Made available in DSpace on 2014-06-11T19:23:29Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-03-28Bitstream added on 2014-06-13T19:50:12Z : No. of bitstreams: 1 silva_scc_me_bauru.pdf: 852083 bytes, checksum: ac164d42c6d5526cc944c7194152c4ef (MD5) / A mistura asfáltica, pode ser usinado a quente e pré-misturado a frio. A mistura denominada pré-misturado, empregada no revestimento de pavimento é a mistura a frio, tendo como composição agregado mineral graduado, material de enchimento e emulsão asfáltica espalhada e comprimida a frio. Esse trabalho irá abordar a mistura asfástica pré-misturado a frio, tendo como objetivo comparar os resultados baseados em ensaios da mistura asfáltica e a caracterização do comportamento da mistura quando preparada com a adição de borracha reciclada de pneus usados. A pesquisa visa qualificar e otimizar o desempenho da mistura asfáltica que receberá a borracha moída com adições de 3%, 4% e 5% em relação à massa total de agregados minerais, comparando-as com a mistura de referência, sem a adição da borracha. A destinação final da borracha constitui em todo o mundo em um grande desafio, em virtude de suas peculiaridades, como seu tempo de degradação, estimado em aproximadamente 600 anos. Além da quantidade gerada nos dias de hoje, volume, peso e principalmente grande dificuldade de alternativas consideradas ecologicamente corretas e economicamente viáveis. Os ensaios realizados baseiam-se em uma faixa de pré-misturado a frio, onde os corpos de prova foram produzidos em laboratório com emulsão asfáltica catiônica. A adição da borracha moída e os teores de emulsão asfáltica foram definidos e analisados após ensaio de Dosagem Marshall a Frio. As características e comportamento das misturas foram avaliados pela densidade da mistura asfáltica, estabilidade e fluência Marshall. Dessa forma, buscando uma alternativa a atender as normas brasileiras e resultados de desempenho dessas misturas asfálticas, conclui-se que... / The asphalt paving mixture can be produced in the heat and premixed in cold. The mixture called premixed, having as mineral aggregate composition graduated, stuffing material and the asphalt emulsion compressed in cold. This work will go to approach the premixed in cold of the asphalt misture, having as objective to compare the results based on assays of the asphalt mixture and the behavior misture characterization when it prepared with the recycled rubber of old tires. The research seeks to qualify and optimize the performance of the asphalt mixture thet will receive the crushed rubber with additions of 3%, 4% and 5% in relation to the total agregate mineral mass, comparing them with the reference mixture, without the rubber addition. The final destination of the rubber to consist of a great challenge all over the world, in virtue of its peculiarities, as its time of degradation, approximately esttmed in 600 years. Beyond the generated amount nowadays, volume, weight and mainly great difficult of considered alternatives correct ecologically and viable economically. The accomplishment rehearsals based on in a strip premixed in cold, called dense strip, where the specimens were produced on the lab wiyh the cationic asphalt emulsion. The crushed rubber addition and the asphalt emulsion texts had been defined and analyzed after rehearsal of in cold Marshall Dosage. The mixture characteristics and behaviour had been evaluated by the stability, Marshall fluency and asphalt mixture density. In the way, looking for an alternative to attend the Brazillians rules and results of performance of these asphalt paving mixture, it follows that the rubber addition benefits are considerable, where the line with 3% addition rubber it presented the smallest index of emptiness, to smallest fluency, the biggest stability Marshall, the biggest apparent density, the biggest relationship polishemptiness and the smallest tenor of emulsion asphalt.

O trincamento por fadiga é um dos principais mecanismos de deterioração dos pavimentos flexíveis e, mesmo assim, é, ainda hoje, um dos defeitos mais difíceis de serem controlados. Uma das alternativas para a melhoria das características de fadiga das misturas asfálticas é o emprego de ligantes asfálticos modificados, porém, há dúvida se o enrijecimento provocado pela adição dos modificadores pode influenciar a resistência à fadiga da mistura asfáltica. Com o intuito de mensurar características do ligante asfáltico que tenham relação com o trincamento por fadiga da mistura asfáltica, alguns ensaios de laboratório foram desenvolvidos recentemente, destacando-se dois: o ensaio de varredura de tempo (time sweep) e o ensaio de varredura de amplitude linear (LAS). O objetivo deste trabalho é caracterizar o comportamento à fadiga de 12 ligantes asfálticos modificados de mesmo grau de desempenho (PG 76-xx). As formulações CAP+PPA, CAP+SBS, CAP+SBS+PPA, CAP+Borracha, CAP+Borracha+PPA, CAP+PE, CAP+PE+PPA, CAP+EVA, CAP+EVA+PPA, CAP+SBR, CAP+SBR+PPA e CAP+Elvaloy+PPA foram preparadas tendo como base um ligante asfáltico 50/70 de classificação PG 64-xx. Com base na caracterização realizada neste estudo, as principais conclusões são: (a) o material que apresentou melhor vida de fadiga foi o CAP+EVA; (b) o material menos sensível à deformação foi o CAP puro; (c) o menos sensível à temperatura foi o CAP+PPA; (d) o efeito do PPA nos ligantes asfálticos com outros aditivos provocou diminuição da vida de fadiga para a maioria das formulações, aumento da sensibilidade aos níveis de deformação para todas as formulações, diminuição da sensibilidade à temperatura e aumento da sensibilidade ao envelhecimento para a maioria das formulações; (e) tomando por base o ordenamento final das melhores características à fadiga dos ligantes asfálticos segundo os parâmetros analisados, o CAP+Borracha apresenta o melhor desempenho global / Fatigue cracking is a major mechanism of deterioration of flexible pavements, and even then, it is still one of the defects that are more difficult to control. One alternative to improve fatigue characteristics of asphalt mixtures is the use of modified asphalt binders; however, there is no doubt that the stiffening caused by the addition of modifiers can influence the fatigue resistance of asphalt mixture. In order to measure characteristics of asphalt binders that are related to the fatigue cracking of asphalt mixture, some laboratory tests have been recently developed such as the time sweep and the linear amplitude sweep (LAS) test. The objective of this study is to characterize the fatigue behavior of 12 modified asphalt binders with the same high-temperature performance grade (PG 76-xx). The formulations AC+PPA, AC+SBS, AC+SBS+PPA, AC+Rubber, AC+Rubber+PPA, AC+PE, AC+PE+PPA, AC+EVA, AC+EVA+PPA, AC+SBR, AC+SBR+PPA and AC+Elvaloy+PPA were prepared with a 50/70 base asphalt binder graded as PG 64-xx in the Superpave specification. Based on the characterization made in this study, the main conclusions are the following: (a) the material that showed better fatigue life was the AC+EVA; (b) the material that is less sensitive to deformation was the neat AC; (c) the less sensitive one to temperature was the AC+PPA; (d) the effect of PPA in asphalt binders prepared with other additives caused a reduction in the fatigue life for many formulations, an increase in the sensitivity levels of deformation for all formulations, a reduction in the sensitivity to temperature and an increase in the sensitivity to aging for several formulations; (e) on the final ranking of the characteristics of asphalt binders according to the parameters analyzed in this research study, the AC+Rubber showed the best overall performance

O trincamento por fadiga é um dos principais mecanismos de deterioração dos pavimentos flexíveis e, mesmo assim, é, ainda hoje, um dos defeitos mais difíceis de serem controlados. Uma das alternativas para a melhoria das características de fadiga das misturas asfálticas é o emprego de ligantes asfálticos modificados, porém, há dúvida se o enrijecimento provocado pela adição dos modificadores pode influenciar a resistência à fadiga da mistura asfáltica. Com o intuito de mensurar características do ligante asfáltico que tenham relação com o trincamento por fadiga da mistura asfáltica, alguns ensaios de laboratório foram desenvolvidos recentemente, destacando-se dois: o ensaio de varredura de tempo (time sweep) e o ensaio de varredura de amplitude linear (LAS). O objetivo deste trabalho é caracterizar o comportamento à fadiga de 12 ligantes asfálticos modificados de mesmo grau de desempenho (PG 76-xx). As formulações CAP+PPA, CAP+SBS, CAP+SBS+PPA, CAP+Borracha, CAP+Borracha+PPA, CAP+PE, CAP+PE+PPA, CAP+EVA, CAP+EVA+PPA, CAP+SBR, CAP+SBR+PPA e CAP+Elvaloy+PPA foram preparadas tendo como base um ligante asfáltico 50/70 de classificação PG 64-xx. Com base na caracterização realizada neste estudo, as principais conclusões são: (a) o material que apresentou melhor vida de fadiga foi o CAP+EVA; (b) o material menos sensível à deformação foi o CAP puro; (c) o menos sensível à temperatura foi o CAP+PPA; (d) o efeito do PPA nos ligantes asfálticos com outros aditivos provocou diminuição da vida de fadiga para a maioria das formulações, aumento da sensibilidade aos níveis de deformação para todas as formulações, diminuição da sensibilidade à temperatura e aumento da sensibilidade ao envelhecimento para a maioria das formulações; (e) tomando por base o ordenamento final das melhores características à fadiga dos ligantes asfálticos segundo os parâmetros analisados, o CAP+Borracha apresenta o melhor desempenho global / Fatigue cracking is a major mechanism of deterioration of flexible pavements, and even then, it is still one of the defects that are more difficult to control. One alternative to improve fatigue characteristics of asphalt mixtures is the use of modified asphalt binders; however, there is no doubt that the stiffening caused by the addition of modifiers can influence the fatigue resistance of asphalt mixture. In order to measure characteristics of asphalt binders that are related to the fatigue cracking of asphalt mixture, some laboratory tests have been recently developed such as the time sweep and the linear amplitude sweep (LAS) test. The objective of this study is to characterize the fatigue behavior of 12 modified asphalt binders with the same high-temperature performance grade (PG 76-xx). The formulations AC+PPA, AC+SBS, AC+SBS+PPA, AC+Rubber, AC+Rubber+PPA, AC+PE, AC+PE+PPA, AC+EVA, AC+EVA+PPA, AC+SBR, AC+SBR+PPA and AC+Elvaloy+PPA were prepared with a 50/70 base asphalt binder graded as PG 64-xx in the Superpave specification. Based on the characterization made in this study, the main conclusions are the following: (a) the material that showed better fatigue life was the AC+EVA; (b) the material that is less sensitive to deformation was the neat AC; (c) the less sensitive one to temperature was the AC+PPA; (d) the effect of PPA in asphalt binders prepared with other additives caused a reduction in the fatigue life for many formulations, an increase in the sensitivity levels of deformation for all formulations, a reduction in the sensitivity to temperature and an increase in the sensitivity to aging for several formulations; (e) on the final ranking of the characteristics of asphalt binders according to the parameters analyzed in this research study, the AC+Rubber showed the best overall performance

O ensaio de fluência e recuperação sob tensão múltipla (MSCR) é resultado do aperfeiçoamento do ensaio de fluência repetida e recuperação (RCRT) pela Administração Rodoviária Federal dos Estados Unidos (FHWA) e tem por objetivo avaliar o percentual de recuperação, a compliância não-recuperável e a dependência dos ligantes asfálticos, especialmente os modificados, quanto ao nível de tensão. O MSCR foi utilizado neste estudo para caracterizar o comportamento fluência-recuperação de diversos ligantes asfálticos modificados virgens e envelhecidos a curto prazo. Foi empregado o procedimento da norma ASTM D7405, que prescreve os tempos de fluência e recuperação de 1 e 9 s, e avaliada a influência do aumento dos tempos de fluência e recuperação de 1 e 9 s para 2 e 18 s nas propriedades dos ligantes asfálticos envelhecidos a curto prazo. Além dos resultados destes ensaios, foram utilizados os valores de penetração, ponto de amolecimento, viscosidade rotacional, penetração retida, incremento do ponto de amolecimento, incremento de viscosidade e perda de massa para verificar quais ligantes asfálticos apresentam melhor comportamento à luz das propriedades e parâmetros considerados. Foram preparados doze materiais modificados e de classificação PG 76-XX tendo como base um CAP 50/70 de classificação PG 64-XX: CAP+PPA, CAP+Elvaloy+PPA, CAP+borracha, CAP+borracha+PPA, CAP+SBS, CAP+SBS+PPA, CAP+EVA, CAP+EVA+PPA, CAP+PE, CAP+PE+PPA, CAP+SBR e CAP+SBR+PPA. O CAP+Elvaloy+PPA apresenta, em um contexto geral, o melhor desempenho nas propriedades e parâmetros analisados em virtude dos bons resultados do percentual de recuperação e da compliância não-recuperável e das menores sensibilidades à tensão. O CAP+PE apresenta o pior desempenho geral dentre os materiais estudados, na medida em que os resultados do percentual de recuperação e da compliância não-recuperável deste ligante asfáltico são ruins e as sensibilidades ao aumento nos tempos de fluência e recuperação de 1 e 9 s para 2 e 18 s são elevadas. Ao ordenar os ligantes asfálticos do melhor para o pior à luz das propriedades e parâmetros considerados, o resultado é: CAP+Elvaloy+PPA, CAP+EVA, CAP+EVA+PPA, CAP+PPA, CAP+borracha+PPA, CAP+SBR+PPA, CAP+SBS+PPA, CAP+SBS, CAP+PE+PPA, CAP+borracha, CAP+SBR, CAP 50/70 e CAP+PE. / The multiple stress creep and recovery (MSCR) test is the result of a refinement of the repeated creep and recovery test (RCRT). This refinement was performed by the United States Federal Highway Administration (FHWA) with the aim of evaluating the percent recovery, the non-recoverable compliance and the stress dependency of asphalt binders, especially the modified ones. The MSCR test was applied in this study in order to characterize the creep-recovery behavior of unaged and short-term aged modified asphalt binders. The test procedure prescribed in ASTM D7405 specification was adopted and, to evaluate the influence of a greater creep-recovery time in the behavior of asphalt binders, the creep and recovery times of 2 and 18 s were also adopted in additional tests. The results of these tests, as well as the penetration, softening point, rotational viscosity, retained penetration, softening point increase, viscosity increase and mass loss data and mixing and compaction temperatures, were used with the objectives of ranking the asphalt binders and checking the ones with the best results in the parameters and properties considered. By using a PG 64-XX base asphalt-binder of 50/70 penetration grade, the following PG 76-XX odified asphalt binders were prepared: AC+PPA, AC+Elvaloy+PPA, AC+crumb rubber, AC+crumb rubber+PPA, AC+SBS, AC+SBS+PPA, AC+EVA, AC+EVA+PPA, AC+PE, AC+PE+PPA, AC+SBR and AC+SBR+PPA. In general, AC+Elvaloy+PPA has the best results in the parameters and properties considered in this study, especially due to the good results in the percent recovery and non-recoverable compliance and the lower stress sensitivity. In general, AC+PE has the worst results among the asphalt binders considered in this work, due to the facts that the percent recovery and non-recoverable compliance results are not good and the sensitivities to the creep-recovery times are high. By taking the results of this study and ranking the asphalt binders from the best to the worst, the following sequence is obtained: AC+Elvaloy+PPA, AC+EVA, AC+EVA+PPA, AC+PPA, AC+crumb rubber+PPA, AC+SBR+PPA, AC+SBS+PPA, AC+SBS, AC+PE+PPA, AC+crumb rubber, AC+SBR, neat AC and AC+PE.

O ensaio de fluência e recuperação sob tensão múltipla (MSCR) é resultado do aperfeiçoamento do ensaio de fluência repetida e recuperação (RCRT) pela Administração Rodoviária Federal dos Estados Unidos (FHWA) e tem por objetivo avaliar o percentual de recuperação, a compliância não-recuperável e a dependência dos ligantes asfálticos, especialmente os modificados, quanto ao nível de tensão. O MSCR foi utilizado neste estudo para caracterizar o comportamento fluência-recuperação de diversos ligantes asfálticos modificados virgens e envelhecidos a curto prazo. Foi empregado o procedimento da norma ASTM D7405, que prescreve os tempos de fluência e recuperação de 1 e 9 s, e avaliada a influência do aumento dos tempos de fluência e recuperação de 1 e 9 s para 2 e 18 s nas propriedades dos ligantes asfálticos envelhecidos a curto prazo. Além dos resultados destes ensaios, foram utilizados os valores de penetração, ponto de amolecimento, viscosidade rotacional, penetração retida, incremento do ponto de amolecimento, incremento de viscosidade e perda de massa para verificar quais ligantes asfálticos apresentam melhor comportamento à luz das propriedades e parâmetros considerados. Foram preparados doze materiais modificados e de classificação PG 76-XX tendo como base um CAP 50/70 de classificação PG 64-XX: CAP+PPA, CAP+Elvaloy+PPA, CAP+borracha, CAP+borracha+PPA, CAP+SBS, CAP+SBS+PPA, CAP+EVA, CAP+EVA+PPA, CAP+PE, CAP+PE+PPA, CAP+SBR e CAP+SBR+PPA. O CAP+Elvaloy+PPA apresenta, em um contexto geral, o melhor desempenho nas propriedades e parâmetros analisados em virtude dos bons resultados do percentual de recuperação e da compliância não-recuperável e das menores sensibilidades à tensão. O CAP+PE apresenta o pior desempenho geral dentre os materiais estudados, na medida em que os resultados do percentual de recuperação e da compliância não-recuperável deste ligante asfáltico são ruins e as sensibilidades ao aumento nos tempos de fluência e recuperação de 1 e 9 s para 2 e 18 s são elevadas. Ao ordenar os ligantes asfálticos do melhor para o pior à luz das propriedades e parâmetros considerados, o resultado é: CAP+Elvaloy+PPA, CAP+EVA, CAP+EVA+PPA, CAP+PPA, CAP+borracha+PPA, CAP+SBR+PPA, CAP+SBS+PPA, CAP+SBS, CAP+PE+PPA, CAP+borracha, CAP+SBR, CAP 50/70 e CAP+PE. / The multiple stress creep and recovery (MSCR) test is the result of a refinement of the repeated creep and recovery test (RCRT). This refinement was performed by the United States Federal Highway Administration (FHWA) with the aim of evaluating the percent recovery, the non-recoverable compliance and the stress dependency of asphalt binders, especially the modified ones. The MSCR test was applied in this study in order to characterize the creep-recovery behavior of unaged and short-term aged modified asphalt binders. The test procedure prescribed in ASTM D7405 specification was adopted and, to evaluate the influence of a greater creep-recovery time in the behavior of asphalt binders, the creep and recovery times of 2 and 18 s were also adopted in additional tests. The results of these tests, as well as the penetration, softening point, rotational viscosity, retained penetration, softening point increase, viscosity increase and mass loss data and mixing and compaction temperatures, were used with the objectives of ranking the asphalt binders and checking the ones with the best results in the parameters and properties considered. By using a PG 64-XX base asphalt-binder of 50/70 penetration grade, the following PG 76-XX odified asphalt binders were prepared: AC+PPA, AC+Elvaloy+PPA, AC+crumb rubber, AC+crumb rubber+PPA, AC+SBS, AC+SBS+PPA, AC+EVA, AC+EVA+PPA, AC+PE, AC+PE+PPA, AC+SBR and AC+SBR+PPA. In general, AC+Elvaloy+PPA has the best results in the parameters and properties considered in this study, especially due to the good results in the percent recovery and non-recoverable compliance and the lower stress sensitivity. In general, AC+PE has the worst results among the asphalt binders considered in this work, due to the facts that the percent recovery and non-recoverable compliance results are not good and the sensitivities to the creep-recovery times are high. By taking the results of this study and ranking the asphalt binders from the best to the worst, the following sequence is obtained: AC+Elvaloy+PPA, AC+EVA, AC+EVA+PPA, AC+PPA, AC+crumb rubber+PPA, AC+SBR+PPA, AC+SBS+PPA, AC+SBS, AC+PE+PPA, AC+crumb rubber, AC+SBR, neat AC and AC+PE.