induction time of 33 days in which the percentage of biodegradation was  7-11%. The biodegradation of PUF containing only HTNR was 8.4% and 31.89% at 28 days and 60 days of testing respectively whereas the PUF containing 1/0.5 HTNR/PCL (by mole) showed a higher biodegradation: 11.31% and 45.6% at 28 days and 60 days of testing respectively. The molar ratio of HTWT/PCL strongly affected the kinetic rate of foam formation and foam morphology. According to SEM micrographs, polyhedral closed cells were observed. The addition of the PCL diol increased the thermal degradation temperature of the PUF based on TGA results. A low kinetic rate provided PUF with a high density, small cell size and a broad cell size distribution. The biodegradation of PUF containing only HTWT was 31.2% and 51.3% at 28 days and 60 days of testing respectively whereas the PUF containing 1/0.5 HTWT/PCL diols (by mole) showed a higher biodegradation: 39.1% and 64.3% at 28 days and 60 days of testing respectively. The foam formation rate of HTWT based PUF was higher than the one of HTNR based PUF. All HTWT based PUF have a higher density than HTNR based PUF. The HTWT based PUF had an inferior cell size in comparison to HTNR based PUF. The cellular structure of HTNR based and HTWT based PUF were different, but all PUFs showed almost closed cells. The HTWT based PUF had a higher thermal degradation temperature and biodegradation properties than foams from HTNR. / วัตถุประสงค์ของงานวิจัยนี้ เพื่อทำการเตรียมโฟมพอลิยูรีเทนชีวภาพ (PUF) จากยางธรรมชาติดัดแปรที่มีหมู่ปลายไฮดรอกซิล (HTNR) ยางคลัมบ์ดัดแปรที่มีหมู่ปลาย ไฮดรอกซิล (HTWT) และพอลิคาโปรแลคโทน (PCL) ศึกษาผลของชนิดพอลิออล และสัดส่วนโดยโมลระหว่าง HTNR/PCL และ HTWT/PCL ที่สัดส่วน 1/0, 1/0.5, 1/1 และ 0.5/1 โดยโมล นํ้าหนักโมเลกุลของ HTNR, HTWT และ PCL ที่ใช้สำหรับงานวิจัยนี้ คำนวณจาก 1H-NMR คือ 1,800, 1,400 และ 2,000 g/mol ตามลำดับ ลักษณะโครงสร้างทางเคมีของ HTNR, HTWT และPUF สามารถวิเคราะห์และยืนยันด้วยเทคนิค FTIR และ 1H-NMR รวมถึงทำการวัดอัตราการก่อโฟม (Foam formation rate) ทดสอบสมบัติทางกายภาพ ทางเคมี และสมบัติการย่อยสลายทางชีวภาพ พบว่าในกรณีของโฟมพอลิยูรีเทนจาก HTNR/PCL เมื่อใช้ PCL ในปริมาณที่มากขึ้นจะส่งผลให้อัตราการก่อโฟมเร็วขึ้น และขนาดของเซลโฟมมีขนาดใหญ่ขึ้นด้วย ในขณะที่ค่าความหนาแน่น และความต้านทานต่อแรงดึงจำเพาะมีการเปลี่ยนแปลงเล็กน้อย การเติม PCL ในส่วนผสมของโฟมยังส่งผลให้ความสามารถในการยืด ณ จุดขาด และความทนทานต่อการกดมีค่าลดลง การคืนตัวหลังการกดของโฟม PUF2 (สัดส่วนระหว่าง HTNR/PCL = 1/0.5) จะให้ค่าตํ่าที่สุดคือ 40% ลักษณะของโฟมที่ได้จากการทดลองนี้โดยส่วนใหญ่จะเป็นแบบเซลปิด ความสามารถในการย่อยสลายทางชีวภาพของโฟม ทดสอบโดยใช้วิธี Sturm Test มี LDPE เป็นตัวเปรียบเทียบเชิงลบ และใช้ Sodium benzoate เป็นตัวเปรียบเทียบเชิงบวก พบว่าโฟมเริ่มมีการย่อยสายเกิดขึ้นอย่างเห็นได้ชัดที่เวลา 33 วัน มีเปอร์เซ็นต์การย่อยสลายในช่วง 7-11 เปอร์เซ็นต์ เปอร์เซ็นต์การย่อยสลายของโฟมจาก HTNR (PUF1) อยู่ที่ระดับ 8.4 และ 31.89 เปอร์เซ็นต์ และเปอร์เซ็นต์การย่อยสลายของโฟมจาก HTNR/PCL (1/0.5) อยู่ที่ระดับ 11.31 และ 45.6 เปอร์เซ็นต์ ที่เวลาในการทดสอบ 28 และ 60 วัน ตามลำดับ กรณีของโฟมพอลิยูรีเทนจาก HTWT/PCL เมื่อใช้ PCL ในปริมาณที่มากขึ้นจะส่งผลให้ค่าความหนาแน่นสูงขึ้น ขนาดของเซลโฟมลดลงมีการกระจายของเซลในวงกว้างไม่สมํ่าเสมอ เปอร์เซ็นต์การย่อยสลายทางชีวภาพของโฟมจาก HTWT (PUF5) อยู่ที่ระดับ 31.2 และ 51.3 เปอร์เซ็นต์ และเปอร์เซ็นต์การย่อยสลายของโฟมจาก HTWT/PCL (1/0.5) อยู่ที่ระดับ 39.1 และ 64.3 เปอร์เซ็นต์ ที่เวลาในการทดสอบ 28 และ 60 วัน ตามลำดับ เมื่อทำการเปรียบเทียบโฟมที่ได้จากการเตรียมโดยใช้พอลิออลหลักเป็น HTNR และ HTWT พบว่าโฟมจากพอลิออลหลัก HTWT ให้อัตราการก่อตัวของโฟมเร็วกว่า ขนาดของเซลโฟมเล็กกว่า ความหนาแน่น ความต้านทานต่อความร้อน และเปอร์เซ็นต์การย่อยสลายทางชีวภาพสูงกว่า เมื่อเทียบกับโฟมจากพอลิออลหลัก HTNR

Dans le contexte de développement durable actuel, les matériaux biosourcés et biodégradables commencent à prendre une place importante d’un point de vue économique et écologique. L’objectif de remplacer les polyoléfines utilisées actuellement dans des domaines clés tels que l’emballage et l’automobile est cependant difficile car les matériaux « verts » sont rarement aussi performants. Ils présentent en général des lacunes au niveau de leurs propriétés mécaniques et sont sensibles à des dégradations qui limitent leur durée de vie. Le poly(butylène succinate) est un polyester connu depuis longtemps mais qui regagne de l’intérêt grâce à son potentiel biosourcé et biodégradable ainsi que ses propriétés mécaniques proches de celles des polyoléfines. Néanmoins, sa rigidité est encore trop faible et sa sensibilité importante à l’hydrolyse limite son utilisation dans le temps, même dans des conditions standards de température et d’humidité. Des améliorations de la stabilité du PBS sont possibles et plusieurs solutions ont été envisagées. L’intérêt s’est porté sur la modification de la balance hydrophile/hydrophobe du PBS par l’ajout d’un comonomère ramifié très hydrophobe, le Pripol 1009 ou possédant un cycle aromatique, l’acide téréphtalique. L’addition de charges dans le matériau peut également s’avérer efficace pour neutraliser les fins de chaines acides catalysant la dégradation, en utilisant du carbonate de calcium, ou pour limiter la perméabilité du matériau, par incorporation de talc. Dans l’optique de moduler les propriétés mécaniques du PBS, la voie de modification la plus fructueuse est le mélange par incorporation de charges minérales, comme le carbonate de calcium ou le talc, ou le mélange avec d’autres polyesters possédant une rigidité plus importante, tels que le poly(acide lactique) ou le poly(butylène téréphtalate). Les mélanges doivent présenter une bonne compatibilité et être mis en œuvre à des températures convenables pour limiter la dégradation du PBS et conserver la ductilité du matériau final, comme c’est le cas des mélanges PBS/PLA. Des combinaisons ont également été envisagées entre les différentes solutions efficaces pour améliorer à la fois les propriétés mécaniques et la stabilité face à l’hydrolyse chimique. / Within the frame of sustainable development, biobased and biodegradable polymers are going to play an important role according to economic and environmental perspectives. The polyolefins currently used in packaging and automotive industries will be replaced by biomaterials. The poly(butylene succinate), an “old” aliphatic polyester, has recently regained interest thanks to its biobased and biodegradable potential and mechanical properties similar to polyolefins. However, this polyester is very sensitive to degradation even at mild ambient conditions and, even though its flexibility is comparable to polyethylene or polypropylene, its modulus is too low. Some modifications of the chemical structure were considered to improve the long-term use of PBS. The synthesis of random copolymers using long-chain fatty acid Pripol 1009 or terephthalic acid allows to reduce significantly the hydrolysis rate and properties are maintained during a longer time. The incorporation of fillers like calcium carbonate and talc also enhance the PBS stability. The addition of calcium carbonate neutralizes carboxyl terminal group, which play an autocatalytic role in the hydrolytic degradation. High aspect ratio of talc increases the gas and liquid diffusion path, reducing permeability and providing better barrier properties to the material. In order to improve Young’s modulus, formulating blends with mineral fillers like calcium carbonate and talc, or with more rigid polyesters like polylactic acid or poly(butylene terephthalate) are efficient. The most interesting results are obtained by using calcium carbonate and polylactic acid, which allow the preservation of PBS’s flexibility. Processing parameters should be maximized to limit the degradation of PBS. Combinations of the most interesting solutions were investigated and lead to materials which fulfill the required specifications.