Tensile Behavior Of Free-Standing Pt-Aluminide (PtAl) Bond CoatsAlam, MD Zafir 10 1900 (has links) (PDF)
Pt-aluminide (PtAl) coatings form an integral part of thermal barrier coating (TBC) systems that are applied on Ni-based superalloy components operating in the hot sections of gas turbine engines. These coatings serve as a bond coat between the superalloy substrate and the ceramic yttrium stabilized zirconia (YSZ) coating in the TBC system and provide oxidation resistance to the superalloy component during service at high temperatures. The PtAl coatings are formed by the diffusion aluminizing process and form an integral part of the superalloy substrate. The microstructure of the PtAl coatings is heavily graded in composition as well as phase constitution. The matrix phase of the coating is constituted of the B2-NiAl phase. Pt, in the coating, is present as a separate PtAl2 phase as well as in solid solution in B2-NiAl. The oxidation resistance of the PtAl bond coat is derived from the B2-NiAl phase. At high temperatures, Al from the B2-NiAl phase forms a regenerative layer of alumina on the coating surface which, thereby, lowers the overall oxidation rate of the superalloy substrate. The presence of Pt is beneficial in improving the adherence of the alumina scale to the surface and thereby enhancing the oxidation resistance of the coating. However, despite its excellent oxidation resistance, the B2-NiAl being an intermetallic phase, renders the PtAl coating brittle and imparts it with a high brittle-to-ductile-transition-temperature (BDTT). The PtAl coating, therefore, remains prone to cracking during service. The penetration of these cracks into the substrate is known to degrade the strain tolerance of the components.
Evaluation of the mechanical behavior of these coatings, therefore, becomes important from the point of views of scientific understanding as well as application of these coatings in gas turbine engine components. Studies on the mechanical behavior of coatings have been mostly carried on coated bulk superalloy specimens. However, since the coating is brittle and the superalloy substrate more ductile when compared to the coating, the results obtained from these studies may not be representative of the coating. Therefore, it is imperative that the mechanical behavior of the coating in stand-alone condition, i.e. the free-standing coating specimen without any substrate attached to it, be evaluated for ascertaining the true mechanical response of the coating. Study of stand-alone bond coats involves complex specimen preparation techniques and challenging testing procedures. Therefore, reports on the evaluation of mechanical properties of stand-alone coatings are limited in open literature. Further, no systematic effort has so far been made to examine important aspects such as the effect of temperature and strain rate on the tensile behavior of these coatings. The deformation mechanisms associated with these bond coats have also not been reported in the literature.
In light of the above, the present research study aims at evaluating the tensile behavior of free-standing PtAl coatings by the micro-tensile testing technique. The micro-tensile testing method was chosen for property evaluation because of its inherent ability to generate uniform strain in the specimen while testing, which makes the results easy to interpret. Further, since the technique offers the feasibility to test the entire graded PtAl coating in-situ, the results remain representative of the coating. Using the above testing technique, the tensile behavior of the PtAl coating has been evaluated at various temperatures and strain rates. The effect of strain rate on the BDTT of the coating has been ascertained. Further, the effect of Pt content on the tensile behavior of these coatings has also been evaluated. Attempts have been made to identify the mechanisms associated with tensile deformation and fracture in these coatings.
The thesis is divided into nine chapters. Chapter 1 presents a brief introduction on the operating environment in gas turbine engines and the materials that are used in the hot sections of gas turbine engines. The degradation mechanisms taking place in the superalloy in gas turbine environments and the need for application of coatings has also been highlighted. The basic architecture of a typical thermal barrier coating (TBC) system applied on gas turbine engine components has been presented. The constituents of the TBC system, i.e. the ceramic YSZ coating, MCrAlY overlay as well as diffusion aluminide bond coats and, the various techniques adopted for the deposition of these coatings have been described in brief.
Chapter 2 presents an overview of the literature relevant to this study. This chapter is divided into four sub-chapters. The formation of diffusion aluminide coatings on Ni-based superalloys has been described in the first sub-chapter. Emphasis has been laid on pack cementation process for the formation of the coatings. The fundamentals of pack aluminizing process, including the thermodynamic and kinetic aspects, have been mentioned in brief. The microstructural aspects of high activity and low activity plain aluminide and Pt-aluminide coatings have also been illustrated. The techniques applied for the mechanical testing of bond coats have been discussed in the second sub-chapter. The macro-scale testing techniques have been mentioned in brief. The small scale testing methods such as indentation, bend tests and micro-tensile testing have also been discussed in the context of evaluation of mechanical properties of bond coats. Since the matrix in the aluminide bond coats is constituted of the B2-NiAl phase, a description of the crystal structure and deformation characteristics of this phase including the flow behavior, ductility and fracture behavior has been mentioned in the third sub-chapter. In the fourth sub-chapter, reported literature on the tensile behavior and brittle-to-ductile-transition-temperature (BDTT) of diffusion aluminide bond coats has been discussed.
In Chapter 3, details on experiments carried out for the formation of various coatings used in the present study and, their microstructural characterization, are provided. The method for extraction of stand-alone coating specimens and their testing is discussed.
The microstructure and composition of the various coatings used in the present study are discussed in detail in Chapter 4. Unlike in case of bulk tensile testing, for which standards on the design of specimens exist, there are no standards available for the design of micro-tensile specimens. Therefore, as part of the present research work, a finite element method (FEM)-based study was carried out for ascertaining the dimensions of the specimens. The simulation studies predicted that failure of the specimens within the gage length can be ensured only when certain correlations between the dimensional parameters are satisfied. Further, the predictions from the simulation study were validated experimentally by carrying out actual testing of specimens of various dimensions. Details on the above mentioned aspects of specimen design are provided in Chapter 5. The PtAl coatings undergo brittle fracture at lower temperatures while ductile fracture occurs at higher temperatures. Further, the coatings exhibit a scatter in the yielding behavior at temperatures in the vicinity of BDTT. Therefore, the BDTT, determined as the temperature at which yielding is first observed in the stress-strain curves, may not be representative of the PtAl coatings. In Chapter 6, a method for the precise determination of BDTT of aluminide bond coats, based on the variation in the plastic strain to fracture with temperature, has been demonstrated. The BDTT determined by the above method correlated well with the variation in fracture surface features of the coating and was found representative of these coatings.
In Chapter 7, the effect of temperature and strain rate on the tensile properties of a PtAl bond coat has been evaluated. The temperature and strain rate was varied between room temperature (RT)-1100°C and 10-5 s-1-10-1 s-1, respectively. The effect of strain rate on the BDTT of the PtAl bond coat has been examined. Further, the variation in fracture surface features and mechanism of fracture with temperature and strain rate are illustrated. The micro-mechanisms of deformation and fracture in the coating at different temperature regimes have also been discussed. The coating exhibited brittle-to-ductile transition with increase in temperature at all strain rates. The BDTT was strain rate sensitive and increased significantly at higher strain rates. Above BDTT, YS and UTS of the coating decreased and its ductility increased with increase in the test temperature at all strain rates. Brittle behavior occurring in the coating at temperatures below the BDTT has been attributed to the lack of operative slip systems in the B2-NiAl phase of the coating. The onset of ductility in the coating in the vicinity of BDTT has been ascribed to generation of additional slip systems caused by climb of dislocations onto high index planes. The coating exhibited two distinct mechanisms for plastic deformation as the temperature was increased from BDTT to 1100°C. For temperatures in the range BDTT to about 100°C above it, deformation was controlled by dislocations overcoming the Peierls-Nabarro barrier. Above this temperature range, non-conservative motion of jogs by jog dragging mechanism controlled the deformation. The transition temperature for change of deformation mechanism also increased with increase in strain rate. For all strain rates, fracture in the coating at test temperatures below the BDTT, occurred by initiation of cracks in the intermediate single phase B2-NiAl layer of the coating and subsequent inside-out propagation of the cracks across the coating thickness. Ductile fracture in the coating above the BDTT was associated with micro-void formation throughout the coating.
The effect of Pt content on the tensile behavior of PtAl coating, evaluated at various temperatures ranging from room temperature (RT) to 1100°C and at a nominal strain rate of 10-3 s-1, is presented in Chapter 8. Irrespective of Pt content in the coating, the variation in tensile behavior of the coating with temperature remained similar. At temperatures below BDTT, the coatings exhibited linear stress-strain response (brittle behavior) while yielding (ductile behavior) was observed at temperatures above BDTT. At any given temperature, the elastic modulus decreased while the strength increased with increase in Pt content in the coating. On the other hand, the ductility of the coating remained unaffected with Pt content. The BDTT of the coating also increased with increase in Pt content in the coating. Addition of Pt did not affect the fracture mechanism in the coating. Fracture at temperatures below BDTT was caused by nucleation of cracks at the intermediate layer and their subsequent inside-out propagation. At high temperatures, fracture occurred in a ductile manner comprising void formation, void linkage and subsequent joining with cracks. The deformation sub-structure of the coating did not get affected with Pt incorporation. Short straight dislocations were observed at temperatures below BDTT, while, curved dislocations marked by jog formation were observed at temperatures above BDTT. The factors controlling fracture stress and strength in the PtAl coatings at various temperatures have also been assessed.
The overall summary of the present research study and recommendations for future studies are presented in the last chapter, i.e. Chapter 9.
|
12 |
Interaction entre fluides de différents réservoirs lors de l'évolution d'un prisme orogénique en contexte de déformation partitionnée : les Cordillères bétiques internes (Espagne) : Implications sur le transfert de métaux dans la croute / Interaction between fluids of different reservoirs in the evolution of an orogenic wedge into a context of partitioned deformation : Internal Betic Cordilleras (Spain) : Implications for the transfer of metals in the crustDyja, Vanessa 10 March 2014 (has links)
La thèse cherche à caractériser les types de fluides à différents niveaux structuraux et types de déformation. Les résultats de la Sierra Bédar indiquent le rôle d'une saumure enrichie en métaux lors des derniers stades de circulation au sein de la croûte ductile dans un domaine encore isolé des fluides de surface. Cette saumure est plus diluée à l'est dans la Sierra Almagrera et où l'impact du système décrochant va devenir de plus en plus important avec du volcanisme et de nombreux gisements. Dans le domaine fragile, des veines de quartz enregistrent des fluides de surface. Suivent des veines de quartz indiquant la réapparition des fluides métamorphiques sous-jacent. La formation de veines de sidérite-pyrite-galène-barytine montre de plus forte salinité et des rapports Cl/Br indiquant la contribution d'une autre source de saumures secondaires issues cette fois des évaporites messiniennes. Le décrochement a modifié le compartimentage de part et d'autre de la transition fragile-ductile / This thesis aim at characterizing the types of fluids concerned structural levels and style of deformation. Results from Sierra Bedar point out the role played by metal-rich brines during late stages of fluid flows within the ductile crust within a domain was still isolated from surficial fluids. Brine concentration drop in the eastern Sierra Almagrera which was progressively more impacted by the major transcurrent system with volcanism and metal ore deposits. At reaching the brittle domain, quartz veins trapped surficial fluids. Soon after, quartz veins indicating the return of metamorphic fluids. Following siderite-pyrite-galena-barite veins display higher salinities and Cl/Br ratios indicate the contribution of another secondary brine coming from early Messinian evaporites. This major transcurrent tectonics clearly modified the partitioning on both sides of the brittle-ductile transition
|
Page generated in 0.102 seconds